Novel Insights into Energy Storage Mechanism of Aqueous Rechargeable Zn/MnO2 Batteries with Participation of Mn2+

View ResearcherID and ORCID

Yongfeng Huang1, 2, #, Jian Mou1, #, Wenbao Liu1, 2, Xianli Wang1, Liubing Dong1, *, Feiyu Kang 1, 2, *, Chengjun Xu1, *

Abstract | Support Info
icon-htmlFull Text Html
icon-pdf-smPDF w/ Links
icon-citExport Citation
Figures
+Show more

Nano-Micro Lett. (2019) 11: 49

First Online: 06 June 2019 (Article)

DOI:10.1007/s40820-019-0278-9

*Corresponding author. E-mail: dong1060@126.com (L. Dong); fykang@mail.tsinghua.edu.cn (F. Kang); vivaxuchengjun@163.com (C. Xu)

 

Abstract

 


Toc

Aqueous rechargeable Zn/MnO2 zinc-ion batteries (ZIBs) are reviving recently due to their low cost, non-toxicity, and natural abundance. However, their energy storage mechanism remains controversial due to their complicated electrochemical reactions. Meanwhile, to achieve satisfactory cyclic stability and rate performance of the Zn/MnO2 ZIBs, Mn2+ is introduced in the electrolyte (e.g., ZnSO4 solution), which leads to more complicated reactions inside the ZIBs systems. Herein, based on comprehensive analysis methods including electrochemical analysis and Pourbaix diagram, we provide novel insights into the energy storage mechanism of Zn/MnO2 batteries in the presence of Mn2+. A complex series of electrochemical reactions with the co-participation of Zn2+, H+, Mn2+, SO42-, and OH- were revealed. During the first discharge process, co-insertion of Zn2+ and H+ promotes the transformation of MnO2 into ZnxMnO4, MnOOH, and Mn2O3, accompanying with increased electrolyte pH and the formation of ZnSO4·3Zn(OH)2·5H2O. During the subsequent charge process, ZnxMnO4, MnOOH, and Mn2O3 revert to α-MnO2 with the extraction of Zn2+ and H+, while ZnSO4·3Zn(OH)2·5H2O reacts with Mn2+ to form ZnMn3O7·3H2O. In the following charge/discharge processes, besides aforementioned electrochemical reactions, Zn2+ reversibly insert into/extract from α-MnO2, ZnxMnO4, and ZnMn3O7·3H2O hosts; ZnSO4·3Zn(OH)2·5H2O, Zn2Mn3O8, and ZnMn2O4 convert mutually with the participation of Mn2+. This work is believed to provide theoretical guidance for further research on high-performance ZIBs.


 

Keywords

Zinc-ion battery; MnO2 cathode; Energy storage mechanism; Phase evolution

 

Full Text Html

1 Introduction

    Lithium-ion batteries (LIBs) have been widely used in consumer electronics due to high energy density, portability, and some other merits [1-4], whereas their security concerns and high cost restrict their large scale applications in stationary grid storage and electric vehicles [5, 6]. Therefore, much attention has been paid to seek safe, eco-friendly, low-cost, and high-performance battery systems [6, 7]. Aqueous rechargeable zinc-ion batteries (ZIBs) are developed as such a battery system, in which low-cost, non-toxic, and naturally abundant zinc metal is used as an anode and environment-friendly neutral aqueous Zn2+-containing solution serves as electrolyte [8]. In recent years, a series of high-performance cathode materials for ZIBs have also been studied such as Prussian blue analog [9-11], vanadium oxides [12-20], manganese oxides [21-28], and some metal sulfides [29-31]. Among these materials, MnO2 is particularly concerned for its high theoretical specific capacity, low cost, eco-friendliness, and diverse crystallographic polymorphs (e.g., α-MnO2, δ-MnO2, and γ-MnO2) [27, 28, 32].
    Many efforts have been made to reveal the energy storage mechanisms of Zn/MnO2 ZIBs. Up to now, three types of energy storage mechanisms were proposed, including (i) Zn2+ insertion/extraction into/from MnO2 [8, 33-36], (ii) conversion between MnO2 and MnOOH with the participation of H+ [37], and (iii) co-insertion of H+ and Zn2+ [38]. Mechanisms (i) and (ii) explain the formation of ZnMn2O4 and MnOOH as discharging products on MnO2 cathode in ZIBs respectively, while cannot explain that there are two redox processes during one charge/discharge cycle of ZIBs. Mechanism (iii) seems to be capable of explaining the co-existence of ZnMn2O4 and MnOOH as discharging products on MnO2 cathode, but deeper analysis will find that it is not accurate: the mechanism deems that potential of Zn2+ insertion is lower than that of H+ insertion (this means that MnOOH forms before ZnMn2O4 once the battery discharge process begins), being conflicted to the experimental result that MnOOH appears latter than ZnMn2O4. In short, the current mechanisms are unsatisfactory to explain genuine charge/discharge process in ZIBs, mainly because they were proposed based on a simplistic view that the insertion of Zn2+ and H+ and the phase change from MnO2 to ZnMn2O4 or MnOOH are highly reversible. Furthermore, to achieve satisfactory cyclic stability and rate performance of the Zn/MnO2 ZIBs, Mn2+ ions are always introduced in the electrolyte [37]. However, electrochemical reactions inside the ZIBs become more complicated in such cases, thus corresponding energy storage mechanism has not been clearly revealed. Therefore, it is necessary to re-examine the thermodynamic and kinetic characteristics of Zn/MnO2 ZIBs to propose a reasonable Zn2+-storage mechanism.
    In fact, for the active materials in aqueous ZIBs and some other rechargeable aqueous batteries, their structure and phase generally undergo complex changes during charge/discharge processes (e.g., the active materials can interact with not only metal ions, but also H+, OH-, and water molecules) [39]. This is an important reason why the energy storage mechanism of MnO2 cathode in ZIBs is still inconclusive [40-43]. Besides general experimental techniques such as cyclic voltammetry (CV) and galvanostatic charge-discharge (GCD) tests, Pourbaix diagram (E-pH diagram) has been widely used to study electrochemical reactions in aqueous solution [44-47]. The electrochemical reductive products of active materials can be predicted according to the thermodynamics, which is beneficial for us to understand the charge/discharge process. Therefore, we combined experimental methods with the E-pH diagram of the Mn-Zn-H2O system together to comprehensively analyze the charge/discharge processes of MnO2 cathode in ZIBs and tried to reveal the authentic energy storage mechanism.
    Herein, based on comprehensive analysis methods including electrochemical analysis and E-pH diagram, etc., we provide novel insights into the energy storage mechanism of Zn/MnO2 batteries with the co-participation of Zn2+, H+, Mn2+, SO42-, and OH-. During the first discharge process, co-insertion of Zn2+ and H+ promotes the transformation of MnO2 into ZnxMnO4, MnOOH, and Mn2O3, accompanying with increased electrolyte pH and the formation of ZnSO4·3Zn(OH)2·5H2O (noted as “BZSP”). During the subsequent charge process, ZnxMnO4, MnOOH, and Mn2O3 revert to α-MnO2 with the extraction of Zn2+ and H+, while BZSP reacts with Mn2+ to form ZnMn3O7·3H2O. In the following charge/discharge processes, besides aforementioned electrochemical reactions, Zn2+ reversibly inserts into/extract from α-MnO2, ZnxMnO4, and ZnMn3O7·3H2O hosts, and BZSP, Zn2Mn3O8, and ZnMn2O4 convert mutually with the participation of Mn2+. This work is believed to provide theoretical guidance for further research on high-performance ZIBs.

2 Experimental

2.1 Material Synthesis
    MnO2 cathode material was synthesized through a chemical co-precipitation method. 150 mL of 0.1 M MnSO4 aqueous solution was dropped into 100 mL of KMnO4 (0.1 M) solution under magnetic stirring, followed by continuous stirring for 6 h at room temperature. The resulting precipitate was filtered, washed repeatedly with deionized water and dried at 80 °C for 12 h. The obtained sample was thoroughly ground in an agate mortar and then annealed at 400 °C for 5 h in air atmosphere. Note that we applied the heat treatment to improve the crystalline of MnO2 because this makes it easier for us to use X-ray diffraction (XRD) and transmission electron microscopy (TEM) to detect the phase evolution of MnO2 cathode during charge/discharge processes.
2.2 Electrochemical Characterizations
    The cathode was prepared by coating a mixture paste of 70 wt% of MnO2 powder, 20 wt% of acetylene black and 10 wt% of LA133 binder on a stainless-steel foil and dried overnight under vacuum conditions at 80 °C. In the prepared cathode, the mass loading of MnO2 is around 1 mg cm-2. Zn/MnO2 ZIBs were assembled based on MnO2 cathode, metallic Zn foil anode, air-laid paper separator, and zinc salt solution electrolyte (2 M ZnSO4 or 2 M ZnSO4 +0.5 M MnSO4 solution).
    The assembled ZIBs were kept more than 4 h before electrochemical measurements. The CV and GCD tests were performed on a Bio-logic VMP3 multichannel electrochemical station and a LAND CT2001 battery tester, respectively. CV tests of the prepared MnO2 cathode were also carried out in a three-electrode system, in which a platinum plate as the counter electrode, a saturated calomel electrode (SCE) as the reference electrode and 50 mL electrolyte was applied.
2.3 Material Characterizations
    Microstructure and composition were characterized by XRD (Rigaku 2500) with Cu-Kα radiation operating at 40 kV and 100 mA within an angle range of 10o to 70o at a scan speed of 5o min-1. Micro-morphology was observed by field emission scanning electron microscopy (SEM, Zeiss Supra 55) and TEM (Tecnai G2 F30). Element content in electrodes and electrolytes was analyzed by inductively coupled plasma atomic emission spectrometry (ICP-AES).

3 Results and Discussion

3.1 Characterization of MnO2
   The MnO2 material used in this work was synthesized through a chemical co-precipitation method. XRD pattern and micro-morphology observations in Fig. 1a-c show that the synthesized MnO2 powder is crystalline α-MnO2 nanorod with a diameter of 10-60 nm and length of several hundred nanometers. From the XRD pattern in Fig. 1a, it seems that the strongest peak is the one at ~12.8o, but if the background is taken into account, the strongest peak is still the one at ~37.5o, which matches well with the α-MnO2 (PDF# 44-0141). In addition, since the as-prepared sample is nanobelts, (110) plane (corresponding to the diffraction peak at ~12.8o) is considered as preferred orientation, thus leading to high diffraction intensity. A similar phenomenon was also observed for some other MnO2 nanomaterials [38]. Based on the high-resolution TEM (HRTEM) image and corresponding the distance (0.238 nm and 0.233 nm) between two planes, it identifies as the crystal planes (121), and (330) of the α-MnO2 in Fig. 1d, great crystallinity of the as-synthesized α-MnO2 is confirmed.

Fig. 1 a XRD pattern, b SEM image, c STEM and d HRSTEM images of the synthesized MnO2 nanorods

Fig. 1 a XRD pattern, b SEM image, c STEM and d HRSTEM images of the synthesized MnO2 nanorods

3.2 Electrochemical Analysis
    We first studied the electrochemical behaviors of MnO2 cathode in two different electrolytes, including 50 mL 2 M ZnSO4 (Fig. 2a) and 50 mL 2 M ZnSO4 + 0.5 M MnSO4 mixture solution (Fig. 2b-d). The capacity and rate performance of the MnO2 cathode in ZnSO4+MnSO4 electrolyte is exhibited in Fig. S1. Note that MnO2 cathode would dissolve in ZnSO4 electrolyte during charge/discharge processes, as detected by ICP-AES tests in Table S1 (this has also been pointed out in previous researches) [37]. With the addition of Mn2+ in the electrolyte, the redox peaks in CV curves (except for the 1st CV cycle) in Fig. 2a, b become more obvious, and meanwhile, the gap between oxidation peak and reduction peak becomes smaller, which indicate that the reversibility of electrochemical process gets better. In Fig. 2a, the reduction peak is much stronger than the oxidation peak in the first cycle, which means that discharge products cannot be electrochemically oxidized completely. By contrast, the intensity of the reduction peak is close to that of the oxidation peak in Fig. 2b. Above phenomenon suggest that Mn2+ concentration in electrolyte plays a crucial role in the first discharge/charge process [48]. There are two pairs of redox peaks when the electrode discharges/charges in the 2 M ZnSO4 + 0.5 M MnSO4 electrolyte (Fig. 2b). The reduction peaks at low and high potentials are denoted as R1 and R2, respectively, and the oxidation peaks at low and high potentials are denoted as O1 and O2, respectively. Considering that electro-deposition of Mn2+ will occur only when the cathode potential reaches about 0.8 V vs. SCE at the constant current of 0.1 A cm-2 (Fig. S2), the oxidation reactions of O1 and O2 ranging from 0.5-0.65 V vs. SCE (Fig. 2b) are not caused by the electro-deposition of Mn2+. This confirms that the preclusion of MnO2 dissolution by Mn2+ in the electrolyte should be the dominant reason for good reversibility of discharge/charge processes in 2 M ZnSO4 + 0.5 M MnSO4 electrolyte.

Fig. 2. Electrochemical behaviors of the prepared cathodes: a CV curves in 50 mL 2 M ZnSO4 solution (1st to 5th cycles); b CV (1st to 5th cycles) and c GCD curves in 50 mL 2 M ZnSO4 + 0.5 M MnSO4 solution; d Constant voltage discharge at various voltages (1.4, 1.2, and 1.1 V) and Local magnification diagram (the inset)

Fig. 2. Electrochemical behaviors of the prepared cathodes: a CV curves in 50 mL 2 M ZnSO4 solution (1st to 5th cycles); b CV (1st to 5th cycles) and c GCD curves in 50 mL 2 M ZnSO4 + 0.5 M MnSO4 solution; d Constant voltage discharge at various voltages (1.4, 1.2, and 1.1 V) and Local magnification diagram (the inset)

    There is a dip and a platform in the initial GCD curve (Fig. 2c) and the reaction type of R1 (at about 1.2 V) and R2 (at about 1.4 V) are further studied by the constant voltage discharge test (Fig. 2d). The current changes greatly when the battery is discharged at 1.2 V at which R1 will happen, and it keeps almost flat when discharged at 1.4 V at which R2 will occur. This indicates that a heterogeneous reaction occurs during R1 and a homogeneous reaction occurs during R2. Such a heterogeneous reaction between solid phases accompanying with nucleation process and electro-crystallization process will cause the formation of the dip and steep curve in the discharge curve in Fig. 2c [49]. With the increasing CV cycles (Fig. 2b), the peak current intensity of R1 and O1 is getting weaker, while the peak current intensity of R2 and O2 becomes stronger. Therefore, the redox reactions R1/O1 and R2/O2 are more likely to be independent of each other. That the initial process differs from the subsequent one can also be seen from Fig. 2c (the red circle). R2 is weaker in the initial discharge process than that in the second one, which indicates that a new phase may generate as active materials.
3.3 Phase Evolution of Cathode in the Initial Discharge Process
    ex-situ XRD tests of the cathodes at different charge/discharge states support were performed. As shown in Fig. S3, when the cathode is initially discharged from 1.9 to 1.4 V, no new phase produces, while the cathode is further discharged to 1.0 V, several new diffraction peaks occur, indicating the appearance of new phases. In the charging process, some diffraction peaks cannot be detected, which means the disappearance of some phases. After 100 charges/discharge cycles, the XRD pattern is not in conformity with the XRD patterns of the cathode at the original state and fully charged state in the 1st charge process. These demonstrate that the cathode undergoes a complicated phase evolution. In the following, phase evolution of MnO2 cathodes during the 1st discharge process, the 1st charge process and subsequent discharge/charge processes were investigated in detail.

Fig. 3 The results of the cathode which is constant current discharged to 1.4 V and then constant voltage discharged at 1.4 V in 2 M ZnSO4 + 0.5 M MnSO4 electrolyte for 2 h: a XRD pattern and locally enlarged image (the inset); b SEM image of the surface of the cathode. Another cathode which is constant current discharged to 1.0 V: c XRD pattern; d SEM image of the surface of the cathode; e Phase evolution of cathode during the 1st discharge process

Fig. 3 The results of the cathode which is constant current discharged to 1.4 V and then constant voltage discharged at 1.4 V in 2 M ZnSO4 + 0.5 M MnSO4 electrolyte for 2 h: a XRD pattern and locally enlarged image (the inset); b SEM image of the surface of the cathode. Another cathode which is constant current discharged to 1.0 V: c XRD pattern; d SEM image of the surface of the cathode; e Phase evolution of cathode during the 1st discharge process

    To investigate phases evolution of cathode in the initial discharge process in 2 M ZnSO4 + 0.5 M MnSO4 electrolyte, R1 and R2 reactions (as defined in Fig. 2, the same hereinafter) are separately studied. Only R2 occurs when the voltage of the battery is above 1.4 V. No new phase produces are seen from the XRD pattern (Fig. 3a). Nevertheless, characteristic peaks of the MnO2 active material such as the peaks at 28o and 38o shift (inset of Fig.3a), which is attributed to the change of the layer spacing of MnO2. This means that the active material undergoes structure change. The nanorods become shorter (Fig. 3b) which is greatly different from that of the as-prepared material (Fig. 1b). Energy dispersive spectrometer (EDS) analysis in Fig. S4 suggests that the molar ratio of Zn, Mn, and S is approximately 1:16:0. To exclude the influence of electrolyte’s absorption, we immersed the electrodes in 2 M ZnSO4 for 48 h and washed several times with deionized water. Neither Zn nor S element is found in the SEM-EDS result (Fig. S5). Thus, the existence of Zn in the cathode when discharging to 1.4 V is caused by the insertion of zinc ions in MnO2, instead of zinc ion adsorption on the cathode surface. In other words, zinc ion insertion happens when the voltage of the Zn/MnO2 battery is above 1.4 V. The process of zinc-ion insertion in MnO2 can be written as:

11 49 gs1

    R1 reaction is then studied. When the battery is discharged to 1.2 V then to the 1 V at constant current several new phases (XRD patterns in Fig. 3c) appear, which are confirmed as BZSP (PDF#39-0688), α-MnOOH (PDF#24-0713), and α-Mn2O3 (PDF#44-1442). There are many large hexagonal nanosheets in the SEM image (Fig. 3d). The Zn, O, and S element distribute evenly over the whole hexagonal nanosheets (Fig. S6b, c, e, f). And the atomic proportion of Zn to S is about 4:1 from the SEM-EDS results (Fig. S6d). Combined with the XRD result, we conclude that the hexagonal nanosheets are BZSP. The structure evolution of cathode in the first discharge is shown in Fig. 3e. The existence of α-MnOOH and α-Mn2O3 is further demonstrated by HRTEM (Fig. 4). The α-Mn2O3 is semi-coherent with the α-MnOOH phase (Fig. 4c). These substances and their reactions can be written as [21, 28, 37]:

11 49 gs234

    Phases in region e, f, g, and h in Fig. 4c, d marked by yellow dash can be identified as α-MnOOH, α-Mn2O3, α-Mn2O3, and α-ZnxMnO2, respectively, through fast Fourier transform (FFT) in Fig. 4e-h (detailed calculation procedures are given in Table S2-S4). From the TEM-EDS result, the Zn element can be found in both regions A and B and there is no S element in these regions (Fig. 4b), further confirming that zinc-ion inserts into the nanorods. Besides, the generation of BZSP and α-MnOOH indicates that H+ and Zn2+ participate in the reaction. From the above discussions, zinc ion insertion in α-MnO2 occurs around 1.4 V vs. Zn2+/Zn to generate α-ZnxMnO2, and proton conversion reaction happens between 1.0-1.3 V in the cathode and leads to the generation of MnOOH, Mn2O3, and BZSP.

Fig. 4 TEM, HRTEM image, and TEM-EDS spectrum of the sample constant current discharge to 1.0 V: a TEM image b TEM-EDS spectrum result of region A and B marked in a. c, d HRTEM image of region A and B marked in Fig. 4a, respectively. e, f FFT of the region marked by a yellow dash in c and d, respectively

Fig. 4 TEM, HRTEM image, and TEM-EDS spectrum of the sample constant current discharge to 1.0 V: a TEM image b TEM-EDS spectrum result of region A and B marked in a. c, d HRTEM image of region A and B marked in Fig. 4a, respectively. e, f FFT of the region marked by a yellow dash in c and d, respectively

3.4 Phase Evolution of Cathode in the First Charge Process
    To detect the phase evolution of MnO2 cathode during the charge process, the battery is discharged to 1.0 V and then charged to 1.9 V in 2 M ZnSO4 and 2 M ZnSO4 + 0.5 M MnSO4 electrolyte respectively. The discharging products of Mn2O3, BZSP, and MnO2 still exist on the charged cathode, and besides, new phase ZnMn3O7·3H2O generates (Fig. 5a). It is worth noting that when adding Mn2+ in the electrolyte, the diffraction peaks of ZnMn3O7·3H2O become strong while the diffraction peaks of BZSP become weak (Fig. 5a). The morphology of cathode changes greatly (from hexagonal nanosheets to ball-like nanoflowers) during the initial charging process as shown in Figs. S7a-f and S8a-d. Figure S7a-f shows that BZSP exists in the 2 M ZnSO4 solution while almost disappears in 2 M ZnSO4 + 0.5 M MnSO4 solution during the charging process. It means that added Mn2+ in the electrolyte can promote the dissolution of BZSP. To confirm this, the fresh cathode was discharged to 1.0 V in 2 M ZnSO4 + 0.5 M MnSO4 solution and then soaked in potassium hydrogen phthalate solution (pH = 4.0) for 72 h to completely dissolve BZSP. The electrode without BZSP was then charged in 2 M ZnSO4 + 0.5 M MnSO4 electrolyte. Meanwhile, the discharged electrode with BZSP was separately charged in the electrolytes of 2 M ZnSO4 and 2 M ZnSO4 + 0.5 M MnSO4. The charge processes of the three conditions are shown in Fig. 5b. It can be seen that the platform, which means heterogeneous reaction happens, occurs at 1.5 V only when BZSP and Mn2+ both exist. To further confirm this, a discharged electrode with BZSP charge at 1.5 V in the 2 M ZnSO4 + 0.5 M MnSO4 solution. The nanoflower-like product generates (inset in Fig. 5c) as expected. ZnMn3O7·3H2O is also found in HRTEM in Fig. 5d. Combining with the result of XRD, the nanoflower is ZnMn3O7·3H2O. The dissolution of BZSP (nanosheets in Fig. S8a-d) and the occurrence of the new phase (nanoflowers in Fig. S8a-b) ZnMn3O7·3H2O indicate that ZnMn3O7·3H2O generate from the conversion reaction between BZSP and Mn2+. The nanoflower is Zn(OH)2 and MnO2 alternately layered structure as seen from Fig. S9. The conversion reactions are as follows: Zn2+ in the interlayer of Zn(OH)2 (Fig. S10) exchanges with Mn2+ and then the Mn2+ is chemically oxidized during the charging process. With continuous oxidation of Mn2+, the Mn2+ reacts with H2O to generate ZnMn3O7·3H2O (Fig. S10). The structure evolution of cathode in the first charge is shown in Fig. 5e. In other words, besides H+ and Zn2+, Mn2+ also participates in the reactions that occur during the discharge/charge process as the conversion reactions are supposed as follows:

11 49 gs5

    The generation of ZnMn3O7·3H2O during the first charge process can explain the phenomenon that the second discharge curve of the battery is different from the first discharge curve. In a word, during the first charging process, ZnxMnO2 and MnOOH reversibly become α-MnO2 with the extraction of Zn2+ and H+, while ZnMn3O7·3H2O acts as the host for the insertion of Zn2+ forms through the reaction between Mn2+and BZSP.

Fig. 5 The first charge process: a XRD pattern of the fully charged cathode in the 1st charge process; b Charging curves of α-MnO2 electrodes after discharge to 1 V in different cases; c Constant Voltage test; d HRTEM image and analysis result. e Phase evolution of cathode during the 1st charge process

Fig. 5 The first charge process: a XRD pattern of the fully charged cathode in the 1st charge process; b Charging curves of α-MnO2 electrodes after discharge to 1 V in different cases; c Constant Voltage test; d HRTEM image and analysis result. e Phase evolution of cathode during the 1st charge process

3.5 Phase Evolution of Cathode in Subsequent Discharge/Charge Processes
    The phases of the battery system after 100 charges/discharge cycles are also studied. XRD patterns of the discharged cathode after 100 cycles in 2 M ZnSO4 + 0.5 M MnSO4 solution in Fig. 6a imply that the main phases of the system are ZnMn2O4 (PDF#24-1133), Zn2Mn3O8 (PDF#32-1472), Mn2O3, BZSP, and α-MnO2. These components are confirmed in HRTEM images in Fig. 6b-d. As a contrast, the battery in the 2 M ZnSO4 solution, the main phases of the system are ZnMn2O4, ZnMn3O7, Mn2O3, and BZSP (Fig. S11a, b). ZnMn2O4 is on the surface of the α-MnO2 in HRTEM (Fig. 6b), so it may be converted from α-MnO2. Zn2Mn3O8 and ZnMn2O4 are coherent in the HRTEM (Fig. 6c, d). Thus, Zn2Mn3O8 reacts with Mn2+ to form ZnMn2O4 (this will be further analyzed in the Mn-Zn-O diagram in the following part). There are two kinds of nanoparticles after 100 cycles (Fig. S12), which may be converted from BZSP and Mn2+ as nanosheets and nanoparticles surround each other. Combining the XRD result (Fig. 6a), the phase is Zn2Mn3O8. Thus, Zn2Mn3O8 is generated from the reactions between BZSP and Mn2+. The structure evolution of cathode after 100 cycles is shown in Fig. 6e. Reactions between them are as follows:

11 49 gs67

    To sum up, within the continuous charge/discharge process, ZnMn2O4 and Zn2Mn3O8 as host for insertion of Zn2+ further generate on the surface of MnO2, which implies that the phase change of MnO2 cathode is irreversible.

Fig. 6 The MnO2 cathode after 100 charge/discharge cycles in 2 M ZnSO4 + 0.5 M MnSO4 electrolyte: a XRD patterns; b-d HRTEM images; e Phase evolution of cathode during the repeated charge/discharge processes after the 1st charge/discharge cycle

Fig. 6 The MnO2 cathode after 100 charge/discharge cycles in 2 M ZnSO4 + 0.5 M MnSO4 electrolyte: a XRD patterns; b-d HRTEM images; e Phase evolution of cathode during the repeated charge/discharge processes after the 1st charge/discharge cycle

3.6 Thermodynamic Analysis
    When dynamic conditions are met, the phases can be predicted from Zn-Mn-O diagram since the system of the Zn/ZnSO4 + MnSO4/MnO2 battery reaches an equilibrium state after a certain cycle. The isothermal cross-section of the phase diagram (25 °C) is shown in Fig. 7a. Since MnO2 is used as an active material and ZnSO4 + MnSO4 as the electrolyte for the beginning, the phase of the reaction is bound to three elements (Mn, O, and Zn). When the thermodynamic stability of the system reaches, the definite phases include manganese oxide (MnO2, Mn2O3, Mn3O4, and MnO) and zinc manganese oxide (ZnMn2O4 and Zn2Mn3O8) (Fig. 7a). Detailed density functional theory calculation and theoretical analysis of MnO2 as a cathode of ZIBs are given in Discussion S1 and S2 in Supporting Information). There are two paths to the reduction of MnO2: (i) MnO2 → Mn2O3 → Mn3O4 → MnO, in which path, there is no Zn involvement; (ii) MnO2 → ZnMn2O4 with Zn involvement. For Mn2O3 oxidation, it is directly oxidized to MnO2: Mn2O3 → MnO2. The oxidation of ZnMn2O4 has two paths: Zn extracts out completely from ZnMn2O4 to generate MnO2 or Mn partially removes from ZnMn2O4 to generate Zn2Mn3O8. They can express as: (1) ZnMn2O4 → MnO2; (2) ZnMn2O4 → Zn2Mn3O8. And there's only one way for the Zn2Mn3O8 reduction: Zn2Mn3O8 → ZnMn2O4. In the Zn/ZnSO4 + MnSO4/α-MnO2 system studied in this paper, MnO dissolves in the electrolyte or can be inhibited when there is a certain concentration of Mn2+. Thus there are five kinds of phases that may exist, such as MnO2, Mn2O3, Mn3O4, ZnMn2O4, and Zn2Mn3O8. When taking PH and potentials into consideration, MnO2, Mn2O3, ZnMn2O4, MnOOH, and Zn2Mn3O8 can form in our system but MnOOH is not stable, which matches well with our work (the red region in Fig. 7b). The reaction route is concluded to be as follows: (1) MnO2 → Mn2O3, (2) MnO2 → ZnMn2O4 and (3) Zn2Mn3O8 → ZnMn2O4 (Fig. 7a). MnO2, Mn2O3, ZnMn2O4, and Zn2Mn3O8 are stable phases and all can store Zn2+ (Fig. 7b).

Fig. 7 a Zn-Mn-O diagram and b E-pH diagram of Zn-Mn-H2O system

Fig. 7 a Zn-Mn-O diagram and b E-pH diagram of Zn-Mn-H2O system

    Overall, we combined electrochemical analysis, phase identification with E-pH diagram of the Mn-Zn-H2O system together to analyze charge/discharge processes of aqueous rechargeable Zn//MnO2 batteries and revealed complicated phase evolution of the cathode (i.e., what new phases will form and how can they form in different charge/discharge stages). We obtained some different conclusions from previous literature. For example, Sun et al. thought that the conversion of H+ occurs before Zn2+ insertion [38]. But we find that Zn2+ insertion occurs before the conversion of H+ in the 1st discharge process, and this is confirmed by thermodynamic analysis. Besides, previous literature deemed that the disappearance of BZSP is always caused by the change of electrolyte pH [34], but we find that BZSP can react with Mn2+ in the electrolyte to form a new phase of ZnMn3O7.

4 Conclusions

    Based on experimental results and theoretical analysis of Zn/MnO2 ZIBs with the mixture electrolyte of ZnSO4 + MnSO4 aqueous solution, we found that the mechanism in ZIBs is dynamic and the phase transformation at MnO2 cathode is irreversible during charge/discharge processes. Not only H+ and Zn2+ but also Mn2+ in the electrolyte take part in the reactions. In the first discharge process, ZnxMnO2, MnOOH, Mn2O3, and byproduct BZSP generate, and then in the first charge process, α-MnO2 and ZnMn3O7·3H2O appear. In the following charge/discharge processes, ZnMn2O4 and ZnMn3O8 are further generated on the surface of MnO2 and serve as the hosts for Zn2+ insertion. The mechanism becomes dynamic and complex because of the co-participation of the insertion process, conversion reaction, and oxidation reactions. The aforementioned phase changes inside ZIBs are well explained by the Mn-Zn-O phase diagram and the E-pH diagram. This work can provide guidance for continual research from the following aspects. (i) The research method combining electrochemical analysis, phase identification with E-pH diagram together can be used to analyze charge/discharge processes of other electrochemical energy storage systems, such as aqueous rechargeable Zn//V2O5 batteries. (ii) According to the proposed energy storage systems in this work, at least two approaches can be applied to enhance cycling performance of ZIBs: one is adding Mn2+ to promote the disappearance of BZSP, and the other one is adding pH buffer into the electrolytes or preparing solid electrolytes to prohibit the generation of OH- and BZSP.

Acknowledgments

    The authors appreciate the financial support from the International Science & Technology Cooperation Program of China (No. 2016YFE0102200), Shenzhen Technical Plan Project (No. JCYJ20160301154114273), National Key Basic Research (973) Program of China (No. 2014CB932400), and Local Innovative and Research Teams Project of Guangdong Pearl River Talents Program (2017BT01N111).

 

References

[1] T.-H. Kim, J.-S. Park, S.K. Chang, S. Choi, J.H. Ryu, H.-K. Song, The current move of lithium-ion batteries towards the next phase. Adv. Energy Mater. 2, 860-872 (2012). https://doi.org/10.1002/aenm.201200028
[2] B. Dunn, H. Kamath, J.M. Tarascon, Electrical energy storage for the grid: A battery of choices. Science 334, 928-935 (2011). https://doi.org/10.1126/science.1212741
[3] H. Sun, J.-G. Wang, Y. Zhang, W. Hua, Y. Li, H. Liu, Ultrafast lithium energy storage enabled by interfacial construction of interlayer-expanded MoS2/N-doped carbon nanowires. J. Mater. Chem. A 6, 13419-13427 (2018). https://doi.org/10.1039/C8TA04852E
[4] J.-G. Wang, H. Liu, R. Zhou, X. Liu, B. Wei, Onion-like nanospheres organized by carbon encapsulated few-layer MoS2 nanosheets with enhanced lithium storage performance. J. Power Sources 413, 327-333 (2019). https://doi.org/10.1016/j.jpowsour.2018.12.055
[5] C. Delmas, M. Maccario, L. Croguennec, F. Le Cras, F. Weill, Lithium deintercalation in LiFePO4 nanoparticles via a domino-cascade model. Nat. Mater. 7, 665-671 (2008). https://doi.org/10.1038/nmat2230
[6] N. Alias, A.A. Mohamad, Advances of aqueous rechargeable lithium-ion battery: A review. J. Power Sources 274, 237-251 (2015). https://doi.org/10.1016/j.jpowsour.2014.10.009
[7] J.O.G. Posada, A.J.R. Rennie, S.P. Villar, V.L. Martins, J. Marinaccio et al., Aqueous batteries as grid-scale energy storage solutions. Renew. Sust. Energ. Rev. 68, 1174-1182 (2017). https://doi.org/10.1016/j.rser.2016.02.024
[8] C. Xu, B. Li, H. Du, F. Kang, Energetic zinc ion chemistry: The rechargeable zinc ion battery. Angew. Chem. Int. Ed. 51, 933-935 (2012). https://doi.org/10.1002/anie.201106307
[9] L. Zhang, L. Chen, X. Zhou, Z. Liu, Towards high-voltage aqueous metal-ion batteries beyond 1.5 V: The zinc/zinc hexacyanoferrate system. Adv. Energy Mater. 5, 1400930 (2015). https://doi.org/10.1002/aenm.201400930
[10] R. Trocoli, F. La Mantia, An aqueous zinc-ion battery based on copper hexacyanoferrate. ChemSusChem 8, 481-485 (2015). https://doi.org/10.1002/cssc.201403143
[11] Z. Liu, G. Pulletikurthi, F. Endres, A prussian blue/zinc secondary battery with a bio-ionic liquid-water mixture as electrolyte. ACS Appl. Mater. Interfaces 8, 12158-12164 (2016). https://doi.org/10.1021/acsami.6b01592
[12] Y. Wu, Y. Yang, X. Zhao, Y. Tan, Y. Liu, Z. Wang, F. Ran, A novel hierarchical porous 3D structured vanadium nitride/carbon membranes for high-performance supercapacitor negative electrodes. Nano-Micro Lett. 10, 63 (2018). https://doi.org/10.1007/s40820-018-0217-1
[13] Y. Yang, Y. Tang, G. Fang, L. Shan, J. Guo et al., Li+ intercalated V2O5·nH2O with enlarged layer spacing and fast ion diffusion as an aqueous zinc-ion battery cathode. Energy Environ. Sci. 11, 3157-3162 (2018). https://doi.org/10.1039/C8EE01651H
[14] J.H. Jo, Y.-K. Sun, S.-T. Myung, Hollandite-type al-doped VO1.52(OH)0.77 as a zinc ion insertion host material. J. Mater. Chem. A 5, 8367-8375 (2017). https://doi.org/10.1039/C7TA01765K
[15] B. Zhang, Y. Liu, X. Wu, Y. Yang, Z. Chang, Z. Wen, Y. Wu, An aqueous rechargeable battery based on zinc anode and Na0.95MnO2. Chem. Commun. 50, 1209-1211 (2014). https://doi.org/10.1039/C3CC48382G
[16] D. Kundu, B.D. Adams, V. Duffort, S.H. Vajargah, L.F. Nazar, A high-capacity and long-life aqueous rechargeable zinc battery using a metal oxide intercalation cathode. Nat. Energy 1, 16119 (2016). https://doi.org/10.1038/nenergy.2016.119
[17] C.W. Mason, F. Lange, Aqueous ion battery systems using sodium vanadium phosphate stabilized by titanium substitution. ECS Electrochem. Lett. 4, A79-A82 (2015). https://doi.org/10.1149/2.0011508eel
[18] H.B. Zhao, C.J. Hu, H.W. Cheng, J.H. Fang, Y.P. Xie et al., Novel rechargeable M3V2(PO4)3//zinc (M= Li, Na) hybrid aqueous batteries with excellent cycling performance. Sci. Rep. 6, 25809 (2016). https://doi.org/10.1038/srep25809
[19] B. Tang, G. Fang, J. Zhou, L. Wang, Y. Lei, C. Wang, T. Lin, Y. Tang, S. Liang, Potassium vanadates with stable structure and fast ion diffusion channel as cathode for rechargeable aqueous zinc-ion batteries. Nano Energy 51, 579-587 (2018). https://doi.org/10.1016/j.nanoen.2018.07.014
[20] X. Guo, G. Fang, W. Zhang, J. Zhou, L. Shan et al., Mechanistic insights of Zn2+ storage in sodium vanadates. Adv. Energy Mater. 18, 1801819 (2018). https://doi.org/10.1002/aenm.201801819
[21] N. Zhang, F. Cheng, Y. Liu, Q. Zhao, K. Lei, C. Chen, X. Liu, J. Chen, Cation-deficient spinel ZnMn2Ocathode in Zn(CF3SO3)electrolyte for rechargeable aqueous Zn-ion battery. J. Am. Chem. Soc. 138, 12894-12901 (2016). https://doi.org/10.1021/jacs.6b05958
[22] G. Yuan, J. Bai, T. N.L. Doan, P. Chen, Synthesis and electrochemical investigation of nanosized LiMn2O4 as cathode material for rechargeable hybrid aqueous batteries. Mater. Lett. 137, 311-314 (2014). https://doi.org/10.1016/j.matlet.2014.09.019
[23] J. Zhao, Y. Li, X. Peng, S. Dong, J. Ma, G. Cui, L. Chen, High-voltage Zn/LiMn0.8Fe0.2PO4 aqueous rechargeable battery by virtue of “water-in-salt” electrolyte. Electrochem. Commun. 69, 6-10 (2016). https://doi.org/10.1016/j.elecom.2016.05.014
[24] G. Fang, C. Zhu, M. Chen, J. Zhou, B. Tang, X. Cao, X. Zheng, A. Pan, S. Liang, Suppressing manganese dissolution in potassium manganate with rich oxygen defects engaged high‐energy‐density and durable aqueous zinc‐ion battery. Adv. Funct. Mater. 29, 1808375 (2019). https://doi.org/10.1002/adfm.201808375
[25] J. Lee, J.B. Ju, W.I. Cho, B.W. Cho, S.H. Oh, Todorokite-type MnO­2 as a Zinc-ion intercalating material. Electrochim. Acta 112, 138-143 (2013). https://doi.org/10.1016/j.electacta.2013.08.136
[26] T. Yamamoto, T. Shoji, Rechargeable Zn∣ZnSO4∣MnO­2 -type cells. Inorg. Chim. Acta 117, L27-L28 (1986). https://doi.org/10.1016/S0020-1693(00)82175-1
[27] M.H. Alfaruqi, S. Islam, J. Gim, J. Song, S. Kim et al., A high surface area tunnel-type α- MnO­2 nanorod cathode by a simple solvent-free synthesis for rechargeable aqueous zinc-ion batteries. Chem. Phys. Lett. 650, 64-68 (2016). https://doi.org/10.1016/j.cplett.2016.02.067
[28] M.H. Alfaruqi, J. Gim, S. Kim, J. Song, D.T. Pham, J. Jo, Z. Xiu, V. Mathew, J. Kim, A layered δ- MnO­2 nanoflake cathode with high zinc-storage capacities for eco-friendly battery applications. Electrochem. Commun. 60, 121-125 (2015). https://doi.org/10.1016/j.elecom.2015.08.019
[29] G. Fang, J. Zhou, A. Pan, S. Liang, Recent advances in aqueous zinc-ion batteries. ACS Energy Lett. 3, 2480-2501 (2018). https://doi.org/10.1021/acsenergylett.8b01426
[30] P. He, M. Yan, G. Zhang, R. Sun, L. Chen, Q. An, L. Mai, Layered VS2 nanosheet-based aqueous Zn ion battery cathode. Adv. Energy Mater. 7, 601920 (2017). https://doi.org/10.1002/aenm.201601920
[31] Y. Cheng, L. Luo, L. Zhong, J. Chen, B. Li et al., Highly reversible zinc-ion intercalation into chevrel phase Mo6S8 nanocubes and applications for advanced zinc-ion batteries. ACS Appl. Mater. Interfaces 8, 13673-13677 (2016). https://doi.org/10.1021/acsami.6b03197
[32] M.H. Alfaruqi, V. Mathew, J. Gim, S. Kim, J. Song, J.P. Baboo, S.H. Choi, J. Kim, Electrochemically induced structural transformation in a γ- MnO­2 cathode of a high capacity zinc-ion battery system. Chem. Mater. 26, 3609-3620 (2015). https://doi.org/10.1021/cm504717p
[33] B. Lee, H.R. Lee, H. Kim, K.Y. Chung, B.W. Cho, S.H. Oh, Elucidating the intercalation mechanism of zinc ions into alpha- MnO­2 for rechargeable zinc batteries. Chem. Commun. 51, 9265-9268 (2015). https://doi.org/10.1039/C5CC02585K
[34] B. Lee, H.R. Seo, H.R. Lee, C.S. Yoon, J.H. Kim, K.Y. Chung, B.W. Cho, S.H. Oh, Critical role of pH evolution of electrolyte in the reaction mechanism for rechargeable zinc batteries. ChemSusChem 9, 2948-2956 (2016). https://doi.org/10.1002/cssc.201600702
[35] B. Lee, C.S. Yoon, H.R. Lee, K.Y. Chung, B.W. Cho, S.H. Oh, Electrochemically-induced reversible transition from the tunneled to layered polymorphs of manganese dioxide. Sci. Rep. 4, 6066 (2014). https://doi.org/10.1038/srep06066
[36] M.H. Alfaruqi, J. Gim, S. Kim, J. Song, J. Jo, S. Kim, V. Mathew, J. Kim, Enhanced reversible divalent zinc storage in a structurally stable α- MnO­2 nanorod electrode. J. Power Sources 288, 320-327 (2015). https://doi.org/10.1016/j.jpowsour.2015.04.140
[37] H. Pan, Y. Shao, P. Yan, Y. Cheng, K.S. Han et al., Reversible aqueous zinc/manganese oxide energy storage from conversion reactions. Nat. Energy 1, 16039 (2016). https://doi.org/10.1038/nenergy.2016.39
[38] W. Sun, F. Wang, S. Hou, C. Yang, X. Fan et al., Zn/ MnO­2 battery chemistry with H+ and Zn2+ coinsertion. J. Am. Chem. Soc. 139, 9775-9778 (2017). https://doi.org/10.1021/jacs.7b04471
[39] G.G. Yadav, J.W. Gallaway, D.E. Turney, M. Nyce, J. Huang, X. Wei, S. Banerjee, Regenerable Cu-intercalated MnO­2 layered cathode for highly cyclable energy dense batteries. Nat. Commun. 8, 14424 (2017). https://doi.org/10.1038/ncomms14424
[40] N. Jabeen, A. Hussain, Q. Xia, S. Sun, J. Zhu, H. Xia, High-performance 2.6 V aqueous asymmetric supercapacitors based on in situ formed Na0.5MnO­2 nanosheet assembled nanowall arrays. Adv. Mater. 29, 1700804 (2017). https://doi.org/10.1002/adma.201700804
[41] A. Konarov, N. Voronina, J.H. Jo, Z. Bakenov, Y.-K. Sun, S.-T. Myung, Present and future perspective on electrode materials for rechargeable zinc-ion batteries. ACS Energy Lett. 3, 2620-2640 (2018). https://doi.org/10.1021/acsenergylett.8b01552
[42] M. Song, H. Tan, D. Chao, H.J. Fan, Recent advances in Zn-ion batteries. Adv. Funct. Mater. 28, 1802564 (2018). https://doi.org/10.1002/adfm.201802564
[43] J. Hao, J. Mou, J. Zhang, L. Dong, W. Liu, C. Xu, F. Kang, Electrochemically induced spinel-layered phase transition of Mn3O4 in high performance neutral aqueous rechargeable zinc battery. Electrochim. Acta 259, 170-178 (2018). https://doi.org/10.1016/j.electacta.2017.10.166
[44] D. Grujicic, B. Pesic, Reaction and nucleation mechanisms of copper electrodeposition from ammoniacal solutions on vitreous carbon. Electrochim. Acta 50, 4426-4443 (2005). https://doi.org/10.1016/j.electacta.2005.02.012
[45] A. Anderko, S.J. Sanders, R.D. Young, Real-solution stability diagrams: A thermodynamic tool for modeling corrosion in wide temperature and concentration ranges. Corrosion 53, 43-53 (1997). https://doi.org/10.5006/1.3280432
[46] A.G. Tyurin, A role of manganese in the corrosion and electrochemical behavior of stainless steels. Protect. Met. 41, 68-75 (2005). https://doi.org/10.1007/s11124-005-0010-7
[47] X. Zhou, C. Wei, M. Li, S. Qiu, X. Li, Thermodynamics of vanadium–sulfur–water systems at 298 K. Hydrometallurgy 106, 104-112 (2011). https://doi.org/10.1016/j.hydromet.2010.12.003
[48] M. Chamoun, W.R. Brant, C.-W. Tai, G. Karlsson, D. Noréus, Rechargeability of aqueous sulfate Zn/ MnO­2 batteries enhanced by accessible Mn2+ ions. Energy Storage Mater. 15, 351-360 (2018). https://doi.org/10.1016/j.ensm.2018.06.019
[49] K.J. Vetter, A general thermodynamic theory of the potential of passive electrodes and its influence on passive corrosion. J. Electrochem. Soc. 110, 597-605 (1963). https://doi.org/10.1149/1.2425837

References

[1] T.-H. Kim, J.-S. Park, S.K. Chang, S. Choi, J.H. Ryu, H.-K. Song, The current move of lithium-ion batteries towards the next phase. Adv. Energy Mater. 2, 860-872 (2012). https://doi.org/10.1002/aenm.201200028
[2] B. Dunn, H. Kamath, J.M. Tarascon, Electrical energy storage for the grid: A battery of choices. Science 334, 928-935 (2011). https://doi.org/10.1126/science.1212741
[3] H. Sun, J.-G. Wang, Y. Zhang, W. Hua, Y. Li, H. Liu, Ultrafast lithium energy storage enabled by interfacial construction of interlayer-expanded MoS2/N-doped carbon nanowires. J. Mater. Chem. A 6, 13419-13427 (2018). https://doi.org/10.1039/C8TA04852E
[4] J.-G. Wang, H. Liu, R. Zhou, X. Liu, B. Wei, Onion-like nanospheres organized by carbon encapsulated few-layer MoS2 nanosheets with enhanced lithium storage performance. J. Power Sources 413, 327-333 (2019). https://doi.org/10.1016/j.jpowsour.2018.12.055
[5] C. Delmas, M. Maccario, L. Croguennec, F. Le Cras, F. Weill, Lithium deintercalation in LiFePO4 nanoparticles via a domino-cascade model. Nat. Mater. 7, 665-671 (2008). https://doi.org/10.1038/nmat2230
[6] N. Alias, A.A. Mohamad, Advances of aqueous rechargeable lithium-ion battery: A review. J. Power Sources 274, 237-251 (2015). https://doi.org/10.1016/j.jpowsour.2014.10.009
[7] J.O.G. Posada, A.J.R. Rennie, S.P. Villar, V.L. Martins, J. Marinaccio et al., Aqueous batteries as grid-scale energy storage solutions. Renew. Sust. Energ. Rev. 68, 1174-1182 (2017). https://doi.org/10.1016/j.rser.2016.02.024
[8] C. Xu, B. Li, H. Du, F. Kang, Energetic zinc ion chemistry: The rechargeable zinc ion battery. Angew. Chem. Int. Ed. 51, 933-935 (2012). https://doi.org/10.1002/anie.201106307
[9] L. Zhang, L. Chen, X. Zhou, Z. Liu, Towards high-voltage aqueous metal-ion batteries beyond 1.5 V: The zinc/zinc hexacyanoferrate system. Adv. Energy Mater. 5, 1400930 (2015). https://doi.org/10.1002/aenm.201400930
[10] R. Trocoli, F. La Mantia, An aqueous zinc-ion battery based on copper hexacyanoferrate. ChemSusChem 8, 481-485 (2015). https://doi.org/10.1002/cssc.201403143
[11] Z. Liu, G. Pulletikurthi, F. Endres, A prussian blue/zinc secondary battery with a bio-ionic liquid-water mixture as electrolyte. ACS Appl. Mater. Interfaces 8, 12158-12164 (2016). https://doi.org/10.1021/acsami.6b01592
[12] Y. Wu, Y. Yang, X. Zhao, Y. Tan, Y. Liu, Z. Wang, F. Ran, A novel hierarchical porous 3D structured vanadium nitride/carbon membranes for high-performance supercapacitor negative electrodes. Nano-Micro Lett. 10, 63 (2018). https://doi.org/10.1007/s40820-018-0217-1
[13] Y. Yang, Y. Tang, G. Fang, L. Shan, J. Guo et al., Li+ intercalated V2O5·nH2O with enlarged layer spacing and fast ion diffusion as an aqueous zinc-ion battery cathode. Energy Environ. Sci. 11, 3157-3162 (2018). https://doi.org/10.1039/C8EE01651H
[14] J.H. Jo, Y.-K. Sun, S.-T. Myung, Hollandite-type al-doped VO1.52(OH)0.77 as a zinc ion insertion host material. J. Mater. Chem. A 5, 8367-8375 (2017). https://doi.org/10.1039/C7TA01765K
[15] B. Zhang, Y. Liu, X. Wu, Y. Yang, Z. Chang, Z. Wen, Y. Wu, An aqueous rechargeable battery based on zinc anode and Na0.95MnO2. Chem. Commun. 50, 1209-1211 (2014). https://doi.org/10.1039/C3CC48382G
[16] D. Kundu, B.D. Adams, V. Duffort, S.H. Vajargah, L.F. Nazar, A high-capacity and long-life aqueous rechargeable zinc battery using a metal oxide intercalation cathode. Nat. Energy 1, 16119 (2016). https://doi.org/10.1038/nenergy.2016.119
[17] C.W. Mason, F. Lange, Aqueous ion battery systems using sodium vanadium phosphate stabilized by titanium substitution. ECS Electrochem. Lett. 4, A79-A82 (2015). https://doi.org/10.1149/2.0011508eel
[18] H.B. Zhao, C.J. Hu, H.W. Cheng, J.H. Fang, Y.P. Xie et al., Novel rechargeable M3V2(PO4)3//zinc (M= Li, Na) hybrid aqueous batteries with excellent cycling performance. Sci. Rep. 6, 25809 (2016). https://doi.org/10.1038/srep25809
[19] B. Tang, G. Fang, J. Zhou, L. Wang, Y. Lei, C. Wang, T. Lin, Y. Tang, S. Liang, Potassium vanadates with stable structure and fast ion diffusion channel as cathode for rechargeable aqueous zinc-ion batteries. Nano Energy 51, 579-587 (2018). https://doi.org/10.1016/j.nanoen.2018.07.014
[20] X. Guo, G. Fang, W. Zhang, J. Zhou, L. Shan et al., Mechanistic insights of Zn2+ storage in sodium vanadates. Adv. Energy Mater. 18, 1801819 (2018). https://doi.org/10.1002/aenm.201801819
[21] N. Zhang, F. Cheng, Y. Liu, Q. Zhao, K. Lei, C. Chen, X. Liu, J. Chen, Cation-deficient spinel ZnMn2O4 cathode in Zn(CF3SO3)2 electrolyte for rechargeable aqueous Zn-ion battery. J. Am. Chem. Soc. 138, 12894-12901 (2016). https://doi.org/10.1021/jacs.6b05958
[22] G. Yuan, J. Bai, T. N.L. Doan, P. Chen, Synthesis and electrochemical investigation of nanosized LiMn2O4 as cathode material for rechargeable hybrid aqueous batteries. Mater. Lett. 137, 311-314 (2014). https://doi.org/10.1016/j.matlet.2014.09.019
[23] J. Zhao, Y. Li, X. Peng, S. Dong, J. Ma, G. Cui, L. Chen, High-voltage Zn/LiMn0.8Fe0.2PO4 aqueous rechargeable battery by virtue of “water-in-salt” electrolyte. Electrochem. Commun. 69, 6-10 (2016). https://doi.org/10.1016/j.elecom.2016.05.014
[24] G. Fang, C. Zhu, M. Chen, J. Zhou, B. Tang, X. Cao, X. Zheng, A. Pan, S. Liang, Suppressing manganese dissolution in potassium manganate with rich oxygen defects engaged high‐energy‐density and durable aqueous zinc‐ion battery. Adv. Funct. Mater. 29, 1808375 (2019). https://doi.org/10.1002/adfm.201808375
[25] J. Lee, J.B. Ju, W.I. Cho, B.W. Cho, S.H. Oh, Todorokite-type MnO­2 as a Zinc-ion intercalating material. Electrochim. Acta 112, 138-143 (2013). https://doi.org/10.1016/j.electacta.2013.08.136
[26] T. Yamamoto, T. Shoji, Rechargeable Zn∣ZnSO4∣MnO­2 -type cells. Inorg. Chim. Acta 117, L27-L28 (1986). https://doi.org/10.1016/S0020-1693(00)82175-1
[27] M.H. Alfaruqi, S. Islam, J. Gim, J. Song, S. Kim et al., A high surface area tunnel-type α- MnO­2 nanorod cathode by a simple solvent-free synthesis for rechargeable aqueous zinc-ion batteries. Chem. Phys. Lett. 650, 64-68 (2016). https://doi.org/10.1016/j.cplett.2016.02.067
[28] M.H. Alfaruqi, J. Gim, S. Kim, J. Song, D.T. Pham, J. Jo, Z. Xiu, V. Mathew, J. Kim, A layered δ- MnO­2 nanoflake cathode with high zinc-storage capacities for eco-friendly battery applications. Electrochem. Commun. 60, 121-125 (2015). https://doi.org/10.1016/j.elecom.2015.08.019
[29] G. Fang, J. Zhou, A. Pan, S. Liang, Recent advances in aqueous zinc-ion batteries. ACS Energy Lett. 3, 2480-2501 (2018). https://doi.org/10.1021/acsenergylett.8b01426
[30] P. He, M. Yan, G. Zhang, R. Sun, L. Chen, Q. An, L. Mai, Layered VS2 nanosheet-based aqueous Zn ion battery cathode. Adv. Energy Mater. 7, 601920 (2017). https://doi.org/10.1002/aenm.201601920
[31] Y. Cheng, L. Luo, L. Zhong, J. Chen, B. Li et al., Highly reversible zinc-ion intercalation into chevrel phase Mo6S8 nanocubes and applications for advanced zinc-ion batteries. ACS Appl. Mater. Interfaces 8, 13673-13677 (2016). https://doi.org/10.1021/acsami.6b03197
[32] M.H. Alfaruqi, V. Mathew, J. Gim, S. Kim, J. Song, J.P. Baboo, S.H. Choi, J. Kim, Electrochemically induced structural transformation in a γ- MnO­2 cathode of a high capacity zinc-ion battery system. Chem. Mater. 26, 3609-3620 (2015). https://doi.org/10.1021/cm504717p
[33] B. Lee, H.R. Lee, H. Kim, K.Y. Chung, B.W. Cho, S.H. Oh, Elucidating the intercalation mechanism of zinc ions into alpha- MnO­2 for rechargeable zinc batteries. Chem. Commun. 51, 9265-9268 (2015). https://doi.org/10.1039/C5CC02585K
[34] B. Lee, H.R. Seo, H.R. Lee, C.S. Yoon, J.H. Kim, K.Y. Chung, B.W. Cho, S.H. Oh, Critical role of pH evolution of electrolyte in the reaction mechanism for rechargeable zinc batteries. ChemSusChem 9, 2948-2956 (2016). https://doi.org/10.1002/cssc.201600702
[35] B. Lee, C.S. Yoon, H.R. Lee, K.Y. Chung, B.W. Cho, S.H. Oh, Electrochemically-induced reversible transition from the tunneled to layered polymorphs of manganese dioxide. Sci. Rep. 4, 6066 (2014). https://doi.org/10.1038/srep06066
[36] M.H. Alfaruqi, J. Gim, S. Kim, J. Song, J. Jo, S. Kim, V. Mathew, J. Kim, Enhanced reversible divalent zinc storage in a structurally stable α- MnO­2 nanorod electrode. J. Power Sources 288, 320-327 (2015). https://doi.org/10.1016/j.jpowsour.2015.04.140
[37] H. Pan, Y. Shao, P. Yan, Y. Cheng, K.S. Han et al., Reversible aqueous zinc/manganese oxide energy storage from conversion reactions. Nat. Energy 1, 16039 (2016). https://doi.org/10.1038/nenergy.2016.39
[38] W. Sun, F. Wang, S. Hou, C. Yang, X. Fan et al., Zn/ MnO­2 battery chemistry with H+ and Zn2+ coinsertion. J. Am. Chem. Soc. 139, 9775-9778 (2017). https://doi.org/10.1021/jacs.7b04471
[39] G.G. Yadav, J.W. Gallaway, D.E. Turney, M. Nyce, J. Huang, X. Wei, S. Banerjee, Regenerable Cu-intercalated MnO­2 layered cathode for highly cyclable energy dense batteries. Nat. Commun. 8, 14424 (2017). https://doi.org/10.1038/ncomms14424
[40] N. Jabeen, A. Hussain, Q. Xia, S. Sun, J. Zhu, H. Xia, High-performance 2.6 V aqueous asymmetric supercapacitors based on in situ formed Na0.5MnO­2 nanosheet assembled nanowall arrays. Adv. Mater. 29, 1700804 (2017). https://doi.org/10.1002/adma.201700804
[41] A. Konarov, N. Voronina, J.H. Jo, Z. Bakenov, Y.-K. Sun, S.-T. Myung, Present and future perspective on electrode materials for rechargeable zinc-ion batteries. ACS Energy Lett. 3, 2620-2640 (2018). https://doi.org/10.1021/acsenergylett.8b01552
[42] M. Song, H. Tan, D. Chao, H.J. Fan, Recent advances in Zn-ion batteries. Adv. Funct. Mater. 28, 1802564 (2018). https://doi.org/10.1002/adfm.201802564
[43] J. Hao, J. Mou, J. Zhang, L. Dong, W. Liu, C. Xu, F. Kang, Electrochemically induced spinel-layered phase transition of Mn3O4 in high performance neutral aqueous rechargeable zinc battery. Electrochim. Acta 259, 170-178 (2018). https://doi.org/10.1016/j.electacta.2017.10.166
[44] D. Grujicic, B. Pesic, Reaction and nucleation mechanisms of copper electrodeposition from ammoniacal solutions on vitreous carbon. Electrochim. Acta 50, 4426-4443 (2005). https://doi.org/10.1016/j.electacta.2005.02.012
[45] A. Anderko, S.J. Sanders, R.D. Young, Real-solution stability diagrams: A thermodynamic tool for modeling corrosion in wide temperature and concentration ranges. Corrosion 53, 43-53 (1997). https://doi.org/10.5006/1.3280432
[46] A.G. Tyurin, A role of manganese in the corrosion and electrochemical behavior of stainless steels. Protect. Met. 41, 68-75 (2005). https://doi.org/10.1007/s11124-005-0010-7
[47] X. Zhou, C. Wei, M. Li, S. Qiu, X. Li, Thermodynamics of vanadium–sulfur–water systems at 298 K. Hydrometallurgy 106, 104-112 (2011). https://doi.org/10.1016/j.hydromet.2010.12.003
[48] M. Chamoun, W.R. Brant, C.-W. Tai, G. Karlsson, D. Noréus, Rechargeability of aqueous sulfate Zn/ MnO­2 batteries enhanced by accessible Mn2+ ions. Energy Storage Mater. 15, 351-360 (2018). https://doi.org/10.1016/j.ensm.2018.06.019
[49] K.J. Vetter, A general thermodynamic theory of the potential of passive electrodes and its influence on passive corrosion. J. Electrochem. Soc. 110, 597-605 (1963). https://doi.org/10.1149/1.2425837

Citation Information

Yongfeng Huang, Jian Mou, Wenbao Liu, Xianli Wang, Liubing Dong, Feiyu Kang, Chengjun Xu , Novel Insights into Energy Storage Mechanism of Aqueous Rechargeable Zn/MnO2 Batteries with Participation of Mn2+. Nano-Micro Lett.(2019) 11: 49. https://doi.org/10.1007/s40820-019-0278-9

History

Received: 15 April 2019 / Accepted: 14 May 2019 / Published online: 06 June 2019


Additional Info

  • Type of Publishing: JOUR - Journal
  • Title: Novel Insights into Energy Storage Mechanism of Aqueous Rechargeable Zn/MnO2 Batteries with Participation of Mn2+
  • Author: Yongfeng Huang, Jian Mou, Wenbao Liu, Xianli Wang, Liubing Dong, Feiyu Kang, Chengjun Xu
  • Year: 2019
  • Volume: 11
  • Journal Name: Nano-Micro Letters
  • ISSN: 2150-5551
  • URL: http://dx.doi.org/10.1007/s40820-019-0278-9
  • Abstract: Aqueous rechargeable Zn/MnO2 zinc-ion batteries (ZIBs) are reviving recently due to their low cost, non-toxicity, and natural abundance. However, their energy storage mechanism remains controversial due to their complicated electrochemical reactions. Meanwhile, to achieve satisfactory cyclic stability and rate performance of the Zn/MnO2 ZIBs, Mn2+ is introduced in the electrolyte (e.g., ZnSO4 solution), which leads to more complicated reactions inside the ZIBs systems. Herein, based on comprehensive analysis methods including electrochemical analysis and Pourbaix diagram, we provide novel insights into the energy storage mechanism of Zn/MnO2 batteries in the presence of Mn2+. A complex series of electrochemical reactions with the co-participation of Zn2+, H+, Mn2+, SO42-, and OH- were revealed. During the first discharge process, co-insertion of Zn2+ and H+ promotes the transformation of MnO2 into ZnxMnO4, MnOOH, and Mn2O3, accompanying with increased electrolyte pH and the formation of ZnSO4·3Zn(OH)2·5H2O. During the subsequent charge process, ZnxMnO4, MnOOH, and Mn2O3 revert to α-MnO2 with the extraction of Zn2+ and H+, while ZnSO4·3Zn(OH)2·5H2O reacts with Mn2+ to form ZnMn3O7·3H2O. In the following charge/discharge processes, besides aforementioned electrochemical reactions, Zn2+ reversibly insert into/extract from α-MnO2, ZnxMnO4, and ZnMn3O7·3H2O hosts; ZnSO4·3Zn(OH)2·5H2O, Zn2Mn3O8, and ZnMn2O4 convert mutually with the participation of Mn2+. This work is believed to provide theoretical guidance for further research on high-performance ZIBs.
  • Publish Date: Thursday, 06 June 2019
  • Start Page: 49
  • DOI: 10.1007/s40820-019-0278-9