Cobalt Sulfide Confined in N-doped Porous Branched Carbon Nanotubes for Lithium-Ion Batteries

View ResearcherID and ORCID

Yongsheng Zhou1, 2, *, Yingchun Zhu2, Bingshe Xu3, Xueji Zhang4, *, Khalid A. Al-Ghanim5, Shahid Mahboob5, 6

Abstract | Support Info
icon-htmlFull Text Html
icon-pdf-smPDF w/ Links
icon-citExport Citation
Figures
+Show more

Nano-Micro Lett. (2019) 11: 29

First Online: 29 March 2019 (Letter)

DOI:10.1007/s40820-019-0259-z

*Corresponding author. E-mail: yszhou1981@gmail.com (Yongsheng Zhou); zhangxueji@ustb.edu.cn (Xueji Zhang)

 

Abstract

 


Toc

Lithium-ion batteries (LIBs) are considered new generation of large-scale energy-storage devices. However, LIBs suffer from a lack of desirable anode materials with excellent specific capacity and cycling stability. In this work, we design a novel hierarchical structure constructed by encapsulating cobalt sulfide nanowires within nitrogen-doped porous branched carbon nanotubes (NBNTs) for LIBs. The unique hierarchical Co9S8@NBNT electrode displayed a reversible specific capacity of 1310 mAh g‒1 at a current density of 0.1 A g−1, and was able to maintain a stable reversible discharge capacity of 1109 mAh g−1 at a current density of 0.5 A g−1 with coulombic efficiency reaching almost 100% for 200 cycles. The excellent rate and cycling capabilities can be ascribed to the hierarchical porosity of the one-dimensionalCo9S8@NBNT internetworks, the incorporation of nitrogen doping, and the carbon nanotube confinement of the active cobalt sulfide nanowires offering a proximate electron pathway for the isolated nanoparticles and shielding of the cobalt sulfide nanowires from pulverization over long cycling periods.


 

Keywords

Lithium-ion batteries; Nitrogen doping; Cobalt sulfide; Branched carbon nanotubes

 

Full Text Html

1 Introduction

    Recently, rechargeable energy storage systems have attracted a great deal of interest because of the escalating requirements of various applications such as hybrid electric vehicles and electronic devices [1-4]. Among various alternatives, lithium-ion batteries (LIBs) have attracted unprecedented attention owing to increasing market demand [5-8]. However, LIBs suffer from a lack of high-performance anode materials, which hinders their practical application [7-11]. Extensive studies have been conducted to solve these problems by structure design to achieve different charge storage mechanisms [10, 11]. Recently, various transition metal sulfides have been proposed because of their high theoretical capacities [12-17]. However, they are limited by their poor rate performance and sharp capacity fading caused by their low electronic conductivity and large volume changes during the charging/discharging process [9, 10, 18]. In recent years, nanostructured carbonaceous materials have been widely investigated to overcome these low capacity and kinetic limitations [18]. Carbon nanotubes (CNTs), one of these promising nanostructured carbonaceous materials with excellent electrical conductivity, large specific surface area, electrochemical and thermal stabilities, and easy ion accessibility, are expected to be an important option for LIBs [19-21]. In particular, Li+ ions can be intercalated not only into the intertube channel, but also into the inner space of the tube cavity, leading to excellent rate performance [22]. However, using CNTs as active materials is difficult because of their limited capacity [23–26].
    Therefore, much work has been carried out to design new nanostructured hybrids for the construction of transition metal sulfide/carbon-based material composites as next-generation anodes [27–32]. One-dimensional (1D) nanomaterials, which have a large accessible area, fast ion diffusion, and percolated electron transport, are considered to be ideal nanoscale building blocks for construction of multidimensional and multifunctional electrode configurations for advanced electrochemical energy storage [27, 33-35]. Hence, construction of integrated 1D nanostructured transition metal sulfides with CNTs can also be regarded as an attractive strategy for developing high-performance anode materials for LIBs. Although high-capacity transition metal sulfides have been incorporated onto the surface of hierarchical CNT networks to improve the rate and cycling performances, these active materials are still unstable because of surface exposure and interparticle aggregation [24].
    Herein, we demonstrate a unique hierarchical hybrid architecture of Co9S8@NBNT for LIBs, wherein cobalt sulfide nanowires are encapsulated inside N-doped porous branched carbon nanotubes (NBNTs) (Fig. 1). Such a unique electrode configuration is expected to have the following features: (i) the 3D networks of NBNTs significantly enhance the electronic conductivity of the hybrid, promoting Li+ diffusion and electron transport through the 3D interconnected pathway; and (ii) the NBNT branches will inhibit the volume expansion of the encapsulated cobalt sulfide during the charge/discharge processes so as to maintain the structural stability.

Fig. 1 Illustration of lithium-ion storage in a Co9S8@NBNT electrode

Fig. 1 Illustration of lithium-ion storage in a Co9S8@NBNT electrode

2 Experimental

2.1 Materials Synthesis
    The Co9S8@NBNT was synthesized by a catalytic decomposition reaction of polyacrylonitrile (PAN) on a Co/MgO catalyst in the presence of sodium polysulfide. The Co/MgO catalyst was prepared as follows. Co(NO3)2•6H2O and Mg(NO3)2•6H2O were mechanically mixed and ground, and then calcined at 600 °C for 1 h in air to decompose the precursor and yield a cluster made of Co and Mg oxides. The formed powder was then reduced in H2 (100 sccm) and Ar (200 sccm) for 30 min at 600 °C to form Co nanoclusters supported on MgO particles, which were collected and used as the catalyst.
    A sodium polysulfide (Na-poly-S) solution was prepared from sulfur (6 g, Puriss, precipitated, 99.5–100.5%) and sodium disulfide (nonahydrate, 18 g, ACS reagent 98%) in water (240 g, distilled) by sonication and stirring overnight with mild heating (40 °C). L-Ascorbic acid (80 mg, 99%) was dissolved in water (26 g, distilled) in a 40 mL glass vial with a PET cap. Subsequently 4 g of the Na-poly-S solution was added and hand shaken. Hydrochloric acid (0.1 mL, Puranal 37%, diluted to 5 M) was then added and the vial was hand shaken. The vial was closed, hand shaken and sonicated at 40 °C for 30 min. The Co/MgO catalyst particles and PAN powder were placed in a graphite crucible enclosed within a graphite susceptor, and heated up to the reaction temperature using an induction furnace with a flow of Ar (2300 sccm) and H2 (100 sccm). H2 was allowed to bubble through the vial. The temperature of the susceptor was controlled to ensure that Co/MgO catalyst particles were heated to 1000 °C. After growth for 15 min, the H2 flow was stopped and the chamber was cooled down to room temperature. During the cooling process, the system was purged with Ar to prevent a backflow of air from the exhaust line.
    The obtained product was washed three times by replacing the liquid products with distilled water and HCl, allowing soluble components to diffuse out of the product for at least 2 h. The washed product was freeze dried to remove the liquid component. The resulting product was cut into discs with a razor blade. Prior to use as an anode, the discs were dried in a vacuum oven at 90 °C for 1 h and directly transferred to an argon-filled glove box.
    Co9S8@CNT was obtained by a catalytic decomposition reaction of dimethyl sulfide (C2H6S) on the Co/MgO catalyst, which was reported in our previous work [34].
    Commercial multiwalled CNTs were obtained from Shenzhen Nano Co. Ltd.
2.2 Characterization
    The products were characterized by scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM, JEM-2010). N2 sorption analysis was conducted on an ASAP 2020 accelerated surface area and porosimetry instrument (Micromeritics) equipped with an automated surface area analyzer at 77 K, using Barrett-Emmett-Teller (BET) calculations for the surface area. The pore-size distribution (PSD) plot was prepared from the adsorption branch of the isotherm based on a density functional theory (DFT) model. X-ray powder diffraction (XRD) patterns of the sample were recorded using a D/Max-3C diffractometer equipped with a Cu-Kα X-ray source. Raman spectra were measured using a Renishaw inVia Raman spectrometer system (Gloucestershire, UK) equipped with a Leica DMLB microscope (Wetzlar, Germany) and a 17 mW at 633 nm Renishaw helium-neon laser source. X-ray photoelectron spectroscopy (XPS) measurements were carried out on a Kratos XSAM 800 spectrometer with a Mg-Kα radiation source. TGA was carried out using a DuPont 2200 thermal analysis station.
2.3 Electrochemical Measurements
    The electrochemical tests were conducted by cycling two-electrode 2032 coin cells with Li discs as both the counter and reference electrode, a Celgard 2400 film as the separator, and a mixed slurry consisting of the prepared Co9S8@NBNT structure (80 wt%) with poly(vinylidene fluoride) (PVDF, 20 wt%) in N-methyl-2-pyrrolidone (NMP) without conducting agents. The Co9S8@NBNT composite electrodes were pressed before being assembled into the coin cells. The loading density, diameter, and thickness of the prepared electrodes were ~1 mg cm-2, ~12 mm, and ~65 to 85 μm, respectively. The electrolyte was 1 M LiPF6 in a 50:50 (w/w) mixture of ethylene carbonate and diethyl carbonate. Cyclic voltammetry and electrochemical impedance spectroscopy were conducted with a CHI 660C electrochemical workstation.

3 Results and Discussion

    The morphology of the Co9S8@NBNT nanocomposites is shown in Fig. 2a. Energy-dispersive X-ray (EDX) spectroscopy firmly demonstrated the existence of C, Co, S, and N (possible locations for N incorporation into the CNTs are shown in Fig. 2c). Figures 2b and S1 are high-magnification scanning electron microscopy images of Co9S8@NBNT, with the porous structures indicated by arrows. Figure 2d contains TEM image of the Co9S8@NBNT and inset shows HRTEM image of the boxed area; the porous structure and filled nanowires are clearly shown. Figure 2e is an enlargement of the boxed area shown in the inset of Fig. 2d. It is clearly shown that the nanowires encapsulated in the NBNTs consisted of well-crystallized Co9S8 cores with a unit cell parameter of a = 0.9907 nm (JCPDS No. 75-2023). The multilayered carbon sheath exhibited an interlayer spacing of 0.34 nm, which corresponds well to the interplanar distance of the (001) planes of graphite. The selected-area electron diffraction (SAED) pattern shows the sharp spots that could be indexed as the reflections of cubic Co9S8 with the [1,−1,0] axis parallel to the electron beam. Remarkably, the specific surface area of Co9S8@NBNT could reach up to 985 m2 g−1 (Fig. S2). The corresponding PSD, estimated from the adsorption branches of the isotherms based on a DFT model, clearly shows the presence of multiple porosities as small as a few nanometers (Fig. 2f). As shown in Fig. 2g, the distinct diffraction peaks in XRD pattern can be assigned to cobalt sulfide (JCPDS No. 75-2023) and graphite. The as-obtained Co9S8@NBNT was also characterized by Raman spectroscopy (Fig. S3) and XPS (Fig. S4). The N 1s band of Co9S8@NBNT can be deconvoluted into three characteristic peaks: pyridinic, pyrrolic, and graphitic N species located at 398.6, 400.8, and 401.3 eV, respectively. The chemical composition of the NBNTs was estimated as 41.09 wt% Co9S8@NBNT, as determined by TGA analysis (Fig. S5).

Fig. 2 a SEM image and corresponding EDX spectra of Co9S8@NBNT. b High-magnification SEM images of Co9S8@NBNT; the porous structures are indicated by arrows. c Schematic diagram of N-doped CNTs. d TEM image of Co9S8@NBNT. Inset is HRTEM image of the boxed area. e Enlargement of the boxed area shown in d and its corresponding SAED pattern (inset). f Pore-size distributions,  g XRD spectra of Co9S8@NBNT

Fig. 2 a SEM image and corresponding EDX spectra of Co9S8@NBNT. b High-magnification SEM images of Co9S8@NBNT; the porous structures are indicated by arrows. c Schematic diagram of N-doped CNTs. d TEM image of Co9S8@NBNT. Inset is HRTEM image of the boxed area. e Enlargement of the boxed area shown in d and its corresponding SAED pattern (inset). f Pore-size distributions, g XRD spectra of Co9S8@NBNT

    The lithium-storage properties of the Co9S8@NBNT nanohybrid were evaluated by conducting various electrochemical measurements. Figure 3a shows the first threeCV curves of the Co9S8@NBNT electrode in the potential range of 0−3.0 V vs. Li at a scanning rate of 0.5 mV s−1. During the first scan, a strong peak was observed at ~1.9 V, which can be attributed to Li insertion into the Co9S8 lattice to form cubic Li2Co9S8, as illustrated by the following reaction: Co9S8 +2Li+ + 2e → Li2(Co9S8). Another peak close to 1.3 V was also observed in the CV curves, corresponding to the formation of Co and Li2S following the reaction: Li2(Co9S8) + 14Li+ + 14e → 9Co + 8Li2S. During charging (Li extraction), a pronounced peak at around 2.3 V can be found, which was attributed to the reconversion reaction of Co with Li2S to reform Co9S8. In the subsequent cycle onwards, it is important to note that the CV curves almost overlapped, indicating the stable and superior reversibility of the prepared Co9S8@NBNT. Typical galvanostatic charge/discharge (GCD) curves of the nanohybrid are in agreement with the above CV curves (Fig. S6). The first reversible capacity of the Co9S8@NBNT nanohybrid is 1310 mAh g−1 at a current density of 0.1 A g−1. The rate capabilities of the Co9S8@NBNT, Co9S8@CNT, and CNT samples are presented in Fig. 3b. The Co9S8@NBNT nanohybrid electrode delivers a high reversible capacity of ~1109 mAh g−1 at a current density of 0.5 A g−1 with no significant decay of capacity after 200 cycles, demonstrating excellent reversibility. The capacity retention of Co9S8@NBNT was greater than those of the Co9S8@CNT and CNT samples at 500 mA g−1, as shown in Fig. S7. To further confirm this benefit, EIS measurements were carried out at the initial state and after being charged/discharged for 200 cycles (Fig. S8). The Nyquist plots of the Co9S8@NBNT, Co9S8@CNT, and CNT samples all show a straight line in the low-frequency region, indicating Warburg-type resistance caused by ion diffusion in the electrode, and an arc in the high-frequency region. The diameter of the arc represents the charge transfer resistance (Rt). Compared with the Co9S8@CNT and CNT composites, the Co9S8@NBNT composite shows a lower Rt, which demonstrates that the Co9S8@NBNT composite has much smaller interfacial charge-transfer and lithium-ion diffusion resistances than that of the Co9S8@CNT and CNT anodes.

Fig. 3 a CV curves of the LIBs with Co9S8@NBNT. b Rate performance at different current densities of Co9S8@NBNT, Co9S8@CNT, and CNT. c Long-term cycling performances of the Co9S8@NBNT anode at different current densities of 1000, 2000, and 5000 mA g−1

Fig. 3 a CV curves of the LIBs with Co9S8@NBNT. b Rate performance at different current densities of Co9S8@NBNT, Co9S8@CNT, and CNT. c Long-term cycling performances of the Co9S8@NBNT anode at different current densities of 1000, 2000, and 5000 mA g−1

    The outstanding cycling capability of Co9S8@NBNT at various current densities shown in Fig. 3c further proves its remarkable reversibility and stability. The capacity of the Co9S8@NBNT electrode reached 945 mAh g−1 after the first 2500 cycles at 1000 mA g−1, 889 mAh g−1 at 2000 mA g−1 after 1500 cycles, and 779 mAh g−1 after another 1000 cycles at 5000 mA g−1, respectively. The coulombic efficiency of the Co9S8@NBNT electrode was nearly 100% after the first few cycles. The irreversible capacity loss in the first cycle can mainly be attributed to the incomplete extraction of Li ions as a result of lithium being trapped in the porous electrodes and unable to be released in the first cycle, the irreversible formation of a solid-electrolyte interface layer, and the formation of insulating Li2S, which is generally observed for nanostructured conversion-based anode materials [35, 36]. This result is consistent with the CV results in which the cathodic peaks only exist in the first cycle and are absent in subsequent cycles.

Fig. 4 a Raman spectra of the pristine and cycled electrode. b SEM and c TEM images of Co9S8@NBNT after 200 cycles. d Schematic illustration of electron transfer and lithium-ion storage in the Co9S8@NBNT electrode

Fig. 4 a Raman spectra of the pristine and cycled electrode. b SEM and c TEM images of Co9S8@NBNT after 200 cycles. d Schematic illustration of electron transfer and lithium-ion storage in the Co9S8@NBNT electrode

    In order to confirm the structural integrity associated with the cycling stability, we carried out a postmortem study using Raman, field-emission SEM, and TEM examinations. Raman spectra of the pristine and cycled electrodes are shown in Fig. 4a. The active material in the electrode was well-maintained after long-term cycling. Figure 4b shows a SEM image of the Co9S8@NBNT nanohybrid after cycling. By comparison with the fresh electrode (Fig. 2a), it can be seen that the hierarchical structure of the Co9S8@NBNT electrode was preserved after 200 charging/discharging cycles. The cobalt sulfide in the darker color was still encapsulated within the NBNTs, as can be seen in the TEM image (Fig. 4c). Moreover, the porous structures were preserved (indicated by arrows in Figs. 4c and S9). As shown in Fig. 4d, the active cobalt sulfide nanowires could expand slightly in the length direction while expansion in the width direction was prevented by the NBNT wall. Clearly, the size, shape, and structural integrity the 1D Co9S8@NBNT were well-retained. These results demonstrate the great structural advantages of such structures. Firstly, the volume expansion and mechanical stress can be relieved during cycling by expansion along the available void space of the tube (Fig. 4d). Secondly, the porous structure plus the high specific surface area (Figs. 2f and S1) of Co9S8@NBNT nanohybrid can shorten the ion-diffusion distance by providing 3D interconnected NBNT networks and conducting pathways of the CNT branches to facilitate electron transport. When the lithium ions were transported through the interconnected porous channels, they could penetrate into the tube interiors through the micro/mesopores (Fig. 4d). Thirdly, the pyridinic and pyrrolic nitrogen (Fig. S4) located at defects were beneficial for adsorption of Li and provided additional Li storage sites [37-39].

4 Conclusions

    In summary, we have designed and prepared a novel hierarchical structure constructed by encapsulating cobalt sulfide nanowires within nitrogen-doped porous branched carbon nanotubes. The Co9S8@NBNT nanohybrid exhibited remarkable electrochemical performance as an anode material in LIBs with a very high specific capacity of up to 1310 mAh g−1 at a current density of 0.1 A g−1, outstanding rate capability, and long cycle life. The Co9S8@NBNT with hierarchical porosity, the incorporation of nitrogen doping, and interconnected NBNT networks played a role in improving the rate capability by allowing rapid Li+ diffusion and facilitating electronic transport. The CNT-confinement of the active cobalt sulfide nanowires offered a proximate electron pathway for the isolated nanoparticles and shielding of the cobalt sulfide nanowires from pulverization for long cycling time periods. Such a strategy could be readily extended to other materials for energy storage and conversion applications.

Acknowledgments

    This work was financially supported by the Natural Science Foundation of Anhui Province (KJ2018A0534), the research fund of Anhui Science and Technology University (ZRC2014402), and Materials Science and Engineering Key Discipline Foundation (AKZDXK2015A01). The authors would like to express their sincere appreciation to the Deanship of Scientific Research at King Saud University for its funding of this research through the Research Group Project No. Prolific Research Group No. 1436-011.

 

References

[1] J.M. Tarascon, M. Armand, Issues and challenges facing rechargeable lithium Batteries. Nature 414(6861), 359-367 (2001). http://doi.org/10.1038/35104644
[2] Y.P. Wang, Y.F. Zhang, J.R. Shi, X.Z. Kong, X.X. Cao, S.Q. Liang, G.Z. Cao, A.Q. Pan, Tin sulfide nanoparticles embedded in sulfur and nitrogen dual-doped mesoporous carbon fibers as high-performance anodes with battery-capacitive sodium storage. Energy Storage Mater. (2018, in press). https://doi.org/10.1016/j.ensm.2018.08.014
[3] Y.P. Wang, Y.F. Zhang, J.R. Shi, A.Q. Pan, F. Jiang, S.Q. Liang, G.Z. Cao, S-doped porous carbon confined SnS nanospheres with enhanced electrochemical performance for sodium-ion batteries. J. Mater. Chem. A 6, 18286 (2018). https://doi.org/10.1039/C8TA06106H
[4] B. Yin, X.X. Cao, A.Q. Pan, Z.G. Luo, S. Dinesh, J.D. Lin, Y. Tang, S.Q. Liang, G.Z. Cao, Encapsulation of CoSx nanocrystals into N/S co-doped honeycomb-like 3D porous carbon for high-performance lithium storage. Adv. Sci. 5, 1800829 (2018). https://doi.org/10.1002/advs.201800829
[5] Z. Li, Q. He, X. Xu, Y. Zhao, X. Liu et al., A 3D nitrogen-doped graphene/TiN nanowires composite as a strong polysulfide anchor for lithium-sulfur batteries with enhanced rate performance and high areal capacity. Adv. Mater. 30(45), 1804089 (2018). http://doi.org/10.1002/adma.201804089
[6] J.X. Zhu, C.J. Tang, Z.C. Zhuang, C.W. Shi, N.R. Li, L. Zhou, L.Q. Mai, Porous and low-crystalline manganese silicate hollow spheres wired by graphene oxide for high-performance lithium and sodium storage. ACS Appl. Mater. Interfaces 9 (29), 24584–24590 (2017). http://doi.org/10.1021/acsami.7b06088
[7] J.J. Chen, Z.Y. Mao, L.X. Zhang, D.J. Wang, R. Xu, L.-J. Bie, B.D. Fahlman, Nitrogen deficient graphitic carbon nitride with enhanced performance for lithium ion battery anodes. ACS Nano 11, 12650-12657 (2017). http://doi.org/10.1021/acsnano.7b07116
[8] J.Y. Liu, X.X. Li, J.R. Huang, J.J. Li, P. Zhou, J.H. Liu, X.J. Huang, Three-dimensional graphene-based nanocomposites for high energy density Li-ion batteries. J. Mater. Chem. A 5, 5977-5994 (2017). http://doi.org/10.1039/C7TA00448F
[9] J.J. Chen, Z.Y. Mao, L.X. Zhang, Y.H. Tang, D.J. Wang, L.J. Bie, B.D. Fahlman, Direct production of nitrogen-doped porous carbon from urea via magnesiothermic reduction. Carbon 130, 41-47 (2018). https://doi.org/10.1016/j.carbon.2017.12.125
[10] Y. T. Zhong, B. Li, S. M. Li, S. Y. Xu, Z. H. Pan, Q. M. Huang, L. D. Xing, C. S. Wang, W. S. Li, Bi nanoparticles anchored in N-doped porous carbon as anode of high energy density lithium ion battery. Nano-Micro Lett. 10, 56 (2018).  https://doi.org/10.1007/s40820-018-0209-1
[11] Y. Wang, X. Zhang, P. Chen, H. Liao, S. Cheng, In situ preparation of CuS cathode with unique stability and high rate performance for lithium ion batteries. Electrochim. Acta 80, 264–268 (2012). https://doi.org/10.1016/j.electacta.2012.07.004
[12] X. Rui, H. Tan, Q. Yan, Nanostructured metal sulfides for energy storage. Nanoscale 6, 9889–9924 (2014). https://doi.org/10.1039/C4NR03057E
[13] X. Xu, W. Liu, Y. Kim, J. Cho, Nanostructured transition metal sulfides for lithium ion batteries: progress and challenges. Nano Today 9, 604–630 (2014). https://doi.org/10.1016/j.nantod.2014.09.005
[14] L. Zhang, L. Zhou, H.B. Wu, R. Xu, X.W. Lou, Unusual formation of single-crystal manganese sulfide microboxes co-mediated by the cubic crystal structure and shape. Angew. Chem. Int. Ed. 51, 7267–7270 (2012). https://doi.org/10.1002/anie.201202877
[15] A. Puglisi, S. Mondini, S. Cenedese, A.M. Ferretti, N. Santo, A. Ponti, Monodisperse octahedral α-MnS and MnO nanoparticles by the decomposition of manganese oleate in the presence of sulfur. Chem. Mater. 22, 2804–2813 (2010). https://doi.org/ 10.1021/cm903735e
[16] C.L. Dai, J.M. Lim, M.Q. Wang, L.Y. Hu, Y.M. Chen et al., Henkelman, M. W. Xu, Honeycomb-like spherical cathode host constructed from hollow metallic and polar Co9S8 tubules for advanced lithium–sulfur batteries. Adv. Funct. Mater. 1704443 (2018). https://doi.org/10.1002/adfm.201704443
[17] C. Wu, J. Maier, Y. Yu, Generalizable synthesis of metal-sulfides/carbon hybrids with multiscale, hierarchically ordered structures as advanced electrodes for lithium storage. Adv. Mater. 28, 174–180 (2016). https://doi.org/10.1002/adma.201503969
[18] A. Eftekhari, Low voltage anode materials for lithium-ion batteries. Energy Storage Mater. 7, 157 (2017). https://doi.org/10.1016/j.ensm.2017.01.009
[19] G. Che, B.B. Lakshmi, E.R. Fisher, C.R. Martin, Carbon nanotubule membranes for electrochemical energy storage and production. Nature 393(6683), 346-349 (1998). https://doi.org/10.1038/30694
[20] E. Frackowiak, F. Beguin, Electrochemical storage of energy in carbon nanotubes and nanostructured carbons. Carbon 40(10), 1775-1787 (2002). https://doi.org/10.1016/S0008-6223(02)00045-3
[21] Z. Zhou, X. Gao, J. Yan, D. Song, M. Morinaga, A first-principles study of lithium absorption in boron- or nitrogen-doped single-walled carbon nanotubes. Carbon 42(12-13), 2677-2682 (2004). https://doi.org/10.1016/j.carbon.2004.06.019
[22] S.W. Kim, D.H. Seo, H. Gwon, J. Kim, K. Kang, Fabrication of FeF3 Nanoflowers on CNT branches and their application to high power lithium rechargeable batteries. Adv. Mater. 22(46), 5260-5264 (2010). https://doi.org/10.1002/adma.201002879
[23] S. -H. Lee, V. Sridhar, J. -H. Jung, K. Karthikeyan, Y. -S. Lee, R. Mukherjee, N. Koratkar, I. -K. Oh, Graphene--nanotube--iron hierarchical nanostructure as lithium ion battery anode. ACS Nano 7(5), 4242-4251 (2013). https://doi.org/10.1021/nn4007253
[24] B.J. Landi, M.J. Ganter, C.D. Cress, R.A. DiLeo, R.P. Raffaelle, Carbon nanotubes for lithium ion batteries. Energy Environ. Sci. 2, 638-654 (2009). https://doi.org/ 10.1039/B904116H
[25] P. Bhattacharya, M. Kota, D.H. Suh, K.C. Roh, H.S. Park, Biomimetic spider-web-like composites for enhanced rate capability and cycle life of lithium ion battery anodes. Adv. Energy Mater. 7, 1700331(2017). https://doi.org/10.1002/aenm.201700331
[26] H.B. Wu, G. Zhang, L. Yu, X.W. Lou, One-dimensional metal oxide–carbon hybrid nanostructures for electrochemical energy storage. Nanoscale Horiz. 1, 27–40 (2016). https://doi.org/10.1039/C5NH00023H
[27] Y. Zhou, J. Tian, H. Xu, J. Yang, Y. Qian, VS4 nanoparticles rooted by a C-coated MWCNTs as an advanced anode material in lithium ion batteries. Energy Storage Mater. 6, 149–156 (2017). https://doi.org/10.1016/j.ensm.2016.10.010
[28] D.L. Chao, P. Liang, Z. Chen, L.Y. Bai, H. Shen et al., Pseudocapacitive Na-Ion storage boosts highrate and areal capacity of self-branched 2D layered metal chalcogenide nanoarrays. ACS Nano 10, 10211–10219 (2016). https://doi.org/10.1021/acsnano.6b05566
[29] J. Xie, S. Liu, G. Cao, T. Zhu, X. Zhao, Self-assembly of CoS2/graphene nanoarchitecture by a facile one-pot route and its improved electrochemical Li storage properties. Nano Energy 2, 49–56 (2013). https://doi.org/10.1016/j.nanoen.2012.07.010
[30] W. Lv, Z. Li, Y. Deng, Q.H. Yang, F. Kang, Graphene-based materials for electrochemical energy storage devices: opportunities and challenges. Energy Storage Mater. 2, 107–138 (2016). https://doi.org/10.1016/j.ensm.2015.10.002
[31] X. Xu, S. Ji, M. Gu, J. Liu, In situ synthesis of mns hollow microspheres on reduced graphene oxide sheets as high-capacity and long-life anodes for Li- and Na-Ion batteries. ACS Appl. Mater. Interfaces 7, 20957–20964 (2015). https://doi.org/10.1021/ acsami.5b06590
[32] M.S. Park, G.X. Wang, Y.M. Kang, D. Wexler, S.X. Dou, H.K. Liu, Preparation and electrochemical properties of SnO2 nanowires for application in lithium-ion batteries. Angew. Chem. Int. Ed. 46, 750–753(2007). https://doi.org/10.1002/anie.200603309
[33] C.K. Chan, H. Peng, G. Liu, K. McIlwrath, X.F. Zhang, R.A. Huggins, Y. Cui, High performance lithium battery anodes using silicon nanowires. Nat. Nanotechnol. 3, 31–35 (2008).https://doi.org/10.1038/nnano.2007.411
[34] Y.S. Zhou, Y.C. Zhu, G.H. Du, B.S. Xu, Single-step synthesis of cobalt sulfide nanowires encapsulated within carbon nanotubes. J. Nanosci. Nanotechno. 13, 6934-6939(2013). https://doi.org/10.1166/jnn.2013.7758
[35] Y. Matsumura, S. Wang, J. Mondori, Mechanism leading to irreversible capacity loss in Li ion rechargeable batteries. J. Electrochem. Soc. 142, 2914 (1995). https://doi.org/ 10.1149/1.2048665
[36] Y.Q. Chang, H. Li, L. Wu, T.H. Lu, Irreversible capacity loss of graphite electrode in lithium-ion batteries. J. Power Sources 68, 187 (1991). https://doi.org/10.1016/S0378-7753(96)02549-9
[37] F. Zheng, Y. Yang, Q. Chen, High lithium anodic performance of highly nitrogen-doped porous carbon prepared from a metal-organic framework. Nat. Commun. 5, 5261 (2014). https://doi.org/10.1038/ncomms6261
[38] J.R. Dahn, T. Zheng, Y. Liu, J. S. Xue, Mechanisms for lithium insertion in carbonaceous materials. Science 270, 590-593 (1995). https://doi.org/10.1126/science.270.5236.590
[39] X.K. Kong, Q.W. Chen, Improved performance of graphene doped with pyridinic N for li-ion battery: a density functional theory model. Phys. Chem. Chem. Phys. 15, 12982-12987 (2013). https://doi.org/10.1039/C3CP51987B

References

[1] J.M. Tarascon, M. Armand, Issues and challenges facing rechargeable lithium Batteries. Nature 414(6861), 359-367 (2001). http://doi.org/10.1038/35104644
[2] Y.P. Wang, Y.F. Zhang, J.R. Shi, X.Z. Kong, X.X. Cao, S.Q. Liang, G.Z. Cao, A.Q. Pan, Tin sulfide nanoparticles embedded in sulfur and nitrogen dual-doped mesoporous carbon fibers as high-performance anodes with battery-capacitive sodium storage. Energy Storage Mater. (2018, in press). https://doi.org/10.1016/j.ensm.2018.08.014
[3] Y.P. Wang, Y.F. Zhang, J.R. Shi, A.Q. Pan, F. Jiang, S.Q. Liang, G.Z. Cao, S-doped porous carbon confined SnS nanospheres with enhanced electrochemical performance for sodium-ion batteries. J. Mater. Chem. A 6, 18286 (2018). https://doi.org/10.1039/C8TA06106H
[4] B. Yin, X.X. Cao, A.Q. Pan, Z.G. Luo, S. Dinesh, J.D. Lin, Y. Tang, S.Q. Liang, G.Z. Cao, Encapsulation of CoSx nanocrystals into N/S co-doped honeycomb-like 3D porous carbon for high-performance lithium storage. Adv. Sci. 5, 1800829 (2018). https://doi.org/10.1002/advs.201800829
[5] Z. Li, Q. He, X. Xu, Y. Zhao, X. Liu et al., A 3D nitrogen-doped graphene/TiN nanowires composite as a strong polysulfide anchor for lithium-sulfur batteries with enhanced rate performance and high areal capacity. Adv. Mater. 30(45), 1804089 (2018). http://doi.org/10.1002/adma.201804089
[6] J.X. Zhu, C.J. Tang, Z.C. Zhuang, C.W. Shi, N.R. Li, L. Zhou, L.Q. Mai, Porous and low-crystalline manganese silicate hollow spheres wired by graphene oxide for high-performance lithium and sodium storage. ACS Appl. Mater. Interfaces 9 (29), 24584–24590 (2017). http://doi.org/10.1021/acsami.7b06088
[7] J.J. Chen, Z.Y. Mao, L.X. Zhang, D.J. Wang, R. Xu, L.-J. Bie, B.D. Fahlman, Nitrogen deficient graphitic carbon nitride with enhanced performance for lithium ion battery anodes. ACS Nano 11, 12650-12657 (2017). http://doi.org/10.1021/acsnano.7b07116
[8] J.Y. Liu, X.X. Li, J.R. Huang, J.J. Li, P. Zhou, J.H. Liu, X.J. Huang, Three-dimensional graphene-based nanocomposites for high energy density Li-ion batteries. J. Mater. Chem. A 5, 5977-5994 (2017). http://doi.org/10.1039/C7TA00448F
[9] J.J. Chen, Z.Y. Mao, L.X. Zhang, Y.H. Tang, D.J. Wang, L.J. Bie, B.D. Fahlman, Direct production of nitrogen-doped porous carbon from urea via magnesiothermic reduction. Carbon 130, 41-47 (2018). https://doi.org/10.1016/j.carbon.2017.12.125
[10] Y. T. Zhong, B. Li, S. M. Li, S. Y. Xu, Z. H. Pan, Q. M. Huang, L. D. Xing, C. S. Wang, W. S. Li, Bi nanoparticles anchored in N-doped porous carbon as anode of high energy density lithium ion battery. Nano-Micro Lett. 10, 56 (2018).  https://doi.org/10.1007/s40820-018-0209-1
[11] Y. Wang, X. Zhang, P. Chen, H. Liao, S. Cheng, In situ preparation of CuS cathode with unique stability and high rate performance for lithium ion batteries. Electrochim. Acta 80, 264–268 (2012). https://doi.org/10.1016/j.electacta.2012.07.004
[12] X. Rui, H. Tan, Q. Yan, Nanostructured metal sulfides for energy storage. Nanoscale 6, 9889–9924 (2014). https://doi.org/10.1039/C4NR03057E
[13] X. Xu, W. Liu, Y. Kim, J. Cho, Nanostructured transition metal sulfides for lithium ion batteries: progress and challenges. Nano Today 9, 604–630 (2014). https://doi.org/10.1016/j.nantod.2014.09.005
[14] L. Zhang, L. Zhou, H.B. Wu, R. Xu, X.W. Lou, Unusual formation of single-crystal manganese sulfide microboxes co-mediated by the cubic crystal structure and shape. Angew. Chem. Int. Ed. 51, 7267–7270 (2012). https://doi.org/10.1002/anie.201202877
[15] A. Puglisi, S. Mondini, S. Cenedese, A.M. Ferretti, N. Santo, A. Ponti, Monodisperse octahedral α-MnS and MnO nanoparticles by the decomposition of manganese oleate in the presence of sulfur. Chem. Mater. 22, 2804–2813 (2010). https://doi.org/ 10.1021/cm903735e
[16] C.L. Dai, J.M. Lim, M.Q. Wang, L.Y. Hu, Y.M. Chen et al., Henkelman, M. W. Xu, Honeycomb-like spherical cathode host constructed from hollow metallic and polar Co9S8 tubules for advanced lithium–sulfur batteries. Adv. Funct. Mater. 1704443 (2018). https://doi.org/10.1002/adfm.201704443
[17] C. Wu, J. Maier, Y. Yu, Generalizable synthesis of metal-sulfides/carbon hybrids with multiscale, hierarchically ordered structures as advanced electrodes for lithium storage. Adv. Mater. 28, 174–180 (2016). https://doi.org/10.1002/adma.201503969
[18] A. Eftekhari, Low voltage anode materials for lithium-ion batteries. Energy Storage Mater. 7, 157 (2017). https://doi.org/10.1016/j.ensm.2017.01.009
[19] G. Che, B.B. Lakshmi, E.R. Fisher, C.R. Martin, Carbon nanotubule membranes for electrochemical energy storage and production. Nature 393(6683), 346-349 (1998). https://doi.org/10.1038/30694
[20] E. Frackowiak, F. Beguin, Electrochemical storage of energy in carbon nanotubes and nanostructured carbons. Carbon 40(10), 1775-1787 (2002). https://doi.org/10.1016/S0008-6223(02)00045-3
[21] Z. Zhou, X. Gao, J. Yan, D. Song, M. Morinaga, A first-principles study of lithium absorption in boron- or nitrogen-doped single-walled carbon nanotubes. Carbon 42(12-13), 2677-2682 (2004). https://doi.org/10.1016/j.carbon.2004.06.019
[22] S.W. Kim, D.H. Seo, H. Gwon, J. Kim, K. Kang, Fabrication of FeF3 Nanoflowers on CNT branches and their application to high power lithium rechargeable batteries. Adv. Mater. 22(46), 5260-5264 (2010). https://doi.org/10.1002/adma.201002879
[23] S. -H. Lee, V. Sridhar, J. -H. Jung, K. Karthikeyan, Y. -S. Lee, R. Mukherjee, N. Koratkar, I. -K. Oh, Graphene--nanotube--iron hierarchical nanostructure as lithium ion battery anode. ACS Nano 7(5), 4242-4251 (2013). https://doi.org/10.1021/nn4007253
[24] B.J. Landi, M.J. Ganter, C.D. Cress, R.A. DiLeo, R.P. Raffaelle, Carbon nanotubes for lithium ion batteries. Energy Environ. Sci. 2, 638-654 (2009). https://doi.org/ 10.1039/B904116H
[25] P. Bhattacharya, M. Kota, D.H. Suh, K.C. Roh, H.S. Park, Biomimetic spider-web-like composites for enhanced rate capability and cycle life of lithium ion battery anodes. Adv. Energy Mater. 7, 1700331(2017). https://doi.org/10.1002/aenm.201700331
[26] H.B. Wu, G. Zhang, L. Yu, X.W. Lou, One-dimensional metal oxide–carbon hybrid nanostructures for electrochemical energy storage. Nanoscale Horiz. 1, 27–40 (2016). https://doi.org/10.1039/C5NH00023H
[27] Y. Zhou, J. Tian, H. Xu, J. Yang, Y. Qian, VS4 nanoparticles rooted by a C-coated MWCNTs as an advanced anode material in lithium ion batteries. Energy Storage Mater. 6, 149–156 (2017). https://doi.org/10.1016/j.ensm.2016.10.010
[28] D.L. Chao, P. Liang, Z. Chen, L.Y. Bai, H. Shen et al., Pseudocapacitive Na-Ion storage boosts highrate and areal capacity of self-branched 2D layered metal chalcogenide nanoarrays. ACS Nano 10, 10211–10219 (2016). https://doi.org/10.1021/acsnano.6b05566
[29] J. Xie, S. Liu, G. Cao, T. Zhu, X. Zhao, Self-assembly of CoS2/graphene nanoarchitecture by a facile one-pot route and its improved electrochemical Li storage properties. Nano Energy 2, 49–56 (2013). https://doi.org/10.1016/j.nanoen.2012.07.010
[30] W. Lv, Z. Li, Y. Deng, Q.H. Yang, F. Kang, Graphene-based materials for electrochemical energy storage devices: opportunities and challenges. Energy Storage Mater. 2, 107–138 (2016). https://doi.org/10.1016/j.ensm.2015.10.002
[31] X. Xu, S. Ji, M. Gu, J. Liu, In situ synthesis of mns hollow microspheres on reduced graphene oxide sheets as high-capacity and long-life anodes for Li- and Na-Ion batteries. ACS Appl. Mater. Interfaces 7, 20957–20964 (2015). https://doi.org/10.1021/ acsami.5b06590
[32] M.S. Park, G.X. Wang, Y.M. Kang, D. Wexler, S.X. Dou, H.K. Liu, Preparation and electrochemical properties of SnO2 nanowires for application in lithium-ion batteries. Angew. Chem. Int. Ed. 46, 750–753(2007). https://doi.org/10.1002/anie.200603309
[33] C.K. Chan, H. Peng, G. Liu, K. McIlwrath, X.F. Zhang, R.A. Huggins, Y. Cui, High performance lithium battery anodes using silicon nanowires. Nat. Nanotechnol. 3, 31–35 (2008). https://doi.org/10.1038/nnano.2007.411
[34] Y.S. Zhou, Y.C. Zhu, G.H. Du, B.S. Xu, Single-step synthesis of cobalt sulfide nanowires encapsulated within carbon nanotubes. J. Nanosci. Nanotechno. 13, 6934-6939(2013). https://doi.org/10.1166/jnn.2013.7758
[35] Y. Matsumura, S. Wang, J. Mondori, Mechanism leading to irreversible capacity loss in Li ion rechargeable batteries. J. Electrochem. Soc. 142, 2914 (1995). https://doi.org/ 10.1149/1.2048665
[36] Y.Q. Chang, H. Li, L. Wu, T.H. Lu, Irreversible capacity loss of graphite electrode in lithium-ion batteries. J. Power Sources 68, 187 (1991). https://doi.org/10.1016/S0378-7753(96)02549-9
[37] F. Zheng, Y. Yang, Q. Chen, High lithium anodic performance of highly nitrogen-doped porous carbon prepared from a metal-organic framework. Nat. Commun. 5, 5261 (2014). https://doi.org/10.1038/ncomms6261
[38] J.R. Dahn, T. Zheng, Y. Liu, J. S. Xue, Mechanisms for lithium insertion in carbonaceous materials. Science 270, 590-593 (1995). https://doi.org/10.1126/science.270.5236.590
[39] X.K. Kong, Q.W. Chen, Improved performance of graphene doped with pyridinic N for li-ion battery: a density functional theory model. Phys. Chem. Chem. Phys. 15, 12982-12987 (2013). https://doi.org/10.1039/C3CP51987B

Citation Information

Yongsheng Zhou, Yingchun Zhu, Bingshe Xu, Xueji Zhang, Khalid A. Al-Ghanim, Shahid Mahboob, Cobalt Sulfide Confined in N-doped Porous Branched Carbon Nanotubes for Lithium-Ion Batteries. Nano-Micro Lett.(2019) 11: 29. https://doi.org/10.1007/s40820-019-0259-z

History

Received: 18 February 2019 / Accepted: 15 March 2019 / Published online: 29 March 2019


Additional Info

  • Type of Publishing: JOUR - Journal
  • Title: Cobalt Sulfide Confined in N-doped Porous Branched Carbon Nanotubes for Lithium-Ion Batteries
  • Author: Yongsheng Zhou, Yingchun Zhu, Bingshe Xu, Xueji Zhang, Khalid A. Al-Ghanim, Shahid Mahboob
  • Year: 2019
  • Volume: 11
  • Journal Name: Nano-Micro Letters
  • ISSN: 2150-5551
  • URL: http://dx.doi.org/10.1007/s40820-019-0259-z
  • Abstract: Lithium-ion batteries (LIBs) are considered new generation of large-scale energy-storage devices. However, LIBs suffer from a lack of desirable anode materials with excellent specific capacity and cycling stability. In this work, we design a novel hierarchical structure constructed by encapsulating cobalt sulfide nanowires within nitrogen-doped porous branched carbon nanotubes (NBNTs) for LIBs. The unique hierarchical Co9S8@NBNT electrode displayed a reversible specific capacity of 1310 mAh g‒1 at a current density of 0.1 A g−1, and was able to maintain a stable reversible discharge capacity of 1109 mAh g−1 at a current density of 0.5 A g−1 with coulombic efficiency reaching almost 100% for 200 cycles. The excellent rate and cycling capabilities can be ascribed to the hierarchical porosity of the one-dimensionalCo9S8@NBNT internetworks, the incorporation of nitrogen doping, and the carbon nanotube confinement of the active cobalt sulfide nanowires offering a proximate electron pathway for the isolated nanoparticles and shielding of the cobalt sulfide nanowires from pulverization over long cycling periods.
  • Publish Date: Friday, 29 March 2019
  • Start Page: 29
  • DOI: 10.1007/s40820-019-0259-z