25September2017

Nano-Micro Letters

Novel Hybrid Nanoparticles of Vanadium Nitride/Porous Carbon as An Anode Material for Symmetrical Supercapacitor

View ResearcherID and ORCID

Yunlong Yang1, Kuiwen Shen1, Ying Liu1, Yongtao Tan1, Xiaoning Zhao1, Jiayu Wu1, Xiaoqin Niu2, Fen Ran1,*

Abstract
icon-htmlFull Text Html
icon-pdf-smPDF w/ Links
icon-citExport Citation
Figures
+Show more

Nano-Micro Lett. (2017) 9: 6

Published Online: 13 September 2016 (Article)

DOI: 10.1007/s40820-016-0105-5

*Corresponding author. ranfen@163.com; or ranfen@lut.cn

 

Abstract

 


Schematic illustration for the preparation of VN/CNPs.
Hybrid materials of vanadium nitride and porous carbon nanoparticles (VN/PCNPs) were fabricated by a facile pyrolysis process of vanadium pentoxide (V2O5) xerogel and melamine at relatively low temperature of 800 °C for supercapacitor application. The effects of the feed ratio of V2O5 to melamine (r), and nitrogen flow rate on the microstructure and electrochemical performance were also investigated. It was found that the size of as-synthesized nanoparticles is about 20 nm. Both r value and N2 flow rate have enormous impacts on morphology and microstructure of the nanoparticle, which correspondingly determined the electrochemical performance of the material. The VN/C hybrid nanoparticles exhibited high capacitive properties, and a maximum specific capacitance of 255.0 F g-1 was achieved at a current density of 1.0 A g-1 in 2 M KOH aqueous electrolyte and the potential range from 0 to -1.15 V. In addition, symmetrical supercapacitor fabricated with as-synthesized VN/PCNPs presents a high specific capacitance of 43.5 F g-1 at 0.5 A g-1 based on the entire cell, and an energy density of 8.0 Wh kg-1 when the power density was 575 W kg-1. Even when the power density increased to 2831.5 W kg-1, the energy density still remained 6.1 Wh kg-1.

 

Keywords

Supercapacitors; Nanoparticle; Vanadium Nitride; Porous carbon; Hybrid Materials

 

Full Text Html

 

 1 Introduction

 

The rapid development of global economy and growing human population worldwide followed by environmental pollution and energy crisis have increased the need for some clean renewable energy sources like solar and wind for powering the electrical grid [1-2]. However, most of these energy sources cannot become continuously available on demand because of their intermittence [3-4]. As such, the development of reliable and environmentally friendly approaches for energy conversion and storage is one of the key challenges that our society is facing [5-6]. Among various energy storage devices, supercapacitors, also called electrochemical capacitors (ECs), are generally viewed as a promising energy storage approach used in hybrid electric vehicles, stand-by power systems, and other portable electronics [3, 7-9]. Despite the fact that supercapacitors exhibit greater power, longer cycle life, and much faster response time than batteries, their practical application is still limited by the low energy density, which is significantly lower than that of batteries [10]. According to E = CV2 (E is energy density, C is capacitance, and V is operation voltage window), enhancing C and widening V can be employed to increase energy density of supercapacitors [11-12].

As we all know, based on the energy storage mechanisms, ECs has two basic types: electric double-layer capacitors (EDLCs) and pseudocapacitors. EDLCs store charge in a thin double-layer located at the interface between the electrolyte and the electrode [10], while pseudocapacitance involving surface or near surface redox reactions through a faradaic process, which offers a means of achieving high energy density at high charge–discharge rates [13]. It has been demonstrated that the performance of ECs intimately depends on the physical and chemical properties of their electrode materials [4, 14], and the energy density is associated with faradaic reactions which is at least 10 times greater than that of double-layer processes [10, 15-17]. Therefore, it is necessary to develop better electrode materials both at storing and delivering large amounts of energy [4, 13].

Transition metal nitrides, especially vanadium nitride (VN) are currently one of the most promising materials for electrodes of supercapacitors owing to its excellent mechanical strength, high electronic conductivity and good mechanical strength [18-21]. Recent years, major progress in the theoretical and practical research have been developed to fabricate various VN materials used as supercapacitor electrode. Choi et al. synthesized nanostructured VN for pseudocapacitor and reported the highest specific capacitance of 1340 F g-1 at a scan rate of 2 mV s-1 in 1 M KOH electrolyte [22]. The high capacitance is ascribed to a pseudocapacitance contribution from the nitride [23]; however, the rate capability of these materials still requires further improvement. Lately, nanocrystalline VN was fabricated by temperature-programmed ammonia reduction of V2O5 and a capacitance of 186 F g-1 in 1 M KOH electrolyte at 1 A g-1 [18] was found. Zhou and his co-workers also synthesized VN powder with a capacitance of 161 F g-1 at 30 mV s-1 by calcining V2O5 xerogel in a furnace under anhydrous NH3 atmosphere at 400 °C [24]. In fact, the electronic conductivity plays a great impact on material’s electrochemical performance. For this purpose, Ghimbeu and his co-workers synthesized vanadium nitride/carbon nanotube (VN/CNTs) composites using a sol-gel approach in presence of CNTs [25]. The VN/CNTs composites delivered high capacitance retention (58 %) at high current density (30 A g-1) compared with just 7 % of the pristine VN. More recently, Shu and his co-workers reported a capacitance of 413 F g-1 at the current density of 1 A g-1 and a retention about 88 % of its maximal capacitance at a current load of 4 A g-1 [23, 26-27]. Unfortunately, despite the fact that these nanocrystalline VN performed an excellent rate capability, they still exhibit relatively short cycle life and low voltage window, which is crucial for the energy density and applications of supercapacitors. Also, the reactive process is still unclear, which is crucial for us to find out the relationship between microstructure and performance.

In this article, vanadium nitride/carbon (VN/C) hybrid nanoparticles were successfully synthesized by pyrolysis of V2O5 xerogel and melamine precursor at 800 °C under N2 atmosphere. Thermogravimetry-differential scanning calorimetry was used to simulate the pyrolysis process of precursor in order to make it clear what is the possible reaction mechanism and what are the behaviors of reactants during nitration. We also make a detailed discussion about the relationships between performances and different microstructures obtained by varying the feed ratio of V2O5 xerogel to C3H6N6 and N2 flow rate during reaction. The results indicate that the feed ratio of V2O5 xerogel to C3H6N6 and N2 flow rate have enormous impacts on morphology and microstructure of the obtained composites, which also greatly influences the electrochemical performances.

 

2. Experimental

 

2.1 Chemicals

 

Vanadium pentoxide (V2O5, analytical reagent) and hydrogen peroxide (H2O2, analytical reagent) were purchased from Sinopharm Chemical Reagent Co. Ltd. and used as received. Vinylcyanide (AN, analytical reagent) was purchased from Sinopharm Chemical Reagent Co. Ltd, and subjected to distillation prior to use. Melamine (C3H6N6, analytical reagent) and all the other chemicals were purchased from Shanghai Meixing Chemical Reagent Factory, P.R. China, and used without further treatment.

 

2.2 Synthesis of Hybrid Vanadium Nitride/Porous Carbon Nanoparticles (VN/PCNPs)

 

In a typical synthesis, as Scheme 1 shows, V2O5 xerogel was prepared by slowly adding 2 g V2O5 powder into 60 mL 30 wt% H2O2 under magnetic stirring until gels formed, which was dried under vacuum at 40 °C for 24 h. After that, the ground V2O5 xerogel powder and melamine were mechanically mixed completely. The mixture used as precursor was heated up to 800 °C in a tube furnace under N2 atmosphere at a temperature rate of 5 °C min-1 and kept at 800 °C for 3 h, and then black VN/CNPs were obtained. The VN/CNPs prepared with different feed ratios of V2O5 xerogel to melamine of 1:5, 1:10, 1:20, and 1:30 (wt%) were named as VN/CNP-5, VN/CNP-10, VN/CNP-20, and VN/CNP-30, respectively. And VN/CNP-10 samples prepared at different N2 flow of 20, 40, and 70 mL min-1 were named as VN/CNP-10-20, VN/CNP-10-40, and VN/CNP-10-70, respectively.

 

2.3 Structure Characterization

 

The microstructure and morphology were characterized by transmission electron microscope (TEM, JEOL, JEM-2010, Japan), field emission scanning electron microscope (SEM, JEOL, JSM-6700F, Japan), and energy dispersive X-ray (EDX) spectroscopy. X-ray diffraction (XRD) patterns were recorded with a Rigaku D/MAX 2400 diffractometer (Japan) with Cu Kα radiation (λ = 1.5418 Å) operating at 40 kV and 60 mA. Thermo gravimetric analysis (TGA) and differential scanning calorimetry (DSC) measurements were carried out in air, and in nitrogen at a heating rate of 10 °C min-1 on a NETZSCH STA 449F3, respectively.

 

2.4 Electrochemical Tests

 

All electrochemical measurements were performed using an electrochemical working station (CHI660E, Shanghai, China). The electrochemical performances of electrode materials were tested in a three-electrode system in 2 M KOH aqueous solution at room temperature with a platinum foil used as counter electrode, and the saturated calomel used as reference electrode (SCE). The working electrodes were prepared according to the method reported in the literatures [28-29]. Typically, 80 wt% of active materials was mixed with 7.5 wt% of acetylene black, 7.5 wt% of graphite and 5 wt% polytetrafluoroethylene, and then pressed onto a Ni-foam current collector at 10 MPa and dried at 60 °C for 8 h. The total quantity of the active substance was 4 mg and had a geometric surface area of 1 cm2. The electrochemical performances of electrodes were characterized with cyclic voltammetry (CV), galvanostatic charge-discharge and impedance spectroscopy tests in 2 M KOH electrolyte. The corresponding specific capacitances were calculated from the discharging time and based on the formula of C = (IDt)/(mDV), where C (F g-1) is the specific capacitance, I(A) is the discharge current, Dt (s) is the discharge time, DV (V) represents the potential drop during discharge process, and m (g) is the mass of the active material. The cyclic stability measurement was carried out on a Land cell tester for 1000 cycles.

For the symmetrical supercapacitor, electrochemical tests were conducted in a traditional two-electrode symmetric supercapacitor system with room temperature in 2 M KOH aqueous solution. The measurements of the device mainly include CV, galvanostatic charge-discharge and impedance spectroscopy. The CV curves were acquired in the voltage range from 0 to -1.15 V vs Hg/HgO at the sweep rate range from 5 to 50 mV s-1, and the galvanostatic measurement of the cell was characterized at the current density from 0.5 to 5 A g-1. Electrochemical impedance spectroscopy was measured in a frequency range from 0.01 to 100 kHz under the current density of 1 A g-1.

 

3. Results and Discussion

 

3.1 Effects of [V2O5]/[C3H6N6] amount and N2 Flow on Microstructure of VN/PCNPs

 

In order to understand the growth mechanism of VN/CNPs, the effects of [V2O5]/[C3H6N6] and N2 flow on Microstructure of VN/CNPs were investigated in detail. Figure 1 depicts the typical high-and-low magnification SEM images of VN/CNP-5, VN/CNP-20, and VN/CNP-30 at different [V2O5]/[C3H6N6] values of 1:5, 1:20, and 1:30, revealing a porous network microstructure feature and areagglomerates mainly composed of numerous uniformly-sized spherical nanoparticles with a average diameter of 20 nm. However, there were differences among these VN/CNPs prepared at different [V2O5]/[C3H6N6] values. When the amount of C3H6N6 was small ([V2O5]/[C3H6N6]=1:5), limited gas and carbon were produced during the pyrolysis process, so the obtained VN/CNP-5 was similar to a blocky-shaped aggregation with few pores accordingly (Fig. 1a and b). With the increase of C3H6N6 amount, the independent nanoparticles with porous structure were obtained (Fig. 1c and d). All of these changes were usually ascribed to the released gas and remained carbon during pyrolysis, which simoutanesously inhibited the formation of hard agglomerates and recrystallization of the VN particle [26-27]. Besides, the boundry between nanoparticles also became more obvious with the increase of C3H6N6 amount, indicating a high active surface area. When the [V2O5]/[C3H6N6] value decreased to 1:30, the obtained VN/CNPs had a porous network morphology and packed with countless particles with a grain size of regarding 20 nm (Fig. 1e and f), which may be an advantage in electrochemical application.

Figure 1 SEM images of a and b VN/CNP-5, c and d VN/CNP-20, and e and f VN/CNP-30.

Figure 1 SEM images of a and b VN/CNP-5, c and d VN/CNP-20, and e and f VN/CNP-30.

The effect of N2 flow on microstructure of VN/CNPs was further studied. Figure 2 shows the SEM images of VN/CNP-10-20, VN/CNP-10-40, and VN/CNP-10-70 prepared at different N2 flow of 20, 40, and 70 mL min-1. Slowly N2 (20 mL min-1) flow was virtually impossible to extract plenty of released gas from the reacting phase within a short time; therefore, much pores formed from the escaping gas was rarely observed (Fig. 2a and b). The morphology of VN/CNP-10-20 was full of rugosity and presents a rippled or flaky structure [30]. As the N2 flow increased to 40 mL min-1, the morphology were the combination both aggregates of nanoparticles and the remaining flaky structure (Fig. 2c and d). Afterwards, as the N2 flow further increased (40 mL min-1), the rippled and flaky structure was replaced by numerous completely, which was also accompanied with the growing pores and grain boundary (Fig. 2e and f).

Figure 2 SEM images of VN/CNP-10-20, VN/CNP-10-40, and VN/CNP-10-70.

Figure 1 SEM images of VN/CNP-10-20, VN/CNP-10-40, and VN/CNP-10-70.

Figure S1 shows the N2 adsorption-desorption isotherms of the as prepared VN/CNP-10-20, VN/CNP-10-40, and VN/CNP-10-70. All of N2 adsorption-desorption isotherms (Fig. S1a, c and e) display combined characteristics of type I/IV, which indicates a hierarchical porous structure combined of micro-, meso- and macropores [31-32]. The BET surface area of VN/CNP-10-20, VN/CNP-10-40 and VN/CNP-10-70 are 206.7, 184.0, and 217.0 m2 g-1, respectively. In fact, according to the analysis of N2 adsorption-desorption isotherms for these samples, the BET surface areas of VN/CNP-10-20, VN/CNP-10-40 and VN/CNP-10-70 are very approximate and similar. Notably, the values of BET surface areas have no direct relationship with electrochemical performance. Moreover, based on the same feed ratio in precursor, it is the surface areas of the electrode materials that contact with electrolyte ions contribute to the capacitance. Based on the results from SEM, the high surface area of VN/CNP-10-20 mainly thanks to the corrugated structure while the high surface area of VN/CNP-10-70 mainly due to the great space benefit from the abundant porosity among the countless nanoparticles. However, VN/CNP-10-40 exhibits a transition state structure combined aggregates of nanoparticles and the remaining cataclastic corrugated structure. Such structure in transition state has less surface area than rippled or flaky structure for VN/CNP-10-20 and simultaneously less than the high surface area benefit from the abundant pores in VN/CNP-10-70. Consequently, such difference of structure resulted a relatively low surface area for VN/CNP-10-40compared to these of VN/CNP-10-20 and VN/CNP-10-70.

Additionally, all the pore size distribution curves exhibit a typical hierarchical porous characteristic. According to the t-plot method the surface area of them were 32.6, 26.7 and 22.2 m2 g-1, respectively. From these pore size distribution curves, we found that all samples had a hierarchical porous structure; and as the N2 flow varied from 20 to 40 mL min-1, the composite had relatively more abundant mesoporous. These mesoporous structure can accelerate the diffusion of electrolyte ion during the interior of the electrode materials, which is crucial to enhance electrochemical performance [33]. Furthermore, when the N2 flow increased to 70 mL min-1, the prepared VN/C composite exhibited greatest amount of macropores than that of the others.

 

3.2 Detailed Morphology, Structure and Composition of VN/CNPs

 

Based on the above investigation, to better understand the forming mechanism of VN nanoparticle, thermal analysis technology was applied to simulate the preparation process. Figure 3 shows TGA and DSC curves of the precursor composed of V2O5 xerogel and C3H6N6 ([V2O5]/[C3H6N6]=1:10) in the temperature range from room temperature to 800 °C at a heating rate of 5 °C min-1 in flowing N2 atmosphere, which is the same reaction condition as that of pyrolysis process in furnace. It can be see that there were three peaks at TGA curve in the temperature ranges from room temperature to 170, 330–380, and 380–670 °C, respectively; and a small peak at about 175 °C, a broad endothermic peak at 360 °C and a spike at 640 °C in DSC curve can be attributed to the loss of crystal water in V2O5 xerogel, decomposition of melamine, reduction and nitridation of V2O5 xerogel. Based on these results, one can describe the actually pyrolysis process as follows: when the mixture of V2O5 xerogel and C3H6N6 was heated up to 150 °C, small molecules and crystal water got lose until the temperature grow up to 200 °C. Then, along with the increase of temperature, the melamine decomposed gradually in the range of 330-380 °C and etching ammonia, nitrogen, and other cyanide. The released nitrogenous substances began to diffuse into the intra lamellar space and react with V2O5 xerogel kept reacting with V2O5 xerogel till the temperature rising to 640 °C, and then the remaining V2O5 xerogel melted to liquid state and reacted with residual nitrogen-rich substances in the three-dimensional of the sample, which agrees well with a spike in DSC curve at 640 °C. More importantly, the pyrolysis of melamine and thus etching nitrogen-contained chemicals would produce porosity, and this kind of reaction would cut large-scale melamine into pieces. Based on these analyses, VN/CNPs would be architected as nanoparticles together with micro/meso porous network.

Figure 3 The TGA and DSC analysis of precursor (Simulation of preparation process of VN/CNPs).

Figure 3 The TGA and DSC analysis of precursor (Simulation of preparation process of VN/CNPs).

Figures 4a, b shows the typical high-and-low magnification SEM images of V2O5 xerogel. Apparently, the morphology of the prepared V2O5 xerogel exhibited aggregates without obvious pores and nanoparticles from Fig. 4b. Hence, we can conclude that the nanoparticles of vanadium nitride and porous carbon hybrid materials formed during the high temperature processing not come from the V2O5 xerogel. Figure 4c shows that the hybrid nanoparticles were prepared with an average particle size of 20 nm, which agrees well with the size obtained from TEM (Fig. 4d and Fig. 4e). It can be seen from the SEM and TEM images that the prepared nanoparticles were size-uniform and the boundaries between nanoparticles are apparent. EDX spectrum as shown in Fig. 4f) reveals that the product mainly composed of C, N and V (the peak of Cu was corresponding to the copper substrate used to support the sample during the test of EDX). It is interesting that the atom contents of V and N are 19.87 and 18.67 at%, respectively. Notably, this result was very close to the mole ratio value of V to N in VN molecule.

Figure 4 a and b SEM images of V2O5 xerogel; c SEM image, d and e TEM images, and f EDX spectrum of VN/CNP-10.

Figure 4 a and b SEM images of V2O5 xerogel; c SEM image, d and e TEM images, and f EDX spectrum of VN/CNP-10.

Based on the elements analysis by EDX, the phase constitution of the product and corresponding intermediate and raw material were further studied by XRD. Figure 5a is the XRD patterns of V2O5 powder, V2O5 xerogel, and VN/CNPs. It is found that commercial V2O5 sample was highly crystallized (curve a), whereas when it transformed into V2O5 xerogel, the sample was almost non-crystal (curve c). Compared to that of V2O5 powder and V2O5 xerogel, the XRD pattern of VN/CNPs shows a broad peak located in the range of 15-30° and centered at 22° (curve b), which is the characteristic peak of amorphous carbon; and three diffraction peaks were observed at 2θ values of 37.4°, 43.6°, and 63.4°, which can be indexed to the cubic VN (ICDD PDF 35-768). The peaks of VN were far weaker than that of VN in the reported works [26-27, 34], and no other peak of impurities or nitrides being detected, demonstrating that the synthesized VN was of low crystalline, which agrees well with the result of TEM mentioned above.

Figure 5 a The XRD patterns of a V2O5 powder, b VN/CNPs-10, and c V2O5 xerogel. b The TGA and DSC analysis of VN/CNP-10.

Figure 5 a The XRD patterns of a V2O5 powder, b VN/CNPs-10, and c V2O5 xerogel. b The TGA and DSC analysis of VN/CNP-10.

The composition of VN/CNPs was also investigated by TGA together with DSC under a constant dried air-flow, as shown in Fig. 5b. The sample was heated from room temperature to 640 °C at a heating rate of 5 °C min-1. The weight loss stage below 100 °C was due to the loss of surface absorbed water, and the slight weight loss stage between 100 °C and 200 °C was due to the loss of crystal water. With the increase of temperature, the TGA curve had tendency of ascending first and descending in succession. In fact, the inverse U-curve results from the combustion weight loss of carbon and oxidation weight gain of VN. Above 500 °C, the sample kept stable weight. In particular, there were two broad exothermic peaks over lapped at 175 and 440 °C, respectively. Besides, there was a broad endothermic in DSC curve corresponding with the melt of V2O5 transformed from VN. In general, after thermo-treated from room temperature to 900 °C, the weight loss was measured to be 9.96 wt%, and the residue was 90.68 wt%, which was contributed by V2O5 transformed from VN. By calculation, the VN/CNPs involved 64.77 wt% of VN, and 35.23 wt% of carbon; these data is great consistent with the result from EDX analysis.

Figure 6 shows further confirmation by XPS analysis.  The full XPS spectrum (Fig. 6a) exhibits that the prepared VN/CNPs mainly composed of C, N, V, and O elements. The high-resolution of C 1s spectrum (Fig. 6b) shows three fitting peaks: the peak around 284.8 eV can be ascribed to the indication of the doubly coordinated carbon atoms; and the other two peaks of 286.4 and 288.9 eV were assigned to C-N, and C=O bonds, respectively [18, 35]. The characteristic peaks corresponded to the existence of O 1s, V 2p1, and V 2p3 peaks are showed in Fig. 6c). The peaks centered at 514.1 and 521.6 eV belonged to vanadium in the VN structure [36-37], while peaks regarding at 517.2, and 524.1 eV ascribed to that in V-O on the material surface [38]. The other peaks at 532.7, and 530.1 eV supported the existence of –OH groups and a thin oxide layer at the surface of VN/CNPs after exposure in air [39]. Furthermore, a strong characteristic peak was observed at 397.4 eV for N 1s (Fig. 6d), belonging to that in VN structure [18]; and at 400.6 eV was ascribed to quaternary nitrogen [38]. Based on the above analysis, we can conclude that the prepared VN/C material is mostly attributable to VN and carbon, with a small amount of complex vanadium oxide on the surface of the composite [39-41]. From these analysis, we can conclude the products are mainly composed of VN and carbon. Moreover, these results show that the hybrid nanoparticles were prepared with an average particle size of 20 nm. Consequently, these structures will have an intensively effects on electrochemical performance of VN/CNPs.

Figure 6 XPS spectra of a full scan, and curve fittings of b C 1s, c V 2p3, and d N 1s for VN/CNP-10.

Figure 6 XPS spectra of a full scan, and curve fittings of b C 1s, c V 2p3, and d N 1s for VN/CNP-10.

 

3.3 Electrochemical Performance of VN/CNPs

 

The electrochemical performance of the prepared VN/CNPs was measured by CV and galvanostatic charge-discharge method. The electrodes were prepared using the obtained materials as active materials and tested in a three-electrode system in 2 M KOH aqueous electrolyte at room temperature. Figure 7a shows the representative CV curves of the prepared VN/CNP-10 at different scan rates from 5 to 50 mV s-1, displaying almost rectangular shape under lower scan rates. Meanwhile, a pair of loosely defined redox peaks was also observed in the whole potential range even at higher scan rate. This indicates that there were some slight reversible faradic redox reactions apart from the predominated absorption and desorption process. The slight shift of peak position in the curves is due to the voltage drop caused by electric resistance at high sweep rates [42]. Figure 7b displays the galvanostatic charging-discharging curves of VN/CNP-10 at current densities varying from 0.5 to 5.0 A g-1. The curves were not linear symmetrical shapes but slightly distorted, which agrees well with the result of CV analysis. By calculation, the specific capacitances of VN/CNP-10 tested at the current density of 1.0, 2.0, 3.0 and 5.0 A g-1 were 255.0, 218.0, 201.0, and 175.0 F g-1, respectively, which are comparable to the other reported nano-VN [26-27, 43]; the superior electrochemical performance can be attributed to the nanoscaled structure and the quantum dot-sized VN.

Figure 7 a CV at various scan rates (5-50 mV s-1), and b Galvanostatic charge-discharge curves at various currents (0.5-5 A g-1) of VN/CNP-10.

Figure 7 a CV at various scan rates (5-50 mV s-1), and b Galvanostatic charge-discharge curves at various currents (0.5-5 A g-1) of VN/CNP-10.

 

3.4 Effects of [V2O5]/[C3H6N6] amount and N2 Flow on Electrochemical Performance of VN/CNPs

 

After the investigation for the effects of [V2O5]/[C3H6N6] and N2 flow on Microstructure of VN/CNPs, the corresponding effects on electrochemical performance were also sdutied. Figure 8 shows the electrochemical performance of VN/CNP-5, VN/CNP-10, and VN/CNP-20. It could be found that the shape of all the CV curves (Fig. 8a) was analogous to rectangular behavior, especially when the amount of C3H6N6 was sufficient. In addition, with the increase of melamine amount, rectangular characteristic became more evident, demonstrating a better capacitive behavior and electrochemical reversibility [43-44] due to the increase of the residual carbon within the obtained VN/CNPs during the reactive process. Accordingly, the CV curves became more similar to the typical rectangular characteristic of carbon. However, the CV curves still had a pairs of weak redox reaction peaks when the mass ratio of [V2O5]/[C3H6N6] were 1:5 and 1:10, preferably the former. The appearance of weak peaks demonstrates that there is slight redox processes occurring in the as-prepared VN/C composites [45]. All the galvanostatic charge-discharge curves of the VN/CNPs at the current density of 1 A g-1 (Fig. 8b) were similar to a typical triangular shape except being less than perfect symmetry, which can be ascribed to the slight redox reaction and is congruent to the result of CV test [46]. According to calculation, the mass specific capacitances of VN/CNP-5, VN/CNP-10 and VN/CNP-20 were 273.0, 261.0 and 166.7 F g-1 at 0.5 A g-1, respectively.

Figure 8 Comparisons of a CV, b galvanostatic charge-discharge curves, c complex-plane impedance plot, and d cycle life of VN/CNPs (scan rate= 10 mV s-1, current density= 1 A g-1, 2 M KOH aqueous solution).

Figure 8 Comparisons of a CV, b galvanostatic charge-discharge curves, c complex-plane impedance plot, and d cycle life of VN/CNPs (scan rate= 10 mV s-1, current density= 1 A g-1, 2 M KOH aqueous solution).

In fact, all of the VN/CNPs composed of VN and porous carbon with different ratios. As a consequent, the capacitance was mainly contributed by electric double layer capacitance resulted from porous carbon and pseudocapacitance resulted by VN. As we all know, based on their mechanism of charge storage, the porous carbon usually possess outstanding power capabilities and high conductivity but a low specific energy while the VN exhibits relatively higher capacitance but an inferior rate capability compared to porous carbon. Thus, like this work, developing hybrid materials with rational ratio is meaningful for the enhancement of electrochemical performance. When the VN amount in the composite is very low, the capacitance of the composite would be not good. Moreover, the capacitance would decrease with the increase of vanadium source in the precursor; however, too much vanadium nitride and too low carbon means the absence of the advanced structure and the decrease of high conductivity. Specifically, compare to the samples of VN/CNP-5 and VN/CNP-10, VN/CNP-20 exhibited a lowest capacitance because of the lowest VN content in the sample.

Electrochemical Impedance Spectroscopy (EIS) measurement is of great importance in revealing the essence of electrochemical reaction. As shown in Fig. 8c, EIS measurements of all the VN/CNPs were conducted for further understanding the relationship between the structure and electrochemical properties. As we know, a typical Nyquist diagrams primarily includes an oblique straight line in the low frequency and a semicircle in high frequency [41]. The semicircle denotes charge-transfer resistance (Rct) and all the VN/C composites display small and similar semidiameter (inset in Fig. 8c), which is closely related to the surface property of the VN/CNPs [47]. Intercepts of the curves on horizontal axis were applied to analysis the internal resistances (Rb) and illustrate its use on experiment data. The Rb of VN/CNP-5, VN/CNP-10, and VN/CNP-20 were 0.97, 1.00 and 1.02 Ω, respectively [48], reflecting an excellent electron transport efficient. With the decrease of frequency, the plot of VN/CNP-10 manifested the lower Warburg impedance compared with that of the other three approximately parallelline [49-51]. Furthermore, the slight difference of resistance among these materials was mainly resulted from the synergistic effect combined morphology and composition. With the increase of C3H6N6 amount, on one hand, the growing enriched porous structure and carbon content are beneficial to the transportation of ion and electron; on the other hand, the increasing boundaries among nanoparticles give rise to the inter particle resistance. This was a formidable challenge during electrochemical process [52-53]

In addition, the VN/CNP-20 and VN/CNP-30 exhibited relatively low specific capacitance of 166.7 and 90 F g-1 at the current density of 0.5 A g-1, respectively. As the current density increased to 5 A g-1, the capacitance retention for VN/CNP-20 is 62 % but a higher value of 66.7 % for VN/CNP-30. These differences can mainly be ascribed to the structure and carbon content in sample. To be sure, based on the above analysis, the electrochemical performances for them were still inferior to these of VN/CNP-5 and VN/CNP-10. Hence, test of cycle life was applied to further evaluate the impact come from the feed ratio on electrochemical performance of composites under the other two feed ratios. As shown in Fig. 8d, the cycling property of the VN/CNPs was tested at the current density of 1 A g-1. According to calculation result, VN/CNP-5 and VN/CNP-10 retained 51 % and 66 % of their initial capacitances after 1000 cycles. Consequently, in general, the VN/CNP-10 had a slightly better stable performance than that of the other. In addition, the reasons that lead to the capacitance fade of VN can be concluded to be originated from the morphological change combined with the partial oxidation of VN during cycling, which lead to the increase of the charge transfer resistance [36, 54]. Based on these changes, the increase of diffusion resistance of ions can also result the volume changes of VN, including aggregation or the collapse of the structure of electrode [55]. Moreover, some VN may dissolve into KOH electrolyte when the cycle time is too long”.

After previously discussion regarding quite a few problems, various situations involving electrochemical performances were investigated in detail. Figure 9a compares the CV profiles of all VN/CNPs composites obtained under diverse N2 flow. By comparing these CV curves, we found that all the CV shapes were analogue and without distinct redox peaks were observed, meaning a similar electrochemical process for all composites. One more point need to be stated is that the area regarding CV profile of VN/CNPs obtained under N2 flow of 40 mL min-1 was bigger than the others, indicating a higher specific capacitance. As shown in Fig. 9b, according to the calculation, the specific capacitances of VN/CNPs obtained under the N2 flow of 20, 40, and 70 mL min-1 at the current density of 1 A g-1 were 88.7, 233.0, 255.0 F g-1, respectively.

Figure 9 Comparisons of a CV, b galvanostatic charge-discharge, and c complex-plane impedance plots of VN/CNP-10-20, VN/CNP-10-40, and VN/CNP-10-70 (scan rate=10 mV s-1, current density= 1 A g-1, 2 M KOH aqueous solution).

Figure 9 Comparisons of a CV, b galvanostatic charge-discharge, and c complex-plane impedance plots of VN/CNP-10-20, VN/CNP-10-40, and VN/CNP-10-70 (scan rate=10 mV s-1, current density= 1 A g-1, 2 M KOH aqueous solution).

In this study, the fabrication strategies and processes for VN/CNP-10-20 and VN/CNP-10-40 are the same but the N2 flow during the pyrolysis is different. As the analysis by SEM in Fig. 2, slowly flowing N2 (20 mL min-1) endows VN/CNP-10-20 a rippled or flaky and corrugated structure while the greater flowing N2 (40 mL min-1) endows VN/CNP-10-40 a structure combined aggregates of nanoparticles and the remaining flaky structure. Moreover, according to N2 adsorption-desorption isotherms, the BET surface areas of VN/CNP-10-20, VN/CNP-10-40 are very approximate and a relatively high value for VN/CNP-10-20 strictly speaking. However, one thing to note here is that such high values of BET surface area means high capacitance. Moreover, it is the surface areas of the electrode materials that contact with electrolyte ions contribute to the capacitance. However, the utilization of surface area may be dramatically different during the charge-discharge process. Specifically, VN/CNP-10-20 possesses a low surface area used for charge storage because the corrugated or flaky structure is hard for the access and diffusion of electrolyte ion, which lead to low contact area corresponds to a low capacitance. On the other hand, the electrolyte ion can diffuse into the interior of VN/CNP-10-40 through the rich pores between nanoparticles, which provides a sufficient utilization of surface area and correspondingly a higher capacitance than that of VN/CNP-10-20.

As shown in Fig. 9c, all the EIS spectra of VN/CNPs obtained under various N2 flow were approximately parallel to each other at low frequency meaning a similar electrochemical process controlled by diffusion. Similarly, in high frequency region, the nearly identical radiuses of semicircles also imply the equal charge transfer resistance (Rct). Whereas, from the intercepts on real axis, the internal resistances of VN/CNPs obtained under the nitrogen flow of 20, 40, and 70 mL min-1 were 1.08, 0.97, and 1.00 Ω, respectively. It is concluded that the emergence of this difference may be linked to the rising interparticle resistence resulted from the growing grain boundary [30, 53].

In conclude, by analyzing the relationship between structure and performance, high contact area, porous structure and appropriate ratio between VN amount and carbon would endow outstanding electrochemical performances (including good conducticity, high specific capacitance, exceeding rate ability and long cycle life).

 

3.5. Electrochemical Performance of the Device Based on VN/CNPs

 

Figure 10a depicts the CV curves of the assembled symmetrical device in the voltage range from 0 to 1.15 V at scanning rates between 5 and 50 mV s-1. The CV plots exhibit a nearly rectangular and mirror shape with respect to the zero-current line indicative of the superior capacitive behavior and fast charge/discharge rate. Figure 10b shows the galvanostatic charge-discharge curves obtained from the full device at current densities vary from 0.5 to 5.0 A g-1. The symmetrical shapes of the curves without obvious ohmic drop further indicated the excellent capacitive behavior. The specific capacitances of the device were calculated to be 43.5 and 33.4 F g-1 at current densities of 0.5 and 5.0 A g-1 based on the whole device, respectively.

Figure 10 a CV, and b galvanostatic charge-discharge curves of the hybrid supercapacitor. c Ragone plots of the VN/CNPs symmetric supercapactitor, and the values reported for other SC devices for comparison [25, 57-59], d Green LED was powered by the tandem VN/CNPs-SSCs. (scan rate=10 mV s-1, current density= 1A g-1, 2 M KOH aqueous solution).

Figure 10 a CV, and b galvanostatic charge-discharge curves of the hybrid supercapacitor. c Ragone plots of the VN/CNPs symmetric supercapactitor, and the values reported for other SC devices for comparison [25, 57-59], d Green LED was powered by the tandem VN/CNPs-SSCs. (scan rate=10 mV s-1, current density= 1A g-1, 2 M KOH aqueous solution).

Energy density and power density are two important parameters for the evaluation of the entire device [56]. Figure 10c compares the power and energy densities of VN/CNP symmetric supercapacitor (SC) to the other reported nitrides based supercapacitors. As is shown in the figure, VN/CNP-SC delivered an energy density of 8.0 Wh kg-1 and a high power density of 2831.5 W kg-1, which was higher than these of recently reported TiN-based SCs [57], VN-based SCs [58], VN/CNTs-based SCs [25] and other symmetric SCs [59], even the VOX//VN asymmetric SCs [58]. Figure 10d exhibits the assembled device in series can light up green LED that have the lowest working potential of 3.0 V.

 

4. Conclusion

 

In summary, we report a convenient strategy to prepare VN/CNP composites by pyrolysising the precursor of V2O5 xerogel and C3H6N6. The results confirmed the samples exhibited porous network morphology with nanoparticles of a grain size of around 20 nm. Our examinations manifested that the feed ratio had a crucial effect on construction of structure and thus affected the electrochemical performances. The VN/CNPs prepared at mass ratio of [V2O5]/[C3H6N6] of 1:10 had a slightly better electrochemical performances than that of the others, including the specific capacitance of 255.0 F g-1 at 1 A g-1, the wide potential window range from -1.15~0 V, and a relatively high cycling stability of 66 % after 1000 cycles. Meanwhile, the N2 flow also had a significant impact on the morphology and performances of composites. Furthermore, the sample obtained at the N2 flow of 70 mL min-1 had a remarkable specific capacitance of 255.0 F g-1 and a relatively low internal resistance of 0.85 Ω. All of these performances can be ascribed to their appropriate porous structure and interparticle resistence. Notably, the symmetrical-supercapacitor boasted a high specific capacitance of 43.5 F g-1 at 0.5 A g-1 and an energy density of 8.0 Wh kg-1 when the power density was 575.0 W kg-1. Even when the power density increased to 2831.5 W kg-1, the energy density was still 6.1 Wh kg-1. Furthermore, the convenient and safe strategy and deep understanding reaction meachnism are of great importance to design other materials and apply in related applications.

 

Acknowledgments

 

This work was partly supported by the National Natural Science Foundation of China (51203071, 51363014 and 51463012), China Postdoctoral Science Foundation (2014M552509, 2015T81064), Natural Science Funds of the Gansu Province (2015GS05123), the Program for Hongliu Distinguished Young Scholars in Lanzhou University of Technology (J201402), and the University Scientific Research Project of Gansu Province (2014B-025).

 

References

 

[1] R.M. Dell, D.A.J. Rand, Energy storage-a key technology for global energy sustainability. J. Power Sources 100(1-2), 2-17 (2001). doi:10.1016/S0378-7753(01)00894-1

[2] X. Lu, T. Liu, T. Zhai, G. Wang, M. Yu, S. Xie, Y. Ling, Y Tong, Improving the Cycling Stability of Metal–Nitride Supercapacitor Electrodes with a Thin Carbon Shell. Adv. Energy Mater. 4(4), 168-175 (2014). doi:10.1002/aenm.201300994

[3] P. Simon, Y. Gogotsi, Materials for electrochemical capacitors. Nat. Mater. 7(11), 845-854 (2008). doi:10.1038/nmat2297

[4] L.F. Chen, X.D. Zhang, H.W. Liang, M. Kong, Q.F. Guan, Synthesis of nitrogen-doped porous carbon nanofibers as an efficient electrode material for supercapacitors. ACS Nano 6(8), 7092-7102 (2012). doi:10.1021/nn302147s

[5] F. Bonaccorso, L. Colombo, G. Yu, M. Stoller, V. Tozzini, Graphene, related two-dimensional crystals, and hybrid systems for energy conversion and storage. Science 347(6217), 1246501 (2015).  doi:10.1126/science.1246501

[6] M.S. Balogun, W. Qiu, J. Jian, Y. Huang, Y. Luo, X.H. Lu, Vanadium Nitride Nanowire Supported SnS2 Nanosheets with High Reversible Capacity as Anode Material for Lithium Ion Batteries. ACS Appl. Mater. Inter. 7(41), 23205–23215 (2015).  doi:10.1021/acsami.5b07044

[7] J.R. Miller, P. Simon, Electrochemical capacitors for energy management. Science 321(5889), 651-652 (2008). doi:10.1126/science.1158736

[8] F. Su, C.K. Poh, J.S. Chen, G. Xu, D. Wang, X.W. Lou, Nitrogen-containing microporous carbon nanospheres with improved capacitive properties. Energ. Environ. Sci. 4(3), 717-724 (2011).  doi:10.1039/C0EE00277A

[9] Y. Zhai, Y. Dou, D. Zhao, P.F. Fulvio, R.T. Mayes, S. Dai, Carbon materials for chemical capacitive energy storage. Adv. Mater. 23(42), 4828-4850 (2011). doi:10.1002/adma.201100984

[10] I.E. Rauda, V. Augustyn, B. Dunn, S.H. Tolbert, Enhancing pseudocapacitive charge storage in polymer template mesoporous materials. Accounts Chem. Res. 46(5), 1113-1124 (2013). doi:10.1021/ar300167h

[11] A. Burke, Ultracapacitors: why, how, and where is the technology. J. Power Sources 91(1), 37-50 (2000). doi:10.1016/S0378-7753(00)00485-7

[12] Y. Gogotsi, P. Simon, True performance metrics in electrochemical energy storage. Science 334(6058), 917-918 (2011). doi:10.1126/science.1213003

[13] V. Augustyn, P. Simon, B. Dunn, Pseudocapacitive oxide materials for high-rate electrochemical energy storage. Energ. Environ. Sci. 7(5), 1597-1614 (2014). doi:10.1039/c3ee44164d

[14] A.S. Arico, P. Bruce, B. Scrosati, J Tarascon, W.V. Schalkwijk, Nanostructured materials for advanced energy conversion and storage devices. Nat. Mater. 4(5), 366-377 (2005). doi:10.1038/nmat1368

[15] B.E. Conway, Electrochemical supercapacitors, Kluwer Academic Plenum Press, New York, 1999. doi:10.1007/978-1-4757-3058-6

[16] G. Wang, L. Zhang, J. Zhang, A review of electrode materials for electrochemical supercapacitors. Chem. Soc. Rev. 41(2), 797-828 (2012). doi:10.1039/C1CS15060J

[17] B.E. Conway, W.G. Pell, Double-layer and pseudocapacitance types of electrochemical capacitors and their applications to the development of hybrid devices. J. Solid State Electr. 7(9), 637-644 (2003). doi:10.1007/s10008-003-0395-7

[18] A.M. Glushenkov, D. Hulicova-Jurcakova, D. Llewellyn, et al. Structure and capacitive properties of porous nanocrystalline VN prepared by temperature-programmed ammonia reduction of V2O5. Chem. Mater. 22(3), 914-921 (2009). doi:10.1021/cm901729x

[19] O. Bondarchuk, A. Morel, D. Bélanger, E. Goikolea, T. Brousse, Thin films of pure vanadium nitride: Evidence for anomalous non-faradaic capacitance. J. Power Sources 324, 439-446 (2016). doi:10.1016/j.jpowsour.2016.05.093

[20] A. Morel, Y. Borjon-Piron, R. L. Porto, T. Brousse, D. Bélanger. Suitable Conditions for the Use of Vanadium Nitride as an Electrode for Electrochemical Capacitor. J. Electrocheml Soc. 163(6), A1077-A1082 (2016). doi:10.1149/2.1221606jes

[21] Y. Zhong, X. Xia, F. Shi, J Zhan, J. Tu, Transition Metal Carbides and Nitrides in Energy Storage and Conversion. Adv Sci. 3(5), 201500286 (2016). doi:10.1002/advs.201500286

[22] D. Choi, P.N. Kumta, Chemically synthesized nanostructured VN for pseudocapacitor application. Electrochem. Solid ST 8(8), A418-A422 (2005). doi:10.1149/1.1951201

[23] M.S. Balogun, W. Qiu, W. Wang, P. Fang, X. Lu, Recent advances in metal nitrides as high-performance electrode materials for energy storage devices. J. Mater. Chem. A 3(4), 1364-1387 (2015). doi:10.1039/C4TA05565A

[24] X. Zhou, H. Chen, D. Shu, C. He, J. Nan, Study on the electrochemical behavior of vanadium nitride as a promising supercapacitor material. J. Phys. Chem. Solids. 70(2), 495-500 (2009). doi:10.1016/j.jpcs.2008.12.004

[25] C.M. Ghimbeu, E. Raymundo-Piñero, P. Fioux, F. Béguin, C. Vix-Guterl, Vanadium nitride/carbon nanotube nanocomposites as electrodes for supercapacitors. J. Mater. Chem. 21(35), 13268-13275 (2011). doi:10.1039/c1jm11014d

[26] F. Cheng, C. He, D. Shu, H. Chen, J. Zhang, Preparation of nanocrystalline VN by the melamine reduction of V2O5 xerogel and its supercapacitive behavior. Mater. Chem. Phys. 131(1), 268-273 (2011). doi:10.1016/j.matchemphys.2011.09.040

[27] D. Shu, C. Lv, F. Cheng, C. He, K. Yang, Enhanced capacitance and rate capability of nanocrystalline VN as electrode materials for supercapacitors. Int. J. Electrochem. Sci. 8(1), 1209-1225 (2013).

[28] J. Lang, X. Yan, W. Liu, R. Wang, Q. Xue, Influence of nitric acid modification of ordered mesoporous carbon materials on their capacitive performances in different aqueous electrolytes. J. Power Sources 204(1), 220-229 (2012). doi:10.1016/j.jpowsour.2011.12.044

[29] H. Fan, F. Ran, X. Zhang, H Song, W Jing, Easy fabrication and high electrochemical capacitive performance of hierarchical porous carbon by a method combining liquid-liquid phase separation and pyrolysis process. Electrochim. Acta. 138(25), 367-375 (2014). doi:10.1016/j.electacta.2014.06.118

[30] W. Ai, J. Jiang, J. Zhu, Z. Fan, Y. Wang, Supramolecular polymerization promoted in situ fabrication of nitrogen-doped porous grapheme sheets as anode materials for Li-ion batteries. Adv. Energy Mater. 5(15), 1500559 (2015). doi:10.1002/aenm.201500559

[31] Y. Han, X. Dong, C. Zhang, S. Liu, Hierarchical porous carbon hollow-spheres as a high performance electrical double-layer capacitor material. J. Power Sources 211, 92-96 (2012). doi:10.1016/j.jpowsour.2012.03.053

[32] Z.C. Yang, C.H. Tang, H. Gong, X. Li, J. Wang, Hollow spheres of nanocarbon and their manganese dioxide hybrids derived from soft template for supercapacitor application. J. Power Sources 240(240), 713-720 (2013). doi:10.1016/j.jpowsour.2013.05.034

[33] F. He, Z. Hu, K. Liu, S. ZhangH. Liu, In situ fabrication of nickel aluminum-layered double hydroxide nanosheets/hollow carbon nanofibers composite as a novel electrode material for supercapacitors. J. Power Sources 267(4), 188-196 (2014). doi:10.1016/j.jpowsour.2014.05.084

[34] Y. Su, I. Zhitomirsky, Hybrid MnO2/carbon nanotube-VN/carbon nanotube supercapacitors. J. Power Sources 267, 235-242 (2014). doi:10.1016/j.jpowsour.2014.05.091

[35] E.F.D. Souza, C.A. Chagas, T.C. Ramalho, V.T.D SilvaD.L.M Aguiar, A combined experimental and theoretical study on the formation of crystalline vanadium nitride (VN) in low temperature through a fully solid-state synthesis route. J. Phys. Chem. C 117(48), 25659-25668 (2013). doi:10.1021/jp410885u

[36] B. Gao, X. Li, X. Guo, X. Zhang, X. Peng, Nitrogen-doped carbon encapsulated mesoporousvanadium nitride nanowires as self-supported electrodes for flexible all-solid-state supercapacitors. Adv. Mater. Interfaces 2(13), 1500211 (2015). doi:10.1002/admi.201500211

[37] X. Zhou, C. Shang, L. Gu, S DongX Chen, Mesoporous coaxial titanium nitride-vanadium nitride fibers of core–shell structures for high-performance supercapacitors. ACS Appl. Mater. Inter. 3(8), 3058-3063 (2011). doi:10.1021/am200564b

[38] Y. M. Shul'Ga, V.N. Troitskii, Study of the surface of finely divided titanium nitride by X-ray photoelectron spectroscopy. Rev. Mex. Biodivers. 6(18), 681-684 (2006). doi:10.1007/BF00797433

[39] D. Choi, G.E. Blomgren, P.N. Kumta, Fast and reversible surface redox reaction in nanocrystalline vanadium nitride supercapacitors. Adv. Mater. 18(9), 1178-1182 (2006). doi:10.1002/adma.200502471

[40] H. Zhao, M. Lei, X. Chen, W. Tang, Facile route to metal nitrides through melamine and metal oxides. J. Mater. Chem. 16(45), 4407-4412 (2006). doi:10.1039/b611381h

[41] J. Buha, I. Djerdj, M. Antonietti, M Niederberger, Thermal transformation of metal oxide nanoparticles into nanocrystalline metal nitrides using cyanamide and urea as nitrogen source. Chem. Mater. 19(14), 3499-3505 (2007). doi:10.1021/cm0701759

[42] Y. Wang, Z. Hong, M. Wei, Y. Xia, Layered H2Ti6O13-Nanowires: A new promising pseudocapacitivematerial in non-aqueous electrolyte. Adv. Funct. Mater. 22(24), 5185-5193 (2012). doi:10.1002/adfm.201200766

[43] K. Shen, F. Ran, Y. Tan, X. Niu, H. Fan, Toward interconnected hierarchical porous structure via chemical depositing organic nano-polyaniline on inorganic carbon scaffold for supercapacitor. Synth. Met. 199, 205-213 (2015). doi:10.1016/j.synthmet.2014.11.034

[44] H. Fan, F. Ran, X. Zhang, H. Song, X. Niu, Hollow carbon microspheres/MnO2 nanosheets composites: hydrothermal synthesis and electrochemical behaviors. Nano-Micro Lett. 7(1), 59-67 (2015). doi:10.1007/s40820-014-0019-z

[45] R. Wang, J. Lang, P. Zhang, Z. Lin, X. Yan, Fast and large lithium storage in 3D porous VN nanowires–graphene composite as a superior anode toward high-performance hybrid supercapacitors. Adv.  Funct. Mater. 25(15), 2270-2278 (2015). doi:10.1002/adfm.201404472

[46] L. Zhao, L.Z. Fan, M.Q. Zhou, H. Guan, S. Qiao, Nitrogen-containing hydrothermal carbons with superior performance in supercapacitors. Adv. Mater. 22(45), 5202-5206 (2010). doi:10.1002/adma.201002647

[47] X. Zhou, H. Chen, D. Shu, C. He, J. Nan, Study on the electrochemical behavior of vanadium nitride as a promising supercapacitor material. J. Phys. Chem. Solids. 70(2), 495-500 (2009). doi:10.1016/j.jpcs.2008.12.004

[48] M.D. Stoller, S. Park, Y. Zhu, J. An, R.S. Ruoff, Graphene-based ultracapacitors. Nano Lett. 8(10), 3498-3502 (2008). doi:10.1021/nl802558y

[49] S. Boukhalfa, K. Evanoff, G. Yushin, Atomic layer deposition of vanadium oxide on carbon nanotubes for high-power supercapacitor electrodes. Energ. Environ. Sci. 5(5), 6872-6879(2012). doi:10.1039/c2ee21110f

[50] M.W. Xu, D.D. Zhao, S.J. Bao, H.L. Li, Mesoporous amorphous MnO2 as electrode material for supercapacitor. J. Solid State Electr. 11(8), 1101-1107 (2007). doi:10.1007/s10008-006-0246-4

[51] S. S. Zhang, K. Xu, T.R. Jow, Electrochemical impedance study on the low temperature of Li-ion batteries. Electrochim. Acta 49(7), 1057-1061 (2004). doi:10.1016/j.electacta.2003.10.016

[52] S. Cong, Y. Tian, Q. Li, Z. Zhao, F. Geng, Single-crystalline tungsten oxide quantum dots for fast pseudocapacitor and electrochromic applications. Adv. Mater. 26(25), 4260-4267 (2014). doi:10.1002/adma.201400447

[53] R. Wang, J. Lang, Y. Liu, Z. Lin, X. Yan, Ultra-small, size-controlled Ni(OH)2 nanoparticles: elucidating the relationship between particle size and electrochemical performance for advanced energy storage devices. NPG Asia Mater. 7(6), e183 (2015). doi: 10.1038/am.2015.42

[54] Y. Xu, J. Wang, L. Shen, H. Dou, X. Zhang, One-dimensional vanadium nitride nanofibers fabricated by electrospinning for supercapacitors. Electrochim. Acta 173, 680-686 (2015). doi:10.1016/j.electacta.2015.05.088

[55] L. Wang, J. Sun, R. Song, S. Yang, H. Song, Hybrid 2D-0D graphene-VN quantum dots for superior lithium and sodium storage. Adv. Energy Mater. 2015. doi:10.1002/aenm.201502067

[56] C. Zhu, P. Yang, D. Chao, X. Wang, X. Zhang, All metal nitrides solid-state asymmetric supercapacitors. Adv. Mater. 27(31), 4566-4571 (2015). doi:10.1002/adma.201501838

[57] X. Lu, G. Wang, T. Zhai, M. Yu, S. Xie, Stabilized TiN nanowire arrays for high-performance and flexible supercapacitors. Nano Lett. 12(10), 5376-81 (2012). doi:10.1021/nl302761z

[58] X. Lu, M. Yu, T. Zhai, G. Wang, S. Xie, High energy density asymmetric quasi-solid-state supercapacitor based on porous vanadium nitride nanowire anode. Nano Lett. 3(6), 2628-2633 (2013). doi:10.1021/nl400760a

[59] S. Zhang, N. Pan, Supercapacitors Performance Evaluation. Adv. Energy Mater. 5(6), 1401401 (2014). doi:10.1002/aenm.201401401

References

[1] R.M. Dell, D.A.J. Rand, Energy storage-a key technology for global energy sustainability. J. Power Sources 100(1-2), 2-17 (2001). doi:10.1016/S0378-7753(01)00894-1

[2] X. Lu, T. Liu, T. Zhai, G. Wang, M. Yu, S. Xie, Y. Ling, Y Tong, Improving the Cycling Stability of Metal–Nitride Supercapacitor Electrodes with a Thin Carbon Shell. Adv. Energy Mater. 4(4), 168-175 (2014). doi:10.1002/aenm.201300994

[3] P. Simon, Y. Gogotsi, Materials for electrochemical capacitors. Nat. Mater. 7(11), 845-854 (2008). doi:10.1038/nmat2297

[4] L.F. Chen, X.D. Zhang, H.W. Liang, M. Kong, Q.F. Guan, Synthesis of nitrogen-doped porous carbon nanofibers as an efficient electrode material for supercapacitors. ACS Nano 6(8), 7092-7102 (2012). doi:10.1021/nn302147s

[5] F. Bonaccorso, L. Colombo, G. Yu, M. Stoller, V. Tozzini, Graphene, related two-dimensional crystals, and hybrid systems for energy conversion and storage. Science 347(6217), 1246501 (2015).  doi:10.1126/science.1246501

[6] M.S. Balogun, W. Qiu, J. Jian, Y. Huang, Y. Luo, X.H. Lu, Vanadium Nitride Nanowire Supported SnS2 Nanosheets with High Reversible Capacity as Anode Material for Lithium Ion Batteries. ACS Appl. Mater. Inter. 7(41), 23205–23215 (2015).  doi:10.1021/acsami.5b07044

[7] J.R. Miller, P. Simon, Electrochemical capacitors for energy management. Science 321(5889), 651-652 (2008). doi:10.1126/science.1158736

[8] F. Su, C.K. Poh, J.S. Chen, G. Xu, D. Wang, X.W. Lou, Nitrogen-containing microporous carbon nanospheres with improved capacitive properties. Energ. Environ. Sci. 4(3), 717-724 (2011).  doi:10.1039/C0EE00277A

[9] Y. Zhai, Y. Dou, D. Zhao, P.F. Fulvio, R.T. Mayes, S. Dai, Carbon materials for chemical capacitive energy storage. Adv. Mater. 23(42), 4828-4850 (2011). doi:10.1002/adma.201100984

[10] I.E. Rauda, V. Augustyn, B. Dunn, S.H. Tolbert, Enhancing pseudocapacitive charge storage in polymer template mesoporous materials. Accounts Chem. Res. 46(5), 1113-1124 (2013). doi:10.1021/ar300167h

[11] A. Burke, Ultracapacitors: why, how, and where is the technology. J. Power Sources 91(1), 37-50 (2000). doi:10.1016/S0378-7753(00)00485-7

[12] Y. Gogotsi, P. Simon, True performance metrics in electrochemical energy storage. Science 334(6058), 917-918 (2011). doi:10.1126/science.1213003

[13] V. Augustyn, P. Simon, B. Dunn, Pseudocapacitive oxide materials for high-rate electrochemical energy storage. Energ. Environ. Sci. 7(5), 1597-1614 (2014). doi:10.1039/c3ee44164d

[14] A.S. Arico, P. Bruce, B. Scrosati, J Tarascon, W.V. Schalkwijk, Nanostructured materials for advanced energy conversion and storage devices. Nat. Mater. 4(5), 366-377 (2005). doi:10.1038/nmat1368

[15] B.E. Conway, Electrochemical supercapacitors, Kluwer Academic Plenum Press, New York, 1999. doi:10.1007/978-1-4757-3058-6

[16] G. Wang, L. Zhang, J. Zhang, A review of electrode materials for electrochemical supercapacitors. Chem. Soc. Rev. 41(2), 797-828 (2012). doi:10.1039/C1CS15060J

[17] B.E. Conway, W.G. Pell, Double-layer and pseudocapacitance types of electrochemical capacitors and their applications to the development of hybrid devices. J. Solid State Electr. 7(9), 637-644 (2003). doi:10.1007/s10008-003-0395-7

[18] A.M. Glushenkov, D. Hulicova-Jurcakova, D. Llewellyn, et al. Structure and capacitive properties of porous nanocrystalline VN prepared by temperature-programmed ammonia reduction of V2O5. Chem. Mater. 22(3), 914-921 (2009). doi:10.1021/cm901729x

[19] O. Bondarchuk, A. Morel, D. Bélanger, E. Goikolea, T. Brousse, Thin films of pure vanadium nitride: Evidence for anomalous non-faradaic capacitance. J. Power Sources 324, 439-446 (2016). doi:10.1016/j.jpowsour.2016.05.093

[20] A. Morel, Y. Borjon-Piron, R. L. Porto, T. Brousse, D. Bélanger. Suitable Conditions for the Use of Vanadium Nitride as an Electrode for Electrochemical Capacitor. J. Electrocheml Soc. 163(6), A1077-A1082 (2016). doi:10.1149/2.1221606jes

[21] Y. Zhong, X. Xia, F. Shi, J Zhan, J. Tu, Transition Metal Carbides and Nitrides in Energy Storage and Conversion. Adv Sci. 3(5), 201500286 (2016). doi:10.1002/advs.201500286

[22] D. Choi, P.N. Kumta, Chemically synthesized nanostructured VN for pseudocapacitor application. Electrochem. Solid ST 8(8), A418-A422 (2005). doi:10.1149/1.1951201

[23] M.S. Balogun, W. Qiu, W. Wang, P. Fang, X. Lu, Recent advances in metal nitrides as high-performance electrode materials for energy storage devices. J. Mater. Chem. A 3(4), 1364-1387 (2015). doi:10.1039/C4TA05565A

[24] X. Zhou, H. Chen, D. Shu, C. He, J. Nan, Study on the electrochemical behavior of vanadium nitride as a promising supercapacitor material. J. Phys. Chem. Solids. 70(2), 495-500 (2009). doi:10.1016/j.jpcs.2008.12.004

[25] C.M. Ghimbeu, E. Raymundo-Piñero, P. Fioux, F. Béguin, C. Vix-Guterl, Vanadium nitride/carbon nanotube nanocomposites as electrodes for supercapacitors. J. Mater. Chem. 21(35), 13268-13275 (2011). doi:10.1039/c1jm11014d

[26] F. Cheng, C. He, D. Shu, H. Chen, J. Zhang, Preparation of nanocrystalline VN by the melamine reduction of V2O5 xerogel and its supercapacitive behavior. Mater. Chem. Phys. 131(1), 268-273 (2011). doi:10.1016/j.matchemphys.2011.09.040

[27] D. Shu, C. Lv, F. Cheng, C. He, K. Yang, Enhanced capacitance and rate capability of nanocrystalline VN as electrode materials for supercapacitors. Int. J. Electrochem. Sci. 8(1), 1209-1225 (2013).

[28] J. Lang, X. Yan, W. Liu, R. Wang, Q. Xue, Influence of nitric acid modification of ordered mesoporous carbon materials on their capacitive performances in different aqueous electrolytes. J. Power Sources 204(1), 220-229 (2012). doi:10.1016/j.jpowsour.2011.12.044

[29] H. Fan, F. Ran, X. Zhang, H Song, W Jing, Easy fabrication and high electrochemical capacitive performance of hierarchical porous carbon by a method combining liquid-liquid phase separation and pyrolysis process. Electrochim. Acta. 138(25), 367-375 (2014). doi:10.1016/j.electacta.2014.06.118

[30] W. Ai, J. Jiang, J. Zhu, Z. Fan, Y. Wang, Supramolecular polymerization promoted in situ fabrication of nitrogen-doped porous grapheme sheets as anode materials for Li-ion batteries. Adv. Energy Mater. 5(15), 1500559 (2015). doi:10.1002/aenm.201500559

[31] Y. Han, X. Dong, C. Zhang, S. Liu, Hierarchical porous carbon hollow-spheres as a high performance electrical double-layer capacitor material. J. Power Sources 211, 92-96 (2012). doi:10.1016/j.jpowsour.2012.03.053

[32] Z.C. Yang, C.H. Tang, H. Gong, X. Li, J. Wang, Hollow spheres of nanocarbon and their manganese dioxide hybrids derived from soft template for supercapacitor application. J. Power Sources 240(240), 713-720 (2013). doi:10.1016/j.jpowsour.2013.05.034

[33] F. He, Z. Hu, K. Liu, S. ZhangH. Liu, In situ fabrication of nickel aluminum-layered double hydroxide nanosheets/hollow carbon nanofibers composite as a novel electrode material for supercapacitors. J. Power Sources 267(4), 188-196 (2014). doi:10.1016/j.jpowsour.2014.05.084

[34] Y. Su, I. Zhitomirsky, Hybrid MnO2/carbon nanotube-VN/carbon nanotube supercapacitors. J. Power Sources 267, 235-242 (2014). doi:10.1016/j.jpowsour.2014.05.091

[35] E.F.D. Souza, C.A. Chagas, T.C. Ramalho, V.T.D SilvaD.L.M Aguiar, A combined experimental and theoretical study on the formation of crystalline vanadium nitride (VN) in low temperature through a fully solid-state synthesis route. J. Phys. Chem. C 117(48), 25659-25668 (2013). doi:10.1021/jp410885u

[36] B. Gao, X. Li, X. Guo, X. Zhang, X. Peng, Nitrogen-doped carbon encapsulated mesoporousvanadium nitride nanowires as self-supported electrodes for flexible all-solid-state supercapacitors. Adv. Mater. Interfaces 2(13), 1500211 (2015). doi:10.1002/admi.201500211

[37] X. Zhou, C. Shang, L. Gu, S DongX Chen, Mesoporous coaxial titanium nitride-vanadium nitride fibers of core–shell structures for high-performance supercapacitors. ACS Appl. Mater. Inter. 3(8), 3058-3063 (2011). doi:10.1021/am200564b

[38] Y. M. Shul'Ga, V.N. Troitskii, Study of the surface of finely divided titanium nitride by X-ray photoelectron spectroscopy. Rev. Mex. Biodivers. 6(18), 681-684 (2006). doi:10.1007/BF00797433

[39] D. Choi, G.E. Blomgren, P.N. Kumta, Fast and reversible surface redox reaction in nanocrystalline vanadium nitride supercapacitors. Adv. Mater. 18(9), 1178-1182 (2006). doi:10.1002/adma.200502471

[40] H. Zhao, M. Lei, X. Chen, W. Tang, Facile route to metal nitrides through melamine and metal oxides. J. Mater. Chem. 16(45), 4407-4412 (2006). doi:10.1039/b611381h

[41] J. Buha, I. Djerdj, M. Antonietti, M Niederberger, Thermal transformation of metal oxide nanoparticles into nanocrystalline metal nitrides using cyanamide and urea as nitrogen source. Chem. Mater. 19(14), 3499-3505 (2007). doi:10.1021/cm0701759

[42] Y. Wang, Z. Hong, M. Wei, Y. Xia, Layered H2Ti6O13-Nanowires: A new promising pseudocapacitivematerial in non-aqueous electrolyte. Adv. Funct. Mater. 22(24), 5185-5193 (2012). doi:10.1002/adfm.201200766

[43] K. Shen, F. Ran, Y. Tan, X. Niu, H. Fan, Toward interconnected hierarchical porous structure via chemical depositing organic nano-polyaniline on inorganic carbon scaffold for supercapacitor. Synth. Met. 199, 205-213 (2015). doi:10.1016/j.synthmet.2014.11.034

[44] H. Fan, F. Ran, X. Zhang, H. Song, X. Niu, Hollow carbon microspheres/MnO2 nanosheets composites: hydrothermal synthesis and electrochemical behaviors. Nano-Micro Lett. 7(1), 59-67 (2015). doi:10.1007/s40820-014-0019-z

[45] R. Wang, J. Lang, P. Zhang, Z. Lin, X. Yan, Fast and large lithium storage in 3D porous VN nanowires–graphene composite as a superior anode toward high-performance hybrid supercapacitors. Adv.  Funct. Mater. 25(15), 2270-2278 (2015). doi:10.1002/adfm.201404472

[46] L. Zhao, L.Z. Fan, M.Q. Zhou, H. Guan, S. Qiao, Nitrogen-containing hydrothermal carbons with superior performance in supercapacitors. Adv. Mater. 22(45), 5202-5206 (2010). doi:10.1002/adma.201002647

[47] X. Zhou, H. Chen, D. Shu, C. He, J. Nan, Study on the electrochemical behavior of vanadium nitride as a promising supercapacitor material. J. Phys. Chem. Solids. 70(2), 495-500 (2009). doi:10.1016/j.jpcs.2008.12.004

[48] M.D. Stoller, S. Park, Y. Zhu, J. An, R.S. Ruoff, Graphene-based ultracapacitors. Nano Lett. 8(10), 3498-3502 (2008). doi:10.1021/nl802558y

[49] S. Boukhalfa, K. Evanoff, G. Yushin, Atomic layer deposition of vanadium oxide on carbon nanotubes for high-power supercapacitor electrodes. Energ. Environ. Sci. 5(5), 6872-6879(2012). doi:10.1039/c2ee21110f

[50] M.W. Xu, D.D. Zhao, S.J. Bao, H.L. Li, Mesoporous amorphous MnO2 as electrode material for supercapacitor. J. Solid State Electr. 11(8), 1101-1107 (2007). doi:10.1007/s10008-006-0246-4

[51] S. S. Zhang, K. Xu, T.R. Jow, Electrochemical impedance study on the low temperature of Li-ion batteries. Electrochim. Acta 49(7), 1057-1061 (2004). doi:10.1016/j.electacta.2003.10.016

[52] S. Cong, Y. Tian, Q. Li, Z. Zhao, F. Geng, Single-crystalline tungsten oxide quantum dots for fast pseudocapacitor and electrochromic applications. Adv. Mater. 26(25), 4260-4267 (2014). doi:10.1002/adma.201400447

[53] R. Wang, J. Lang, Y. Liu, Z. Lin, X. Yan, Ultra-small, size-controlled Ni(OH)2 nanoparticles: elucidating the relationship between particle size and electrochemical performance for advanced energy storage devices. NPG Asia Mater. 7(6), e183 (2015). doi: 10.1038/am.2015.42

[54] Y. Xu, J. Wang, L. Shen, H. Dou, X. Zhang, One-dimensional vanadium nitride nanofibers fabricated by electrospinning for supercapacitors. Electrochim. Acta 173, 680-686 (2015). doi:10.1016/j.electacta.2015.05.088

[55] L. Wang, J. Sun, R. Song, S. Yang, H. Song, Hybrid 2D-0D graphene-VN quantum dots for superior lithium and sodium storage. Adv. Energy Mater. 2015. doi:10.1002/aenm.201502067

[56] C. Zhu, P. Yang, D. Chao, X. Wang, X. Zhang, All metal nitrides solid-state asymmetric supercapacitors. Adv. Mater. 27(31), 4566-4571 (2015). doi:10.1002/adma.201501838

[57] X. Lu, G. Wang, T. Zhai, M. Yu, S. Xie, Stabilized TiN nanowire arrays for high-performance and flexible supercapacitors. Nano Lett. 12(10), 5376-81 (2012). doi:10.1021/nl302761z

[58] X. Lu, M. Yu, T. Zhai, G. Wang, S. Xie, High energy density asymmetric quasi-solid-state supercapacitor based on porous vanadium nitride nanowire anode. Nano Lett. 3(6), 2628-2633 (2013). doi:10.1021/nl400760a

[59] S. Zhang, N. Pan, Supercapacitors Performance Evaluation. Adv. Energy Mater. 5(6), 1401401 (2014). doi:10.1002/aenm.201401401

Citation Information

Yunlong Yang, Kuiwen Shen, Ying Liu, Yongtao Tan, Xiaoning Zhao, Jiayu Wu, Xiaoqin Niu, Fen Ran, Novel Hybrid Nanoparticles of Vanadium Nitride/Porous Carbon as An Anode Material for Symmetrical Supercapacitor. Nano-Micro Lett.(2017) 9: 6. http://dx.doi.org/10.1007/s40820-016-0105-5

History

Received: 27 June 2016 / Accepted: 5 August 2016


Additional Info

  • Type of Publishing: JOUR - Journal
  • Title:

    Novel Hybrid Nanoparticles of Vanadium Nitride/Porous Carbon as An Anode Material for Symmetrical Supercapacitor

  • Author: Yunlong Yang, Kuiwen Shen, Ying Liu, Yongtao Tan, Xiaoning Zhao, Jiayu Wu, Xiaoqin Niu, Fen Ran
  • Year: 2017
  • Volume: 9
  • Issue: 1
  • Journal Name: Nano-Micro Letters
  • Publisher: OPEN ACCESS HOUSE SCIENCE & TECHNOLOGY
  • ISSN: 2150-5551
  • URL: http://dx.doi.org/10.1007/s40820-016-0105-5
  • Abstract:

    Hybrid materials of vanadium nitride and porous carbon nanoparticles (VN/PCNPs) were fabricated by a facile pyrolysis process of vanadium pentoxide (V2O5) xerogel and melamine at relatively low temperature of 800 °C for supercapacitor application. The effects of the feed ratio of V2O5 to melamine (r), and nitrogen flow rate on the microstructure and electrochemical performance were also investigated. It was found that the size of as-synthesized nanoparticles is about 20 nm. Both r value and N2 flow rate have enormous impacts on morphology and microstructure of the nanoparticle, which correspondingly determined the electrochemical performance of the material. The VN/C hybrid nanoparticles exhibited high capacitive properties, and a maximum specific capacitance of 255.0 F g-1 was achieved at a current density of 1.0 A g-1 in 2 M KOH aqueous electrolyte and the potential range from 0 to -1.15 V. In addition, symmetrical supercapacitor fabricated with as-synthesized VN/PCNPs presents a high specific capacitance of 43.5 F g-1 at 0.5 A g-1 based on the entire cell, and an energy density of 8.0 Wh kg-1 when the power density was 575 W kg-1. Even when the power density increased to 2831.5 W kg-1, the energy density still remained 6.1 Wh kg-1.

  • Publish Date: Tuesday, 13 September 2016
  • DOI: 10.1007/s40820-016-0105-5