Electrochemical Synthesis of Novel Zn-Doped TiO2 Nanotube/ZnO Nanoflake Heterostructure with Enhanced DSSC Efficiency

John K Aijo1, Johns Naduvath2,6 , Sudhanshu Mallick2, Jacob W. Pledger3, S.K Remillard3, P.A. DeYoung3, Manju Thankamoniamma4, T.Shripathi5, Rachel Reena Philip1,*

Abstract
icon-htmlFull Text Html
icon-pdf-smPDF w/ Links
icon-citExport Citation
Figures
+Show more

Nano-Micro Letters, October 2016, Volume 8, Issue 4, pp 381–387

First Online: 02 July 2016 (Article)

DOI: 10.1007/s40820-016-0099-z

*Corresponding author. E-mail: reenatara@rediffmail.com

 

Abstract

 


Schematic of fabrication of Zn-TONT/ZnO nanoflake heterostructure.
The paper reports fabrication of Zn-doped TiO2 nanotubes (Zn-TONT)/ZnO nanoflakes heterostructure for the first time, which shows improved performance as photoanode in dye sensitized solar cell (DSSC). The layered structure of this novel nanoporous structure has been analysed unambiguously by Rutherford backscattering spectroscopy, scanning electron microscopy and X-ray diffractometer. The cell using the heterostructure as photoanode manifests an enhancement of about an order in the magnitude of the short circuit current and a seven-fold increase in efficiency, over pure TiO2 photoanodes.  Characterizations further reveal that the Zn-TONT is preferentially oriented in [001] direction and there is a Ti metal depleted interface layer which leads to the better band alignment in DSSC.

 

Keywords

Zn-doped TiO2 nanotubes; ZnO nanoflakes; Heterostructures; DSSC

 

Full Text Html

 

1 Introduction

 

The ability to fine tune the opto-electronic and transport properties of the metal oxide semiconductors nominates them as promising candidates for chemical-gas sensing, photo catalysis, energy conversion, and storage applications [1]. Among the metal oxide semiconductors, TiO2 and ZnO have been studied extensively in the recent years owing to their exceptional characteristics such as high stability, low cost fabrication, non-toxicity, and excellent photo-electro chemical properties [2-5]. Nevertheless, these pure metal oxides individually exhibit relatively low energy conversion efficiencies because of the limited photo response range and the fast recombination rate of the generated charge carriers [6-9].

These drawbacks of the pure metal oxide semiconductors have led researchers to explore the heterostructures using TiO2 and ZnO. These heterostructures exhibit good stability because of the good compatibility between TiO2 and ZnO and similar band alignments [2]. Also TiO2/ZnO hetero structures are expected to act as better photoanodes on account of the combination of the very high reactivity of TiO2 and large binding energy of ZnO [10, 11].

Several attempts are being made to fabricate heterostructures based on nanostructures of TiO2 and ZnO such as TiO2 nanotube/ZnO nanorod composite, ZnO-coated TiO2 nanotubes, and branched ZnO nanorod/TiO2 nanotube arrays due to the high surface to volume ratio attainable [12-17]. It has been found that the presence of ZnO prevents the fast recombination of the photo generated charge carriers with the dye molecules in dye sensitized solar cells because of the slightly higher band gap of the ZnO compared to the TiO2 [18, 19]. The extension of the photo response range and enhanced mobility of the charge carrier can also be expected from these hetero structures.

In the present work, heterostructure of ZnO nanoflakes partially covering the Zn-doped TiO2 nanotube (Zn-TONT) was fabricated for the first time. The layer of ZnO nanoflakes are expected to increase the dye absorption and the Zn doping of TiO2 nanotubes tend to increase their electrical transport properties. The improved performance of a dye sensitized solar cell (DSSC) with Zn-TONT/ZnO nanoflake heterostructure instead of pure TONT as photoanode is also demonstrated.

 

2 Experimental Methods

 

The Zn-TONT/ZnO nanoflake heterostructure was fabricated by a two-step method (Fig. 1). In the first step well-aligned and uniform TONT were fabricated on titanium foil by electrochemical anodization [20]. In the second step Zn doping and tailoring of ZnO nanoflakes on the Zn-TONT were done using a three electrode system, where TONT was used as the working electrode, platinum rod as counter electrode, and Ag/AgCl as reference electrode  (3 M KCl electrolyte), with 0.1 M ZnSO4 in ionized water as the solution for doping. A negative voltage pulse of 1-2.5 V was applied to the working electrode for duration of 2-10 s to trigger the doping process.

Schematic of fabrication of Zn-TONT/ZnO nanoflake heterostructure.

Schematic of fabrication of Zn-TONT/ZnO nanoflake heterostructure.

The detailed analysis of the Zn-TONT/ZnO nanoflake heterostructure was performed using X-ray diffractometer (XRD), field emission scanning electron microscopy (FESEM), Rutherford backscattering spectroscopy (RBS) and X-ray photoelectron spectroscopy (XPS). The current density-voltage (J-V) data of the DSSC was carried on a Solar Simulator (NEWPORT) under the standard solar conditions.

 

3 Results and Discussion

 

The FESEM surface images of the pure TONT and Zn-TONT/ZnO nanoflakes are shown in Fig. 2. Figure 2a indicates that the pure TONT formed by electrochemical anodization possesses an approximate inner diameter of 100 nm, wall thickness of 16 nm and thickness of 6.9 µm. The side view of the as-formed aligned nanotubes is shown in the inset of Fig. 2a. Sponge-like ZnO nanoflakes (Fig. 2b) appear on the surface of TONT when doping was done for  a short time of ~2 s, and partially cover the top of the tubes upon annealing, as seen in the inset of Fig. 2b.

FESEM images of a top view of undoped TONT, and side view of undoped TONT (inset). b top view of Zn-TONT/ZnO nanoflake heterostructure, and top view of the heterostructure after annealing at 500 °C (inset).

FESEM images of a top view of undoped TONT, and side view of undoped TONT (inset). b top view of Zn-TONT/ZnO nanoflake heterostructure, and top view of the heterostructure after annealing at 500 °C (inset).

More detailed layered structures of both pure TONT and the heterostructure were studied using RBS of 2.97 MeV a particles, a technique that can effectively bring out the at% composition and thickness of different layers through SIMNRA fitting [21]. The RBS spectrum of pure TONT fitted with SIMNRA shows a structure of ~7 µm TiO2 as the top layer and a Ti metal substrate as the bottom layer (Fig. 3a).  The spectrum from the Zn-TONT/ZnO structure suggests four layers (Fig. 3b), with a partial coverage by ZnO flakes at the top surface and a slightly Ti depleted layer at the interface of the heterostructure. Partial coverage of ZnO flakes is simulated by superposing weighted models of ZnO covered Zn-TONT and uncovered Zn-TONT. The thickness of the ZnO flakes assuming ~14 % coverage of the top, is around 22 nm and the Zn-TONT beneath the ZnO layer consists of >3 µm with a Zn doping at% of  2.7±0.4. Between the TONT layer and the ZnO layer, the Ti depleted layer (Ti: 25.3±1.3 %) has a thickness of 320±30 nm. The fourth and last layer is the Ti metal substrate with infinite thickness.

RBS of a pure TONT (areal thickness of 1.1 × 1019 atoms cm-2), and b Zn-TONT/ZnO nanoflake heterostructure (Layer 1: areal thickness of 1.5 × 1017 atoms cm-2, Layer 2: areal thickness of 2.9 ×1018 atoms cm-2 , and Layer 3: areal thickness of  3  1019 atoms cm-2).

RBS of a pure TONT (areal thickness of 1.1 × 1019 atoms cm-2), and b Zn-TONT/ZnO nanoflake heterostructure (Layer 1: areal thickness of 1.5 × 1017 atoms cm-2, Layer 2: areal thickness of 2.9 ×1018 atoms cm-2 , and Layer 3: areal thickness of >3  1019 atoms cm-2).

RBS confirms that during the doping step, in-addition to the formation of ZnO nanoflakes on top, a small percentage of Zn was doped into the TONT, the adsorption has led to a preferential orientation of the nanocrystallites in the tube on annealing. This phenomenon has been discussed in detail elsewhere [22]. The 3 % Zn doping of the TiO2 nanotubes was confirmed by taking the XPS of the heterostructure after removing the top ZnO nanoflake layer by dipping in 1 M HCl for one hour. The inset of Fig. 4 shows the detailed spectrum of the titanium, oxygen, and zinc respectively.

XPS of the Zn-TONT with 3 % zinc doping.

XPS of the Zn-TONT with 3 % zinc doping.

The crystallinity of the annealed pure TONT and Zn-TONT/ZnO nanoflake heterostructure characterized by XRD (Fig. 5) reveals that the pure TONT (Fig. 5a) consist of (101), (004), (200), and (105) planes with preferential orientation along (101) plane (JCPDS 89-4203). Contrary to this observation, the TONT in the heterostructure (Fig. 5b) shows preferential orientation along (004) plane. This strong preferential orientation has been interpreted on the basis of the Zn assisted minimization of the surface energy of (004) plane [22].

XRD patterns of a pure TONT, and b Zn-TONT/ZnO nanoflake heterostructure.

XRD patterns of a pure TONT, and b Zn-TONT/ZnO nanoflake heterostructure.

When Zn is doped into the tubes and then annealed, the amorphous TONT break up into crystallites and Zn gets preferentially adsorbed on the higher surface energy (0.90 J m-2) facets {001} which possess more adsorption ability. The Zn adsorption reduces the surface energy of the facet, resulting in the enhancement of the surface area, until the differential adsorption ability of that facet gets weaker and further adsorption and growth are impeded. There will be no further reduction in the surface energy of the {001} facets and hence it does not go below the surface energy (0.44 J m-2) of {101} facets. During the stacking of the crystallites, the comparatively higher energy {001} facets connects each other and hence the {001} surfaces faces the tube up. The XRD peaks observed at 34.4° and 36.6° confirms the formation of the ZnO layer on the top of TONT (JCPDS- 79-0205).

The performance comparison of the TONT and the heterostructure Zn-TONT/ZnO nanoflake in DSSC application was done by fabricating both type of cells, one with TONT and the other with Zn-TONT/ZnO nanoflake heterostructure as the photoanode, and platinum-coated FTO as the front electrode. After dye sensitization of the photoanode with N719, a redox electrolyte was sandwiched between the photoanode and the front electrode for the regeneration of the dye molecules (Fig. 6a).

The J-V data of the DSSC is depicted in Fig. 6c. The J-V characteristics of the DSSC (Fig. 6c) using Zn-TONT/ZnO nanoflake heterostructure and the Zn-doped TONT after removing the top ZnO nanoflake layer are compared with that of DSSC using as prepared TONT. While the improvement in the open circuit voltage (Voc) with the heterostructure DSSC is only about 70 mV than that with pure TONT, the short circuit current for the heterostructure (ISc ~4 mA) is about an order of magnitude higher on comparison with the pure TONT (Isc~0.6 mA). The Voc and Isc of DSSC with Zn-doped TONT show a slight increase ~30 mV and 0.6 mA, respectively. This has produced a considerable increase (>7 times) in the efficiency of the heterostructure cell over the pure TONT based cell, fabricated and operated under the same conditions, while the efficiency of DSSC with Zn-doped TONT over that of pure TONT is ~ 2 times. The result shows that though efficiency is slightly increased in the DSSC using Zn-TONT in comparison with that using pure TONT, the DSSC fabricated with Zn-TONT/ZnO nanoflake heterostructure shows still a significant enhancement when compared to either of them. Hence, it can be concluded that the improved performance is due to the combined effect of ZnO nanoflake and preferential [001] orientation of the anatase TONT, where the effect of ZnO nanoflakes is more prominent than the orientation effect. The results emphasize the significance of TONT/ZnO photoanodes over pure TONT photoanodes, for improved DSSC performance.

a Schematic of the DSSC with Zn-TONT/ZnO nanoflake heterostructure, b band structure of the DSSC fabricated using Zn-TONT/ZnO nanoflake heterostructure, and c J-V curves of DSSCs.

a Schematic of the DSSC with Zn-TONT/ZnO nanoflake heterostructure, b band structure of the DSSC fabricated using Zn-TONT/ZnO nanoflake heterostructure, and c J-V curves of DSSCs.

The improvement in the efficiency of DSSC could be explained based on the more effective processes of carrier production and transport in the heterostructure-based DSSC whose band alignment is illustrated in Fig. 6b.  In TONT based DSSC when the solar radiation falls on the dye molecules through the transparent platinum FTO window and the electrons from the HOMO (highest occupied molecular orbital) of the N719 dye are excited to the LUMO (lowest unoccupied molecular orbital), the photo generated electrons are injected into the conduction band of the TONT and are collected by the Ti metal back contact. In this process, there is a large possibility for the charge recombination of the electrons in the conduction band of the TONT and holes present in the HOMO of the dye, which may reduce the efficiency of the device. In the Zn-TONT/ZnO nanoflake heterostructure based DSSC, the presence of ZnO nanoflakes (band gap ~3.37 eV with conduction band and valence band positioned slightly above that of the corresponding bands in TONT) on the top of the TiO2 nanotubes (band gap ~3.2 eV) decreases the recombination rate of the electrons owing to the small energy barrier created by them [19, 23]. In addition, ZnO lattice was reported to provide electron mobility almost 3 times larger compared to the TONT which facilitates faster transport of the generated electrons to the back metal contact [18]. This increased mobility thus acts as an additional factor that further reduces the recombination rate of the photo generated charge carriers. This synergetic property of Zn-TONT/ZnO nanoflakes in promoting efficient separation of carriers may be the reason for improved solar cell efficiency

 

4 Conclusion

 

In conclusion, a clear picture of the layered structure, morphology and crystallinity of the Zn-TONT/ZnO heterostructure was gained using RBS, SEM and XRD. The advantage of using heterostructures of the Zn-TONT/ZnO nanoflake heterostructure in a DSSC constructed by a cost-effective and highly reproducible method was analyzed. This layered heterostructure shows enhanced DSSC efficiency over the pure TiO2 nanotubes.

 

Acknowledgement

 

AJK, MT and RRP acknowledge UGC-DAE CSR, Indore for funding through a collaborative project and SAIF IIT Bombay for the help with SEM. The work at Hope College was supported by the Michigan Space Grant Consortium and by Hope College.  AJK and MT acknowledge DAE-BRNS for funding the preliminary works.

 

References

 

[1] I. Concina, A. Vomiero, Metal oxide semiconductor for dye and quantum-dot sensitized solar cells. Small 11(15), 1744-774 (2015). doi:10.1002/smll.201402334

[2] H. Cai, Q. Yang, Z. Hu, Z. Duan, Q. You, J. Sun, N. Xu, J. Wu, Enhanced photo electrochemical activity of vertically aligned ZnO coated TiO2 nanotubes. Appl. Phys. Lett. 104, 053114 (2014). doi:10.1063/1.4863852

[3] A. Hagfeldt, G. Boschloo, L. Sun, L. Kloo, H. Pettersson, Dye sensitized solar cells. Chem. Rev. 110(11), 6595-6663 (2010). doi:10.1021/cr900356p

[4] T.P. Gujarati, A.G. Ashish, M. Rai, M.M. Shajumon, Highly ordered vertical arrays of TiO2/ZnO hybrid nanowires: synthesis and electrochemical characterization. J. Nanosci. Nanotech. 15(8), 5833-5839 (2015). doi:10.1166/jnn.2015.10040

[5] B. Zhang, F. Wang, C. Zhu, Q. Li, J. Song, M. Zheng, L. Ma, W. Shen, A facileself-assembly synthesis of hexagonal ZnO nanosheet films and their photoelectrochemical properties. Nano-Micro Lett. 8(2), 137-142 (2016). doi:10.1007/s40820-015-0068-y

[6] P.E. De Jongh, E.A. Meulenkamp, D. Vanmackelbergh, J.J. Kelly, Charge carrier dynamics in illuminated particulate ZnO electrode. J. Phys. Chem. B 104(32), 7686-7693 (2000). doi:10.1021/jp000616a

[7] G.H. Schoenmakers, D. Vanmackelbergh, J.J. Kelly, Study of charge carrier dynamics at illuminated ZnO photoanodes. J. Phys. Chem. 100(8), 3215-3220 (1996). doi:10.1021/jp952392f

[8] A.J. Frank, N. Kopidakis, J.V. De Langemaat, Electrons in nanostructured TiO2 solar cells; transport, recombination and photovoltaic properties. Coordin. Chem. Rev. 248(13-14), 1165-1179 (2004). doi:10.1016/j.ccr.2004.03.015

[9] Y. Liu, H. Zhou, J. Li, H. Chen, D. Li, B. Zhou, W. Cai, Enhanced photoelectrochemical properties of Cu2O-loaded short TiO2 nanotube array electrode prepared by sonoelectrochemical deposition. Nano-Micro Lett. 2(4), 277-284 (2010). doi:10.3786/nml.v2i4.p277-284

[10] U. Diebold, The surface science of titanium dioxide. Surf. Sci. Rep. 48(5-8), 53-229 (2003). doi:10.1016/S0167-5729(02)00100-0

[11] A.B. Djurišić, X. Chen, V.H. Leung, A.M. Ching Ng, ZnO nanostructures: growth, properties and applications. J. Mater. Chem. 22(14), 6526-6535 (2012). doi:10.1088/0953-8984/16/25/R01

[12] Y. Yang, X. Wang, C. Sun, L. Li, Photoluminescence of ZnO nanorod-TiO2 nanotube hybrid arrays produced by electrodeposition. J. Appl. Phys. 105, 094304 (2009). doi:10.1063/1.3121202

[13] H. Cai, Q. You, Z. Hu, Z. Duan, Y. Cui, J. Sun, N. Xu, J. Wu, Fabrication and correlation between photoluminescence and photo electrochemical properties of vertically aligned ZnO coated TiO2 nanotube arrays. Sol. Energ. Mater. Sol. Cells 123, 233-238 (2014). doi:10.1016/j.solmat.2014.01.033 

[14] Y.C. Huang, S.Y. Chang, C.F. Lin, W.J. Tseng, Synthesis of ZnO nanorod grafted TiO2 nanotube 3-D array heterostructure as supporting platform for nanoparticle deposition. J. Mater. Chem. 21(36), 14056-14061 (2011). doi:10.1039/c1jm11659b

[15] W. Liu, P. Su, S. Chen, N. Wang, Y. Ma, Y. Liu, J. Wang, Z. Zhang, H. Li, T.J. Webster, Synthesis of TiO2 nanotubes with ZnO nanoparticles to achieve antibacterial properties and stem cell compatibility. Nanoscale 6(15), 9050-9062 (2014). doi:10.1039/C4NR01531B

[16] Y. Let, G. Zhao, M. Liu, Z. Zhang, X. Tong, T. Cao, Fabrication characterization and photoelectrocatalytic application of ZnO nanorods grafted on vertically aligned TiO2 nanotubes. J. Phys. Chem. C 113(44), 19067-19076 (2009). doi:10.1021/jp9071179

[17] F.X. Xiao, S.F. Hung, H.B. Tao, J. Miao, H.B. Yang, B. Liu, Spatially branched hierarchical ZnO nanorod-TiO2 nanotube array heterostructures for versatile photocatalytic and photoelectrocatalytic applications: towards intimate integration of 1D-1D nanostructures. Nanoscale 6(24), 14950-14961 (2014). doi:10.1039/c4nr04886e

[18] J. Ren, W. Que, X. Yin, Y. He, H.M.A. Javed, Novel fabrication of TiO2/ZnO nanotube array heterojunction for dye sensitized solar cells. RSC Adv. 4(15), 7454-7460 (2014). doi:10.1039/c3ra45741a

[19] S.S. Kim, S. In Na, Y.C. Nah, TiO2 nanotubes decorated with ZnO rod like nanostructures for efficient dye sensitized solar cells. Electrochimica Acta 58(1), 503-509 (2011). doi:10.1016/j.electacta.2011.09.076

[20] P. Roy, S. Berger, P. Schmuki, TiO2 Nanotubes: synthesis and applications. Angew. Chem. Int. Ed. 50(13), 2904-2939 (2011). doi:10.1002/anie.201001374

[21] M. Mayer, SIMNRA User's Guide, Report IPP 9/113, Max-Planck-InstitutfürPlasmaphysik,Garching, Germany, 1997.

[22] J.K. Aijo, N. Johns, S. Mallick, T. Shripathi, T. Manju, R.P. Reena, Novel cost effective fabrication technique for highly preferential oriented TiO2 nanotubes. Nanoscale 7(48), 20386-20390. doi:10.1039/C5NR06328K

C.S. Chou, F.C. Chou, Y.G. Ding, P. Wu, The effect of ZnO coating on the performance of a dye sensitized solar cell. Solar Energy 86(5), 1435-1442 (2012). doi:10.1016/j.solener.2012.02.003

References

[1] I. Concina, A. Vomiero, Metal oxide semiconductor for dye and quantum-dot sensitized solar cells. Small 11(15), 1744-774 (2015). doi:10.1002/smll.201402334

[2] H. Cai, Q. Yang, Z. Hu, Z. Duan, Q. You, J. Sun, N. Xu, J. Wu, Enhanced photo electrochemical activity of vertically aligned ZnO coated TiO2 nanotubes. Appl. Phys. Lett. 104, 053114 (2014). doi:10.1063/1.4863852

[3] A. Hagfeldt, G. Boschloo, L. Sun, L. Kloo, H. Pettersson, Dye sensitized solar cells. Chem. Rev. 110(11), 6595-6663 (2010). doi:10.1021/cr900356p

[4] T.P. Gujarati, A.G. Ashish, M. Rai, M.M. Shajumon, Highly ordered vertical arrays of TiO2/ZnO hybrid nanowires: synthesis and electrochemical characterization. J. Nanosci. Nanotech. 15(8), 5833-5839 (2015). doi:10.1166/jnn.2015.10040

[5] B. Zhang, F. Wang, C. Zhu, Q. Li, J. Song, M. Zheng, L. Ma, W. Shen, A facileself-assembly synthesis of hexagonal ZnO nanosheet films and their photoelectrochemical properties. Nano-Micro Lett. 8(2), 137-142 (2016). doi:10.1007/s40820-015-0068-y

[6] P.E. De Jongh, E.A. Meulenkamp, D. Vanmackelbergh, J.J. Kelly, Charge carrier dynamics in illuminated particulate ZnO electrode. J. Phys. Chem. B 104(32), 7686-7693 (2000). doi:10.1021/jp000616a

[7] G.H. Schoenmakers, D. Vanmackelbergh, J.J. Kelly, Study of charge carrier dynamics at illuminated ZnO photoanodes. J. Phys. Chem. 100(8), 3215-3220 (1996). doi:10.1021/jp952392f

[8] A.J. Frank, N. Kopidakis, J.V. De Langemaat, Electrons in nanostructured TiO2 solar cells; transport, recombination and photovoltaic properties. Coordin. Chem. Rev. 248(13-14), 1165-1179 (2004). doi:10.1016/j.ccr.2004.03.015

[9] Y. Liu, H. Zhou, J. Li, H. Chen, D. Li, B. Zhou, W. Cai, Enhanced photoelectrochemical properties of Cu2O-loaded short TiO2 nanotube array electrode prepared by sonoelectrochemical deposition. Nano-Micro Lett. 2(4), 277-284 (2010). doi:10.3786/nml.v2i4.p277-284

[10] U. Diebold, The surface science of titanium dioxide. Surf. Sci. Rep. 48(5-8), 53-229 (2003). doi:10.1016/S0167-5729(02)00100-0

[11] A.B. Djurišić, X. Chen, V.H. Leung, A.M. Ching Ng, ZnO nanostructures: growth, properties and applications. J. Mater. Chem. 22(14), 6526-6535 (2012). doi:10.1088/0953-8984/16/25/R01

[12] Y. Yang, X. Wang, C. Sun, L. Li, Photoluminescence of ZnO nanorod-TiO2 nanotube hybrid arrays produced by electrodeposition. J. Appl. Phys. 105, 094304 (2009). doi:10.1063/1.3121202

[13] H. Cai, Q. You, Z. Hu, Z. Duan, Y. Cui, J. Sun, N. Xu, J. Wu, Fabrication and correlation between photoluminescence and photo electrochemical properties of vertically aligned ZnO coated TiO2 nanotube arrays. Sol. Energ. Mater. Sol. Cells 123, 233-238 (2014). doi:10.1016/j.solmat.2014.01.033 

[14] Y.C. Huang, S.Y. Chang, C.F. Lin, W.J. Tseng, Synthesis of ZnO nanorod grafted TiO2 nanotube 3-D array heterostructure as supporting platform for nanoparticle deposition. J. Mater. Chem. 21(36), 14056-14061 (2011). doi:10.1039/c1jm11659b

[15] W. Liu, P. Su, S. Chen, N. Wang, Y. Ma, Y. Liu, J. Wang, Z. Zhang, H. Li, T.J. Webster, Synthesis of TiO2 nanotubes with ZnO nanoparticles to achieve antibacterial properties and stem cell compatibility. Nanoscale 6(15), 9050-9062 (2014). doi:10.1039/C4NR01531B

[16] Y. Let, G. Zhao, M. Liu, Z. Zhang, X. Tong, T. Cao, Fabrication characterization and photoelectrocatalytic application of ZnO nanorods grafted on vertically aligned TiO2 nanotubes. J. Phys. Chem. C 113(44), 19067-19076 (2009). doi:10.1021/jp9071179

[17] F.X. Xiao, S.F. Hung, H.B. Tao, J. Miao, H.B. Yang, B. Liu, Spatially branched hierarchical ZnO nanorod-TiO2 nanotube array heterostructures for versatile photocatalytic and photoelectrocatalytic applications: towards intimate integration of 1D-1D nanostructures. Nanoscale 6(24), 14950-14961 (2014). doi:10.1039/c4nr04886e

[18] J. Ren, W. Que, X. Yin, Y. He, H.M.A. Javed, Novel fabrication of TiO2/ZnO nanotube array heterojunction for dye sensitized solar cells. RSC Adv. 4(15), 7454-7460 (2014). doi:10.1039/c3ra45741a

[19] S.S. Kim, S. In Na, Y.C. Nah, TiO2 nanotubes decorated with ZnO rod like nanostructures for efficient dye sensitized solar cells. Electrochimica Acta 58(1), 503-509 (2011). doi:10.1016/j.electacta.2011.09.076

[20] P. Roy, S. Berger, P. Schmuki, TiO2 Nanotubes: synthesis and applications. Angew. Chem. Int. Ed. 50(13), 2904-2939 (2011). doi:10.1002/anie.201001374

[21] M. Mayer, SIMNRA User's Guide, Report IPP 9/113, Max-Planck-InstitutfürPlasmaphysik,Garching, Germany, 1997.

[22] J.K. Aijo, N. Johns, S. Mallick, T. Shripathi, T. Manju, R.P. Reena, Novel cost effective fabrication technique for highly preferential oriented TiO2 nanotubes. Nanoscale 7(48), 20386-20390. doi:10.1039/C5NR06328K

C.S. Chou, F.C. Chou, Y.G. Ding, P. Wu, The effect of ZnO coating on the performance of a dye sensitized solar cell. Solar Energy 86(5), 1435-1442 (2012). doi:10.1016/j.solener.2012.02.003

Citation Information

John K Aijo, Johns Naduvath, Sudhanshu Mallick, Jacob W. Pledger, S.K Remillard, P.A. DeYoung, Manju Thankamoniamma, T.Shripathi, Rachel Reena Philip, Electrochemical Synthesis of Novel Zn-Doped TiO2 Nanotube/ZnO Nanoflake Heterostructure with Enhanced DSSC Efficiency. Nano-Micro Lett. 8(4), 381-387 (2016). http://dx.doi.org/10.1007/s40820-016-0099-z

History

Received: 11 May 2016 / Accepted: 8 June 2016


Additional Info

  • Type of Publishing: JOUR - Journal
  • Title:

    Electrochemical Synthesis of Novel Zn-Doped TiO2 Nanotube/ZnO Nanoflake Heterostructure with Enhanced DSSC Efficiency

  • Author: John K Aijo, Johns Naduvath, Sudhanshu Mallick, Jacob W. Pledger, S.K Remillard, P.A. DeYoung, Manju Thankamoniamma, T.Shripathi, Rachel Reena Philip
  • Year: 2016
  • Volume: 8
  • Issue: ?
  • Journal Name: Nano-Micro Letters
  • Publisher: OPEN ACCESS HOUSE SCIENCE & TECHNOLOGY
  • ISSN: 2150-5551
  • URL: http://dx.doi.org/10.1007/s40820-016-0099-z
  • Abstract:

    The paper reports fabrication of Zn-doped TiO2 nanotubes (Zn-TONT)/ZnO nanoflakes heterostructure for the first time, which shows improved performance as photoanode in dye sensitized solar cell (DSSC). The layered structure of this novel nanoporous structure has been analysed unambiguously by Rutherford backscattering spectroscopy, scanning electron microscopy and X-ray diffractometer. The cell using the heterostructure as photoanode manifests an enhancement of about an order in the magnitude of the short circuit current and a seven-fold increase in efficiency, over pure TiO2 photoanodes.  Characterizations further reveal that the Zn-TONT is preferentially oriented in [001] direction and there is a Ti metal depleted interface layer which leads to the better band alignment in DSSC.